01.03.2014 | Ausgabe 3/2014

Journal of Materials Engineering and Performance 3/2014

A Study on the Passivation Behavior and Semiconducting Properties of Gamma Titanium Aluminide in 0.1 N H2SO4, HNO3, and HClO4 Acidic Solutions

Zeitschrift:
Journal of Materials Engineering and Performance > Ausgabe 3/2014
Autoren:
S. Memarbashi, E. Saebnoori, T. Shahrabi

Abstract

The study focuses on the passivation behavior of single-gamma-phase titanium aluminide in acidic solutions with a particular emphasis on the role of oxidizing strength in characteristics of passive layer. The report includes potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) studies along with Mott-Schottky analysis in order to determine the corrosion behavior of the alloy and the semiconducting properties of the scale formed during exposure to acidic environment. Passive current density measured from potentiodynamic polarization curve, polarization resistance (R p) estimated by EIS, defect density, and flatband potential drawn from Mott-Schottky analysis are mainly used in estimating the ability of passive film formed on alloy in protecting it against high corrosion rates in Sulfuric acid (a non-oxidizing acid), perchloric acid, and nitric acid (oxidizing acid with different oxidizing strength). The results show that passive current density (i pass) in Sulfuric acid is 2.67 × 10−5 A cm−2, which is 2.5 and 3 times greater than the values obtained in perchloric acid (i pass = 9.91 × 10−6) and nitric acid (i pass = 7.98 × 10−6), respectively. EIS data reveal that the value of R p in sulfuric acid (20 kΩ cm2) is about three and five times smaller than that its value in perchloric acid and Nitric acid, respectively. Mott-Schottky analysis shows that the passive layer exhibits an n-type semiconducting characteristics irrespective of acidic environment. The greatest and the smallest values of donor density (N D) are obtained for the passive scale formed in sulfuric acid (N D, H2SO4 = 18.36 × 1019) and nitric acid (N D, HNO3 = 13.13 × 1019), respectively. The report concludes that characteristics of the passive scale are directly affected by reduction potential of the acid, which is the criterion of its oxidizing strength. An increase in the oxidizing strength of the acidic solution results in formation of more protective and less conductive layer on γ phase titanium aluminide.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 3/2014

Journal of Materials Engineering and Performance 3/2014 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise