Activation of Nanoparticle and Alkaline Environment on Fly Ash Geopolymer Mortar

verfasst von : Tan No Nguyen, Huu Quoc Phong Le, Anh Tuan Le

Erschienen in: ICSCEA 2021

Verlag: Springer Nature Singapore

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The goal of this study is to evaluate the influences of nanoparticles on the mechanical property of fly ash geopolymer mortars. The nano-silica (NS) and nano-alumina (NA) were added to geopolymer mortar with a various amount of nanoparticle-to-fly ash in range from 5 to 25% by weight, respectively. In this research, the different NS/NA ratios in range from 0.5 to 2, by weight, were investigated. For the geopolymerization process, the alkaline solutions (AS) including sodium hydroxide (SH) and sodium silicate solution (SS) were mixed with the SH/SS ratio of 1, by weight. The different ratios of alkaline liquid to fly ash in range from 0.4 to 0.6, by weight, were investigated. The results were focused on the geopolymerization between nanoparticles and alumino-silicate resource by strength in ambient temperature condition. The compressive strength of geopolymer mortar can be up to 22.62 MPa. The suitable mix proportion can be obtained by amount of 5% nanoparticle by fly ash weight, a ratio of NS/NA as 0.5, and ratio of AS/FA as 0.5, by weight, respectively.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Assaedi H, Shaikh FUA, Low IM (2015) Characteristics of nanosilica-geopolymer nanocomposites and mixing effect. Int J Chem Mol Eng 9(12):1471–1478 Assaedi H, Shaikh FUA, Low IM (2015) Characteristics of nanosilica-geopolymer nanocomposites and mixing effect. Int J Chem Mol Eng 9(12):1471–1478
2.
Zurück zum Zitat Bakharev T (2005) Resistance of geopolymer materials to acid attack. Cem Concr Res 35(4):658–670CrossRef Bakharev T (2005) Resistance of geopolymer materials to acid attack. Cem Concr Res 35(4):658–670CrossRef
3.
Zurück zum Zitat Cheng TW, Chiu JP (2003) Fire-resistant geopolymer produced by granulated blast furnace slag. Miner Eng 16(3):205–210CrossRef Cheng TW, Chiu JP (2003) Fire-resistant geopolymer produced by granulated blast furnace slag. Miner Eng 16(3):205–210CrossRef
4.
Zurück zum Zitat Comrie DC, Kriven WM (2012) Composite cold ceramic geopolymer in a refractory application. Ceram Trans 153:211–225 Comrie DC, Kriven WM (2012) Composite cold ceramic geopolymer in a refractory application. Ceram Trans 153:211–225
5.
Zurück zum Zitat Davidovits J (2005) Geopolymer chemistry and sustainable development. The Poly(sialate) terminology: A very useful and simple model for the promotion and understanding of green-chemistry. Geopolymer Green Chemistry and Sustainable Development Solutions, Geopolymer 1:9–17 Davidovits J (2005) Geopolymer chemistry and sustainable development. The Poly(sialate) terminology: A very useful and simple model for the promotion and understanding of green-chemistry. Geopolymer Green Chemistry and Sustainable Development Solutions, Geopolymer 1:9–17
6.
Zurück zum Zitat Khale D, Chaudhary R (2007) Mechanism of geopolymerization and factors influencing its development: A review. J Mater Sci 42:729–746CrossRef Khale D, Chaudhary R (2007) Mechanism of geopolymerization and factors influencing its development: A review. J Mater Sci 42:729–746CrossRef
7.
Zurück zum Zitat Kim B, Lee S (2020) Review on characteristics of metakaolin-based geopolymer and fast setting. J Korean Ceram Soc 57(4):368–377CrossRef Kim B, Lee S (2020) Review on characteristics of metakaolin-based geopolymer and fast setting. J Korean Ceram Soc 57(4):368–377CrossRef
8.
Zurück zum Zitat Kwon H-M, Nguyen TN, Le TA (2009) Improvement of the strength of acrylic emulsion polymer-modified mortar in high temperature and high humidity by blast furnace slag. KSCE J Civ Eng 13(1):23–30CrossRef Kwon H-M, Nguyen TN, Le TA (2009) Improvement of the strength of acrylic emulsion polymer-modified mortar in high temperature and high humidity by blast furnace slag. KSCE J Civ Eng 13(1):23–30CrossRef
9.
Zurück zum Zitat Naskar S, Chakraborty AK (2016) Effect of nano materials in geopolymer concrete. Perspect Sci 8:273–275CrossRef Naskar S, Chakraborty AK (2016) Effect of nano materials in geopolymer concrete. Perspect Sci 8:273–275CrossRef
10.
Zurück zum Zitat Nguyen KT, Nguyen QD, Le TA, Shin J, Lee K (2020) Analyzing the compressive strength of green fly ash based geopolymer concrete using experiment and machine learning approaches. Constr Build Mater 247:118581CrossRef Nguyen KT, Nguyen QD, Le TA, Shin J, Lee K (2020) Analyzing the compressive strength of green fly ash based geopolymer concrete using experiment and machine learning approaches. Constr Build Mater 247:118581CrossRef
11.
Zurück zum Zitat Nguyen T-N, Le A-T, Nguyen M-T (2017) Factors influencing strength development in soft soil clay mixed rice husk ash based geopolymer. Adv Exp Mech 2:153–158 Nguyen T-N, Le A-T, Nguyen M-T (2017) Factors influencing strength development in soft soil clay mixed rice husk ash based geopolymer. Adv Exp Mech 2:153–158
12.
Zurück zum Zitat Pham KVA, Nguyen TK, Le TA, Han SW, Lee G, Lee K (2019) Assessment of performance of fiber reinforced geopolymer composites by experiment and simulation analysis. Appl Sci 9(16):3424CrossRef Pham KVA, Nguyen TK, Le TA, Han SW, Lee G, Lee K (2019) Assessment of performance of fiber reinforced geopolymer composites by experiment and simulation analysis. Appl Sci 9(16):3424CrossRef
13.
Zurück zum Zitat Phoo-ngernkham T, Chindaprasirt P, Sata V, Hanjitsuwan S, Hatanaka S (2014) The effect of adding nano-SiO2 and nano-Al2O3 on properties of high calcium fly ash geopolymer cured at ambient temperature. Mater Des 55:58–65CrossRef Phoo-ngernkham T, Chindaprasirt P, Sata V, Hanjitsuwan S, Hatanaka S (2014) The effect of adding nano-SiO2 and nano-Al2O3 on properties of high calcium fly ash geopolymer cured at ambient temperature. Mater Des 55:58–65CrossRef
14.
Zurück zum Zitat Rattanasak U, Chindaprasirt P (2009) Influence of NaOH solution on the synthesis of fly ash geopolymer. Miner Eng 22(12):1073–1078CrossRef Rattanasak U, Chindaprasirt P (2009) Influence of NaOH solution on the synthesis of fly ash geopolymer. Miner Eng 22(12):1073–1078CrossRef
15.
Zurück zum Zitat Stefanidou M, Papayianni I (2012) Influence of nano-SiO2 on the Portland cement pastes. Compos B Eng 43(6):2706–2710CrossRef Stefanidou M, Papayianni I (2012) Influence of nano-SiO2 on the Portland cement pastes. Compos B Eng 43(6):2706–2710CrossRef
16.
Zurück zum Zitat Turner LK, Collins FG (2013) Carbon dioxide equivalent (CO2-e) emissions: A comparison between geopolymer and OPC cement concrete. Constr Build Mater 43:125–130CrossRef Turner LK, Collins FG (2013) Carbon dioxide equivalent (CO2-e) emissions: A comparison between geopolymer and OPC cement concrete. Constr Build Mater 43:125–130CrossRef
17.
Zurück zum Zitat Zidi Z, Ltifi M, Ben Ayadi Z, El Mir L (2019) Synthesis of nano-alumina and their effect on structure, mechanical and thermal properties of geopolymer. J Asian Ceram Soc 7(4):524–535CrossRef Zidi Z, Ltifi M, Ben Ayadi Z, El Mir L (2019) Synthesis of nano-alumina and their effect on structure, mechanical and thermal properties of geopolymer. J Asian Ceram Soc 7(4):524–535CrossRef
Metadaten
Titel
Activation of Nanoparticle and Alkaline Environment on Fly Ash Geopolymer Mortar
verfasst von
Tan No Nguyen
Huu Quoc Phong Le
Anh Tuan Le
Copyright-Jahr
2023
Verlag
Springer Nature Singapore
DOI
https://doi.org/10.1007/978-981-19-3303-5_29