AC conductivity properties of annealed In2S3 film deposited by spray technique

verfasst von: N. Bouguila, I. Najeh, N. Ben Mansour, H. Bouzouita, S. Alaya

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2015

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In2S3 thin film was prepared by chemical spray pyrolysis technique onto clean soda–lime glass substrate. Indium chloride and thiourea were used as reagents. This film was sealed into Pyrex tube at a pressure of 10−6 Torr and then annealed at 673 K for 3 h. The film was characterized by means of X-ray diffraction (XRD), atomic force microscope (AFM) and by impedance spectroscopy measurements. XRD spectra show that In2S3 film is polycrystalline with a cubic phase and preferentially oriented towards (400). The film grain size is about 45 nm. AFM analysis shows that root mean square (RMS) roughness is equal to 112 nm. The film electrical conductance is found to be dependent on measurement temperature and frequency. The direct current conductivity measurement outlines the dominance of the hopping mechanism. The alternating current electrical conductivity of the sample is controlled by the correlated barrier hopping conduction mechanism. The activation energy is found to be in the order of 90 meV. Furthermore, the film exhibits a photoconductive behavior.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat K. Hara, K. Sayama, H. Arakawa, Sol. Energy Mater. Sol. Cells 62, 441 (2000)CrossRef K. Hara, K. Sayama, H. Arakawa, Sol. Energy Mater. Sol. Cells 62, 441 (2000)CrossRef
2.
Zurück zum Zitat L. Bhira, H. Essaidi, S. Belgacem, G. Couturier, J. Salardenne, N. Barreau, J.C. Bernede, Phys. Status Solidi A 181, 427 (2000)CrossRef L. Bhira, H. Essaidi, S. Belgacem, G. Couturier, J. Salardenne, N. Barreau, J.C. Bernede, Phys. Status Solidi A 181, 427 (2000)CrossRef
3.
Zurück zum Zitat T. John, M. Mathew, C.S. Kartha, K.P. Vijayakumar, T. Abe, Y. Kashiwaba, Sol. Energy Mater. Sol. Cells 89, 27 (2005)CrossRef T. John, M. Mathew, C.S. Kartha, K.P. Vijayakumar, T. Abe, Y. Kashiwaba, Sol. Energy Mater. Sol. Cells 89, 27 (2005)CrossRef
4.
Zurück zum Zitat N. Naghavi, S. Spiering, M. Powalla, B. Cavana, D. Lincot, Prog. Photovolt. Res. Appl. 11, 437 (2003)CrossRef N. Naghavi, S. Spiering, M. Powalla, B. Cavana, D. Lincot, Prog. Photovolt. Res. Appl. 11, 437 (2003)CrossRef
5.
Zurück zum Zitat K. Ernits, D. Bremaud, S. Buecheler, C.J. Hibberd, M. Kaelin, G. Khrypunov, U. Muller, E. Mellikov, A.N. Tiwari, Thin Solid Films 515, 6051 (2007)CrossRef K. Ernits, D. Bremaud, S. Buecheler, C.J. Hibberd, M. Kaelin, G. Khrypunov, U. Muller, E. Mellikov, A.N. Tiwari, Thin Solid Films 515, 6051 (2007)CrossRef
6.
Zurück zum Zitat S. Cingarapu, M.A. Ikenberry, D.B. Hamal, C.M. Sorensen, K. Hohn, K.J. Klabunde, Langmuir 28, 3569 (2012)CrossRef S. Cingarapu, M.A. Ikenberry, D.B. Hamal, C.M. Sorensen, K. Hohn, K.J. Klabunde, Langmuir 28, 3569 (2012)CrossRef
7.
Zurück zum Zitat L.J. Liu, W.D. Xiang, J.S. Zhong, X.Y. Yang, X.J. Liang, H.T. Liu, W. Cai, J. Alloys Compd. 493, 309 (2010)CrossRef L.J. Liu, W.D. Xiang, J.S. Zhong, X.Y. Yang, X.J. Liang, H.T. Liu, W. Cai, J. Alloys Compd. 493, 309 (2010)CrossRef
9.
Zurück zum Zitat H. Spasevska, C.C. Kitts, C. Ancora, G. Ruani, Int. J. Photoenergy 2012, 637943 (2012)CrossRef H. Spasevska, C.C. Kitts, C. Ancora, G. Ruani, Int. J. Photoenergy 2012, 637943 (2012)CrossRef
10.
Zurück zum Zitat M. Roy, B.P. Mandal, D.P. Dutta, A.K. Tyagi, Scr. Mater. 63, 93 (2010)CrossRef M. Roy, B.P. Mandal, D.P. Dutta, A.K. Tyagi, Scr. Mater. 63, 93 (2010)CrossRef
11.
Zurück zum Zitat S. Acharya, M. Dutta, S. Sarkar, D. Basak, S. Chakraborty, N. Pradhan, J. Mater. Chem. 24, 1779 (2012)CrossRef S. Acharya, M. Dutta, S. Sarkar, D. Basak, S. Chakraborty, N. Pradhan, J. Mater. Chem. 24, 1779 (2012)CrossRef
12.
Zurück zum Zitat Y. Yasaki, N. Sonoyama, T. Sakata, J. Electroanal. Chem. 469, 116 (1999)CrossRef Y. Yasaki, N. Sonoyama, T. Sakata, J. Electroanal. Chem. 469, 116 (1999)CrossRef
13.
Zurück zum Zitat N. Jebbari, F. Saadallah, C. Guasch, N.K. Turki, N. Yacoubi, R. Bennaceur, Appl. Phys. A 116, 2011 (2014)CrossRef N. Jebbari, F. Saadallah, C. Guasch, N.K. Turki, N. Yacoubi, R. Bennaceur, Appl. Phys. A 116, 2011 (2014)CrossRef
14.
Zurück zum Zitat M. Mathew, R. Jayakrishnan, P.M.R. Kumar, C. Sudha Kartha, K.P. Vijayakumar, T. Abe, Y. Kashiwaba, J. Appl. Phys. 100, 033504 (2006)CrossRef M. Mathew, R. Jayakrishnan, P.M.R. Kumar, C. Sudha Kartha, K.P. Vijayakumar, T. Abe, Y. Kashiwaba, J. Appl. Phys. 100, 033504 (2006)CrossRef
15.
Zurück zum Zitat Z. Li, X. Tao, Z. Wu, P. Zhang, Z. Zhang, Ultrason. Sonochem. 16, 221 (2009)CrossRef Z. Li, X. Tao, Z. Wu, P. Zhang, Z. Zhang, Ultrason. Sonochem. 16, 221 (2009)CrossRef
16.
Zurück zum Zitat B. Asenjo, C. Sanz, C. Guillén, A.M. Chaparro, M.T. Gutiérrez, J. Herrero, Thin Solid Films 515, 6041 (2007)CrossRef B. Asenjo, C. Sanz, C. Guillén, A.M. Chaparro, M.T. Gutiérrez, J. Herrero, Thin Solid Films 515, 6041 (2007)CrossRef
17.
Zurück zum Zitat N. Barreau, J.C. Bernède, C. Deudon, L. Brohan, S. Marsillac, Thin Solid Films 241, 4 (2002) N. Barreau, J.C. Bernède, C. Deudon, L. Brohan, S. Marsillac, Thin Solid Films 241, 4 (2002)
18.
Zurück zum Zitat N.D. Sankir, E. Aydin, M. Sankir, Int. J. Electrochem. Sci. 9, 3864 (2014) N.D. Sankir, E. Aydin, M. Sankir, Int. J. Electrochem. Sci. 9, 3864 (2014)
19.
Zurück zum Zitat A. Timoumi, Int. J. Adv. Res. Electr. Electron. Instrum. Eng. 2, 5207 (2013) A. Timoumi, Int. J. Adv. Res. Electr. Electron. Instrum. Eng. 2, 5207 (2013)
20.
Zurück zum Zitat M.A.M. Seyam, A.E. Bekheet, A. Elfalaky, Eur. Phys. J. Appl. Phys. 16, 99 (2001)CrossRef M.A.M. Seyam, A.E. Bekheet, A. Elfalaky, Eur. Phys. J. Appl. Phys. 16, 99 (2001)CrossRef
21.
Zurück zum Zitat B.D. Cullity, Elements of X-ray Diffraction (Addison-Wesley, Reading, 1978) B.D. Cullity, Elements of X-ray Diffraction (Addison-Wesley, Reading, 1978)
22.
Zurück zum Zitat N.F. Mott, E.A. Davis, Electronic Processes in Non Crystalline Materials (Clarendon, Oxford, 1979), p. 157 N.F. Mott, E.A. Davis, Electronic Processes in Non Crystalline Materials (Clarendon, Oxford, 1979), p. 157
23.
Zurück zum Zitat Lily, K. Kumari, K. Prasad, R.N.P. Choudhary, J. Alloy. Compd. 453, 325 (2008)CrossRef Lily, K. Kumari, K. Prasad, R.N.P. Choudhary, J. Alloy. Compd. 453, 325 (2008)CrossRef
24.
Zurück zum Zitat N.F. Mott, E.A. Davis, Electronic Process in Non-crystalline Materials (Clarendon Press, Oxford, 1979) N.F. Mott, E.A. Davis, Electronic Process in Non-crystalline Materials (Clarendon Press, Oxford, 1979)
26.
27.
Zurück zum Zitat Y. Matsuura, Y. Oshima, K. Tanaka, T. Yamabe, Synth. Met. 79, 7 (1996)CrossRef Y. Matsuura, Y. Oshima, K. Tanaka, T. Yamabe, Synth. Met. 79, 7 (1996)CrossRef
28.
29.
Zurück zum Zitat S. Chakraborty, M. Sadhukhan, B.K. Chaudhuri, H. Mori, H. Sakata, Mater. Chem. Phys. 50, 219 (1997)CrossRef S. Chakraborty, M. Sadhukhan, B.K. Chaudhuri, H. Mori, H. Sakata, Mater. Chem. Phys. 50, 219 (1997)CrossRef
31.
32.
Zurück zum Zitat B.J. Ingram, M.I. Bertoni, K.R. Poeppelmeier, T.O. Mason, Thin Solid Films 486, 86 (2005)CrossRef B.J. Ingram, M.I. Bertoni, K.R. Poeppelmeier, T.O. Mason, Thin Solid Films 486, 86 (2005)CrossRef
33.
Zurück zum Zitat O.O. Ilori, O. Osasona, M.A. Eleruja, G.O. Egharevba, G.A. Adegboyega, G. Chiodelli, G. Boudreault, C. Jeynes, E.O.B. Ajayi, Thin Solid Films 472, 387 (2005)CrossRef O.O. Ilori, O. Osasona, M.A. Eleruja, G.O. Egharevba, G.A. Adegboyega, G. Chiodelli, G. Boudreault, C. Jeynes, E.O.B. Ajayi, Thin Solid Films 472, 387 (2005)CrossRef
34.
37.
Zurück zum Zitat D.K. Pradhan, B.K. Samantary, R.N.P. Chaudhary, A.K. Thakur, Mater. Sci. Eng. B 116, 7 (2005)CrossRef D.K. Pradhan, B.K. Samantary, R.N.P. Chaudhary, A.K. Thakur, Mater. Sci. Eng. B 116, 7 (2005)CrossRef
38.
Zurück zum Zitat B.E. Kilbride, J.N. Coleman, J. Fraysse, P. Fournet, M. Cadek, A. Drury, S. Hutzler, S. Roth, W.J. Blau, J. Appl. Phys. 92, 4024 (2002)CrossRef B.E. Kilbride, J.N. Coleman, J. Fraysse, P. Fournet, M. Cadek, A. Drury, S. Hutzler, S. Roth, W.J. Blau, J. Appl. Phys. 92, 4024 (2002)CrossRef
40.
Zurück zum Zitat J.L. Barton, Verres Refract. 20, 328 (1966) J.L. Barton, Verres Refract. 20, 328 (1966)
42.
Zurück zum Zitat C. Sanz, C. Guillén, J. Herrero, Semicond. Sci. Technol. 28, 015004 (2013)CrossRef C. Sanz, C. Guillén, J. Herrero, Semicond. Sci. Technol. 28, 015004 (2013)CrossRef
43.
Zurück zum Zitat G.J. Brug, A.L.G. Van Den Eeden, M. Sluyters-Rehbach, J.H. Sluyters, J. Electroanal. Chem. 176, 275 (1984)CrossRef G.J. Brug, A.L.G. Van Den Eeden, M. Sluyters-Rehbach, J.H. Sluyters, J. Electroanal. Chem. 176, 275 (1984)CrossRef
45.
Zurück zum Zitat M. Hasan Zadeh Maha, M.-M. Bagheri-Mohagheghi, H. Azimi-Juybari, Thin Solid Films 536, 57 (2013)CrossRef M. Hasan Zadeh Maha, M.-M. Bagheri-Mohagheghi, H. Azimi-Juybari, Thin Solid Films 536, 57 (2013)CrossRef
46.
Zurück zum Zitat R.R. Pai, T.T. John, Y. Kashiwaba, T. Abe, K.P. Vijayakumar, C.S. Kartha, J. Mater. Sci. 40, 741 (2005)CrossRef R.R. Pai, T.T. John, Y. Kashiwaba, T. Abe, K.P. Vijayakumar, C.S. Kartha, J. Mater. Sci. 40, 741 (2005)CrossRef
Metadaten
Titel
AC conductivity properties of annealed In2S3 film deposited by spray technique
verfasst von
N. Bouguila
I. Najeh
N. Ben Mansour
H. Bouzouita
S. Alaya
Publikationsdatum
01.09.2015
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 9/2015
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-015-3238-2

Weitere Artikel der Ausgabe 9/2015

Journal of Materials Science: Materials in Electronics 9/2015 Zur Ausgabe

Neuer Inhalt