A Study of Microstructures and Tensile Properties of Two Fe-Mn-Al-Si-C Alloys

verfasst von: B. Bhattacharya, A.S. Sharma, S.S. Hazra, R.K. Ray

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 5/2009

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Two high-manganese steel compositions were prepared (low-carbon steel (LC): 0.05C-26.3Mn-4.88Si-4.13Al-Fe, and high-carbon steel (HC): 0.52C-29.8Mn-2.96Si-2.73Al-Fe). These were homogenized, hot rolled, heat treated, and finally subjected to tensile testing and other characterizations. The LC steel, with a duplex microstructure containing body-centered-cubic (bcc) and face-centered-cubic (fcc) phases, exhibited extremely poor room-temperature ductility. On the other hand, the HC steel, with a single-phase austenitic structure, showed a good tensile property due to twin-induced plasticity (TWIP) effect, with total tensile elongation as high as 56 pct. Structural analysis of steel LC was carried out and it was found that the bcc phase of steel LC was actually an ordered DO3 phase, which was identified as the principal reason of poor ductility of steel LC.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat S. Allain, J.-P. Chateau, and O. Bouaziz: Mater. Sci. Eng. A, 2004, vols. 387A–389A, pp. 143–47. S. Allain, J.-P. Chateau, and O. Bouaziz: Mater. Sci. Eng. A, 2004, vols. 387A–389A, pp. 143–47.
2.
Zurück zum Zitat O. Grässel, L. Krüger, G. Frommeyer, and L.W. Meyer: Int. J. Plast., 2000, vol. 16, pp. 1391–1409.MATHCrossRef O. Grässel, L. Krüger, G. Frommeyer, and L.W. Meyer: Int. J. Plast., 2000, vol. 16, pp. 1391–1409.MATHCrossRef
3.
Zurück zum Zitat S. Vercammen, B. Blanpain, B.C. DeCooman, and P. Wollants: Acta Mater., 2004, vol. 52, pp. 2005–12.CrossRef S. Vercammen, B. Blanpain, B.C. DeCooman, and P. Wollants: Acta Mater., 2004, vol. 52, pp. 2005–12.CrossRef
4.
Zurück zum Zitat Y.G. Kim, J.M. Han, and J.S. Lee: Mater. Sci. Eng. A, 1989, vol. 114, pp. 51–59.CrossRef Y.G. Kim, J.M. Han, and J.S. Lee: Mater. Sci. Eng. A, 1989, vol. 114, pp. 51–59.CrossRef
5.
Zurück zum Zitat N. Cabaňas, N. Akdut, J. Penning, and B.C. DeCooman: Metall. Mater. Trans. A, 2006, vol. 37A, pp. 3305–15.CrossRef N. Cabaňas, N. Akdut, J. Penning, and B.C. DeCooman: Metall. Mater. Trans. A, 2006, vol. 37A, pp. 3305–15.CrossRef
6.
Zurück zum Zitat P. Yang, Q. Xie, L. Meng, H. Ding, and Z. Tang: Scripta Mater., 2006, vol. 55, pp. 629–31.CrossRef P. Yang, Q. Xie, L. Meng, H. Ding, and Z. Tang: Scripta Mater., 2006, vol. 55, pp. 629–31.CrossRef
7.
Zurück zum Zitat D. Hua, T.Z. You, L. Wei, W. Me, and S. Dan: J. Iron Steel Res. Int., 2006, vol. 13 (6), pp. 66–70.CrossRef D. Hua, T.Z. You, L. Wei, W. Me, and S. Dan: J. Iron Steel Res. Int., 2006, vol. 13 (6), pp. 66–70.CrossRef
8.
Zurück zum Zitat K. Ishida, H. Ohtani, N. Satoh, R. Kainuma, and T. Nishijawa: ISIJ Int., 1990, vol. 30, pp. 680–86.CrossRef K. Ishida, H. Ohtani, N. Satoh, R. Kainuma, and T. Nishijawa: ISIJ Int., 1990, vol. 30, pp. 680–86.CrossRef
9.
Zurück zum Zitat O. Acselrad, I.S. Kalashnikov, E.M. Silva, R.A. Simao, C.A. Achete, and L.C. Pereira: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3569–73.CrossRef O. Acselrad, I.S. Kalashnikov, E.M. Silva, R.A. Simao, C.A. Achete, and L.C. Pereira: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3569–73.CrossRef
10.
Zurück zum Zitat K. Sato, M. Ichinose, Y. Ohirotsu, and Y. Inoue: ISIJ Int., 1989, vol. 29, pp. 868–77.CrossRef K. Sato, M. Ichinose, Y. Ohirotsu, and Y. Inoue: ISIJ Int., 1989, vol. 29, pp. 868–77.CrossRef
11.
Zurück zum Zitat S. Allain, J.-P. Chateau, D. Dahmoun, and O. Bouaziz: Mater. Sci. Eng., 2004, vols. A 387–A389, pp. 272–76. S. Allain, J.-P. Chateau, D. Dahmoun, and O. Bouaziz: Mater. Sci. Eng., 2004, vols. A 387–A389, pp. 272–76.
12.
Zurück zum Zitat D. Cornette, P. Cugy, A. Hildenbrand, M. Bouzekri, and G. Lovato: Rev. Métallurgie-CIT, 2005, Dec., pp. 905–18. D. Cornette, P. Cugy, A. Hildenbrand, M. Bouzekri, and G. Lovato: Rev. Métallurgie-CIT, 2005, Dec., pp. 905–18.
13.
Zurück zum Zitat R. Ueji, K. Harada, N. Tsuchida, and K. Kunishige: Mater. Sci. Forum, 2007, vols. 561–565, pp. 107–10.CrossRef R. Ueji, K. Harada, N. Tsuchida, and K. Kunishige: Mater. Sci. Forum, 2007, vols. 561–565, pp. 107–10.CrossRef
14.
Zurück zum Zitat ASM Handbook, vol. 3, Alloy Phase Diagrams, ASM INTERNATIONAL, Metals Park, OH, 1992. ASM Handbook, vol. 3, Alloy Phase Diagrams, ASM INTERNATIONAL, Metals Park, OH, 1992.
15.
Zurück zum Zitat R. Ramesh, R. Vasudevan, B. Pathiraj, and B.H. Kolster: J. Mater. Sci., 1992, vol. 27, pp. 270–78.CrossRef R. Ramesh, R. Vasudevan, B. Pathiraj, and B.H. Kolster: J. Mater. Sci., 1992, vol. 27, pp. 270–78.CrossRef
16.
Zurück zum Zitat B.D. Cullity: Elements of X-Ray Diffraction, Addison-Wesley, New York, NY, 1978. B.D. Cullity: Elements of X-Ray Diffraction, Addison-Wesley, New York, NY, 1978.
17.
Zurück zum Zitat B. Bhattacharya and R.K. Ray: Metall. Mater. Trans. A, 2000, vol. 31A, pp. 3001–10.CrossRef B. Bhattacharya and R.K. Ray: Metall. Mater. Trans. A, 2000, vol. 31A, pp. 3001–10.CrossRef
18.
Zurück zum Zitat B. Bhattacharya and R K. Ray: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3605–18.CrossRef B. Bhattacharya and R K. Ray: Metall. Mater. Trans. A, 2002, vol. 33A, pp. 3605–18.CrossRef
19.
20.
Zurück zum Zitat M.G. Mendiratta and H.A. Lips: in High-Temperature Ordered Intermetallic Alloys, C.C. Koch, C.T. Liu, and N.S. Stoloff, eds., MRS, Pittsburgh, PA, 1989, pp. 155–72. M.G. Mendiratta and H.A. Lips: in High-Temperature Ordered Intermetallic Alloys, C.C. Koch, C.T. Liu, and N.S. Stoloff, eds., MRS, Pittsburgh, PA, 1989, pp. 155–72.
21.
Zurück zum Zitat C.G. McKamey, C.T. Liu, J.V. Cathcart, S.A. David, and E.H. Lee: Evaluation of Mechanical and Metallurgical Properties of Fe 3 Al Based Aluminides, Oak Ridge National Laboratory, Oak Ridge, TN, 1986. C.G. McKamey, C.T. Liu, J.V. Cathcart, S.A. David, and E.H. Lee: Evaluation of Mechanical and Metallurgical Properties of Fe 3 Al Based Aluminides, Oak Ridge National Laboratory, Oak Ridge, TN, 1986.
22.
Zurück zum Zitat F. Sorbello, P.E.J. Flewitt, A.G. Crocker, and G. E. Smith: Key Eng. Mater., 2008, vol. 385–87, pp. 1–4.CrossRef F. Sorbello, P.E.J. Flewitt, A.G. Crocker, and G. E. Smith: Key Eng. Mater., 2008, vol. 385–87, pp. 1–4.CrossRef
23.
Zurück zum Zitat G. Frommeyer and U. Brüx: Steel Res. Int., 2006, vol. 77, pp. 627–33. G. Frommeyer and U. Brüx: Steel Res. Int., 2006, vol. 77, pp. 627–33.
Metadaten
Titel
A Study of Microstructures and Tensile Properties of Two Fe-Mn-Al-Si-C Alloys
verfasst von
B. Bhattacharya
A.S. Sharma
S.S. Hazra
R.K. Ray
Publikationsdatum
01.05.2009
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 5/2009
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-009-9797-1

Weitere Artikel der Ausgabe 5/2009

Metallurgical and Materials Transactions A 5/2009 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.