Adsorption behaviors of CO₂ and CH₄ on zeolites JSR and Na_nJSR using the GCMC simulations

The adsorption behaviors of CO₂ and CH₄ on new siliceous zeolites JSR and Na_nJSR (n = 2, 8, 16) were simulated using the Grand Canonical Monte Carlo method. The adsorption isotherms of CO₂ became higher with an increase in the Na⁺ number at a low pressure range (<150 kPa), whereas the isotherms showed a crossover with increasing pressure and the adsorption amount became smaller at a high pressure range (>850 kPa). With an increase in Na⁺ number, the pore volume decreased as the pore space was occupied by increasing Na⁺ ions. Additionally, two energy peaks on the interaction energy curves implied that CO₂ was adsorbed on two active sites. On the other hand, the adsorption amount of CH₄ decreased with an increase in the Na⁺ number and only one energy peak was observed. Adsorption isotherms were well fitted with the Langmuir and Freundlich equations up to 1000 kPa and the adsorption affinity of CO₂ on Na₁₆JSR zeolite was highest. The adsorption capacities of CO₂ in the studied zeolites were up to 38 times higher than those of CH₄. Diffusion constants of CO₂ and CH₄ decreased with an increase in the adsorbed amount and Na⁺ number. Considering the adsorbed amount, adsorption selectivity and affinity, zeolites JSR with a low Na⁺ number (JSR and Na₂JSR) is a good candidate for a pressure swing adsorption in the separation of CO₂/CH₄ mixture whereas JSR zeolites with high Na⁺ ratios (Na₁₆JSR and Na₈JSR) may be a better selection for a vacuum swing adsorption.