The paper is devoted to the structure and behavior of Cu-Ni-Zn system cast bar under the lost-wax method. A method of estimating casting mold fillability has been proposed. The method involves determining perforated plate-filled cell fraction. The effect of casting temperature on casting mold fillability and casting bar structure has been studied. The casting temperature of Cu-15Ni-20Zn alloy is determined as 1190 °C; it ensures the best casting mold fillability. Moreover, the influence of an alloying addition such as Sn and Al on casting mold fillability and the behavior of Cu-Ni-Zn alloy under mechanical testing have been studied. The addition of 4.0 mass % Sn and 0.4 mass % Al enables increasing casting mold fillability by 5% and reducing casting temperature to 1170 °C. It has been established that the alloying addition of elements such as Sn and Al makes a more compact and close-grained microstructure, increases the mechanical properties of Cu-Ni-Zn alloy by 10–12% and improves the cast bar surface considerably. In all cases melting and casting were performed by an INDUTHERM-MUVV700 machine. Casting investment mold annealing was carried out in the same step-by-step conditions. The temperature of all molds before casting was set at 560 °C.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:
Kurdumov, A. V., Pikunov, M. V., Chursin, V. M., & Bibikov, E. A. (1986). Castings production from non-ferrous alloys (pp. 217–218). Moscow: Metallurgy.
Osintsev, O. E., & Fedorov, V. N. (2004). Copper and copper alloys (pp. 186–187). Moscow: Mechanical engineering.
Gruzdeva I. A. (2013). Casting mold fillability studying by alloy МНЦ15-20 under the lost-wax process. In S. S. Gerasimov, A.V. Sulitsin, (Eds.), Proceeding of the 13th Conference Russian Founders, (pp. 254–259), Ekaterinburg.
- Alloying Addition Effect on the Structure and Behavior of a Cu-Ni-Zn Three-Component System Alloy Under Lost-Wax Casting
I. A. Gruzdeva
S. S. Gerasimov
- Chapter 2
in-adhesives, MKVS, Zühlke/© Zühlke, Nordson/© Nordson, ViscoTec/© ViscoTec, Hellmich GmbH/© Hellmich GmbH