Alpha and deuteron irradiation effects on silica nanoparticles

Zeitschrift:
Journal of Materials Science > Ausgabe 18/2014
Autoren:
A. Alessi, S. Agnello, G. Buscarino, M. Cannas, F. M. Gelardi, A. Sporea, D. Sporea, I. Vâţă

Abstract

We present an experimental investigation focused on the effects of alpha and deuteron irradiation on different silica nanoparticles. The study has been devoted also to characterize the induced point defects and the eventual structural modifications to evaluate the effects of the different irradiation source in comparison with the bulk materials. After irradiation up to about 1016 ions cm−2, we performed electron paramagnetic resonance (EPR), photoluminescence (PL), infrared (IR) absorption, Raman, and atomic force microscopy (AFM) measurements. We found that the two types of irradiation qualitatively induce comparable effects. Furthermore, irradiation generates the so-called twofold coordinated Si and the H(I) point defects, originating from the reaction of the former with hydrogen atoms. The occurrence of these defects is a not trivial and interesting finding due to its connection to irradiation-induced oxygen deficiency, not yet evidenced by other irradiation of silica nanoparticles. We also detected the E′Si paramagnetic centers and found that their lineshape at the highest fluence, independently from the nanoparticles size and irradiation source, is different from the one observed in the bulk. Furthermore, the integral of the E′Si signal does not depend significantly on the nanoparticles size differing from previous irradiation with β-ray of the same nanoparticles. AFM images indicate the absence of significant radiation induced sintering between the nanoparticles in the plan orthogonal to the irradiation direction suggesting the absence of morphological changes, whereas IR measurements suggest the occurrence of some structural modifications in all the nanoparticles, which consist in the decrease of the peak value of the Si–O–Si angle distribution. Finally, irradiation effects are induced not uniformly along the irradiation direction, as supported also by micro-Raman investigation of an irradiated bulk silica material and simulations of ions penetration profiles. These results suggest the occurrence of some irradiation effects due to light ion bombardment specific of nanoparticles.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 18/2014

Journal of Materials Science 18/2014 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise