A Neutron Diffraction Study of the Effect of Holdings and Heat Treatment on Residual Stresses in a Steel Weld

verfasst von: I. D. Karpov, V. T. Em, I. G. Karpov, A. V. Il’in

Erschienen in: Physics of Metals and Metallography | Ausgabe 9/2022

Einloggen, um Zugang zu erhalten
share
TEILEN

Abstract

Residual stresses in an X-shaped weld of 32-mm-thick steel plates have been studied using neutron diffraction. The effect of pre-holding of weldments and their post-weld heat treatment on the distribution of residual stresses has been studied. The stress distribution is close to symmetric with respect to the centerline of the weld section and clearly asymmetric with respect to the middle of the weld thickness. The maximum tensile (longitudinal) stresses occur in the weld half-thickness, which was welded first. The peak value of longitudinal stresses in a fixed plate is 800 MPa (98% of the yield strength of the weld metal), which is significantly higher than that in a free plate (530 MPa). The zone of maximum compressive (transverse) stresses of –400 MPa in a fixed plate is located in the first half-thickness of the weld, while its second half occurs in the free plate. After heat treatment, the tensile and compressive stresses remained in general tensile and compressive, respectively. The maximum tensile longitudinal stresses were reduced to 270 MPa in the fixed plate and to 220 MPa in the free plate. The maximum compressive transverse stresses in both plates were reduced to ‒170 MPa.

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt 90 Tage mit der neuen Mini-Lizenz testen!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 58.000 Bücher
  • über 300 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko





Jetzt 90 Tage mit der neuen Mini-Lizenz testen!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe



 


Jetzt 90 Tage mit der neuen Mini-Lizenz testen!

Literatur
1.
Zurück zum Zitat P. J. Withers and H. K. Bhadeshia, “Residual Stress – II: Nature and Origins,” Mater. Sci. Technol. 17, 366–375 (2001). CrossRef P. J. Withers and H. K. Bhadeshia, “Residual Stress – II: Nature and Origins,” Mater. Sci. Technol. 17, 366–375 (2001). CrossRef
2.
Zurück zum Zitat M. T. Hutchings, P. J. Withers, T. M. Holden, and T. Lorentzen, Introduction to the Characterization of Residual Stress by Neutron Diffraction, 1st ed. (Taylor and Francis, London, 2005). CrossRef M. T. Hutchings, P. J. Withers, T. M. Holden, and T. Lorentzen, Introduction to the Characterization of Residual Stress by Neutron Diffraction, 1st ed. (Taylor and Francis, London, 2005). CrossRef
3.
Zurück zum Zitat M. Mochizuki, “Control of welding residual stress for ensuring integrity against fatigue and stress–corrosion cracking,” Nucl. Eng. Des. 237, 107–123 (2007). CrossRef M. Mochizuki, “Control of welding residual stress for ensuring integrity against fatigue and stress–corrosion cracking,” Nucl. Eng. Des. 237, 107–123 (2007). CrossRef
4.
Zurück zum Zitat N. Winzer, A. Atrens, W. Dietzel, V. S. Raja, G. Song, and K. U. Kainer, “Characterisation of Stress Corrosion Cracking (SCC) of Mg–Al Alloys”, Mater. Sci. Eng., A 488 (1–2), 339–351 (2008). CrossRef N. Winzer, A. Atrens, W. Dietzel, V. S. Raja, G. Song, and K. U. Kainer, “Characterisation of Stress Corrosion Cracking (SCC) of Mg–Al Alloys”, Mater. Sci. Eng., A 488 (1–2), 339–351 (2008). CrossRef
5.
Zurück zum Zitat Z. Barsoum and I. Barsoum, “Residual stress effects on fatigue life of welded structures using LEFM,” Eng. Fail. Anal. 16, 449–467 (2009). CrossRef Z. Barsoum and I. Barsoum, “Residual stress effects on fatigue life of welded structures using LEFM,” Eng. Fail. Anal. 16, 449–467 (2009). CrossRef
6.
Zurück zum Zitat L. Doremus, J. Cormier, P. Villechaise, G. Henaff, Y. Nadot, and S. Pierret, “Influence of residual stresses on the fatigue crack growth from surface anomalies in a nickel-based superalloy,” Mater. Sci. Eng., A 644, 234–246 (2015). CrossRef L. Doremus, J. Cormier, P. Villechaise, G. Henaff, Y. Nadot, and S. Pierret, “Influence of residual stresses on the fatigue crack growth from surface anomalies in a nickel-based superalloy,” Mater. Sci. Eng., A 644, 234–246 (2015). CrossRef
7.
Zurück zum Zitat X. Cheng, J. W. Fisher, H. J. Prask, T. Gnaupel-Herold, B. T. Yen, and S. Roy, “Residual stress modification by post-weld treatment and its beneficial effect on fatigue strength of welded structures,” Int. J. Fatigue 25, 1259–1269 (2003). CrossRef X. Cheng, J. W. Fisher, H. J. Prask, T. Gnaupel-Herold, B. T. Yen, and S. Roy, “Residual stress modification by post-weld treatment and its beneficial effect on fatigue strength of welded structures,” Int. J. Fatigue 25, 1259–1269 (2003). CrossRef
8.
Zurück zum Zitat M. Xu, J. Chen, H. Lu, J. Xu, C. Yu, and X. Wei, “Effects of residual stress and grain boundary character on creep cracking in 2.25Cr–1.6W steel,” Mater. Sci. Eng., A 659, 188–197 (2016). CrossRef M. Xu, J. Chen, H. Lu, J. Xu, C. Yu, and X. Wei, “Effects of residual stress and grain boundary character on creep cracking in 2.25Cr–1.6W steel,” Mater. Sci. Eng., A 659, 188–197 (2016). CrossRef
10.
Zurück zum Zitat A. M. Paradowska, J. W. H. Price, T. R. Finlauson, R. B. Rogge, R. L. Donaberger, and R. Ibrahim, “Comparison of neutron diffraction measurements of residual stress of steel butt welds with current fitness-for-purpose assessments,” J. Pressure Vessels Technol. Trans. ASME 132, 051503-7 (2010). CrossRef A. M. Paradowska, J. W. H. Price, T. R. Finlauson, R. B. Rogge, R. L. Donaberger, and R. Ibrahim, “Comparison of neutron diffraction measurements of residual stress of steel butt welds with current fitness-for-purpose assessments,” J. Pressure Vessels Technol. Trans. ASME 132, 051503-7 (2010). CrossRef
11.
Zurück zum Zitat W. Woo, G. An, E. Kingston, A. Dewald, D. Smith, and M. R. Hill, “Through-thickness distributions of residual stresses in two extreme heat-input thick welds: a neutron diffraction, contour method and deep hole drilling study,” Acta Mater. 61, 3564–3574 (2013). CrossRef W. Woo, G. An, E. Kingston, A. Dewald, D. Smith, and M. R. Hill, “Through-thickness distributions of residual stresses in two extreme heat-input thick welds: a neutron diffraction, contour method and deep hole drilling study,” Acta Mater. 61, 3564–3574 (2013). CrossRef
12.
Zurück zum Zitat D. J. Smith, G. Zheng, P. R. Hurrell, C. M. Gill, B. M. E. Pellereau, K. Ayres, D. Goudar, and E. Kingston, “Measured and predicted residual stresses in thick section electron beam welded steels,” Int. J. Pressure Vessels Piping 120– 121, 66–79 (2014). CrossRef D. J. Smith, G. Zheng, P. R. Hurrell, C. M. Gill, B. M. E. Pellereau, K. Ayres, D. Goudar, and E. Kingston, “Measured and predicted residual stresses in thick section electron beam welded steels,” Int. J. Pressure Vessels Piping 120121, 66–79 (2014). CrossRef
13.
Zurück zum Zitat H. Alipooramirabad, A. Paradowska, R. Ghomashchi, A. Kotousov, and M. Reid, “Quantification of residual stresses in multi-pass welds using neutron diffraction,” J. Mater. Process. Technol. 226, 40–49 (2015). CrossRef H. Alipooramirabad, A. Paradowska, R. Ghomashchi, A. Kotousov, and M. Reid, “Quantification of residual stresses in multi-pass welds using neutron diffraction,” J. Mater. Process. Technol. 226, 40–49 (2015). CrossRef
14.
Zurück zum Zitat W. Jiang, W. Woo, Y. Wan, Y. Luo, X. Xie, and S. T. Tu, “Evaluation of through-thickness residual stresses by neutron diffraction and finite-element method in thick weld plates,” J. Pressure Vessel Technol. 139, 031401-11 (2017). CrossRef W. Jiang, W. Woo, Y. Wan, Y. Luo, X. Xie, and S. T. Tu, “Evaluation of through-thickness residual stresses by neutron diffraction and finite-element method in thick weld plates,” J. Pressure Vessel Technol. 139, 031401-11 (2017). CrossRef
15.
Zurück zum Zitat Y. Wan, W. Jiang, J. Lu, G. Sun, D. K. Kim, W. Woo, and S. T. Tu, “Weld residual stresses in a thick plate considering back chipping: neutron diffraction, contour method and finite element simulation study,” Mater. Sci. Eng., A 699, 62–70 (2017). CrossRef Y. Wan, W. Jiang, J. Lu, G. Sun, D. K. Kim, W. Woo, and S. T. Tu, “Weld residual stresses in a thick plate considering back chipping: neutron diffraction, contour method and finite element simulation study,” Mater. Sci. Eng., A 699, 62–70 (2017). CrossRef
16.
Zurück zum Zitat D. J. Smith and S. J. Garwood, “Influence of postweld heat treatment on the variation of residual stresses in 50 mm thick welded ferritic steel plates,” Int. J. Pressure Vessels Piping 51, 241–256 (1992). CrossRef D. J. Smith and S. J. Garwood, “Influence of postweld heat treatment on the variation of residual stresses in 50 mm thick welded ferritic steel plates,” Int. J. Pressure Vessels Piping 51, 241–256 (1992). CrossRef
17.
Zurück zum Zitat Y. Shim, Z. Feng, S. Lee, D. Kim, J. Jaeger, J. C. Parritan, and C. L. Tsai, “Determination of residual stresses in thick-section weldments,” Weld. Res. Supplem. 71, 305–312 (1992). Y. Shim, Z. Feng, S. Lee, D. Kim, J. Jaeger, J. C. Parritan, and C. L. Tsai, “Determination of residual stresses in thick-section weldments,” Weld. Res. Supplem. 71, 305–312 (1992).
18.
Zurück zum Zitat V. T. Em, A. M. Balagurov, V. P. Glazkov, I. D. Karpov, P. Mikula, N. F. Miron, V. A. Somenkov, V. V. Sumin, J. Šaroun, and M. N. Shushunov, “A double-crystal monochromator for neutron stress diffractometry,” Instr. Exp. Technol. 60, 526–532 (2017). CrossRef V. T. Em, A. M. Balagurov, V. P. Glazkov, I. D. Karpov, P. Mikula, N. F. Miron, V. A. Somenkov, V. V. Sumin, J. Šaroun, and M. N. Shushunov, “A double-crystal monochromator for neutron stress diffractometry,” Instr. Exp. Technol. 60, 526–532 (2017). CrossRef
21.
Zurück zum Zitat S. Ganguly, L. Edwards, and M. E. Fitzpatrick, “Problems in using a comb sample as a stress-free reference for the determination of welding residual stress by diffraction,” Mater. Sci. Eng., A 528, 1226–1232 (2011). CrossRef S. Ganguly, L. Edwards, and M. E. Fitzpatrick, “Problems in using a comb sample as a stress-free reference for the determination of welding residual stress by diffraction,” Mater. Sci. Eng., A 528, 1226–1232 (2011). CrossRef
22.
Zurück zum Zitat C. Ohms, P. Hornak, R. Wimpory, and A. G. Youtsos, “Residual stress analyses based on neutron diffraction in double-V butt welded steel plates,” J. Neutron Res. 11, 273–276 (2003). CrossRef C. Ohms, P. Hornak, R. Wimpory, and A. G. Youtsos, “Residual stress analyses based on neutron diffraction in double-V butt welded steel plates,” J. Neutron Res. 11, 273–276 (2003). CrossRef
23.
Zurück zum Zitat H. Suzuki and T. M. Holden, “Neutron diffraction measurements of stress in an austenitic butt weld,” J. Strain Anal. 41 (8), 575–581 (2006). CrossRef H. Suzuki and T. M. Holden, “Neutron diffraction measurements of stress in an austenitic butt weld,” J. Strain Anal. 41 (8), 575–581 (2006). CrossRef
Metadaten
Titel
A Neutron Diffraction Study of the Effect of Holdings and Heat Treatment on Residual Stresses in a Steel Weld
verfasst von
I. D. Karpov
V. T. Em
I. G. Karpov
A. V. Il’in
Publikationsdatum
01.09.2022
Verlag
Pleiades Publishing
Erschienen in
Physics of Metals and Metallography / Ausgabe 9/2022
Print ISSN: 0031-918X
Elektronische ISSN: 1555-6190
DOI
https://doi.org/10.1134/S0031918X22090058

Weitere Artikel der Ausgabe 9/2022

Physics of Metals and Metallography 9/2022 Zur Ausgabe

STRUCTURE, PHASE TRANSFORMATIONS, AND DIFFUSION

The Fine Structure of MgB2 Alloyed with Y and Gd