Analysis of Diffusional Solidification in a Wide-Gap Brazing Powder Mixture Using Differential Scanning Calorimetry

verfasst von: Stephen F. Corbin, D. Clark Murray, Alain Bouthillier

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 12/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The diffusional solidification (DS) of a mixed powder system, consisting of pure Ni base metal powder and BNi-2 braze powder, suitable for wide-gap brazing was investigated using differential scanning calorimetry (DSC) and parallel microstructural examination. It was determined that very little interdiffusion between the powders developed in the solid state prior to braze powder melting. Once liquid formed, rapid DS occurred such that, when the powders were loosely mixed together, only 20 to 50 wt pct of the potential liquid fraction actually developed, leading to poor densification. Separating the braze and Ni into a layered structure leads to less DS, increased liquid formation (i.e., 35 to 80 wt pct of the potential liquid fraction) and improved densification. The rate of isothermal solidification in layered structures consisting of 30 and 40 wt pct BNi-2 braze material was determined using DSC. After 30 minutes of braze time at 1323 K (1050 °C), complete IS occurred, thus avoiding the formation of a continuous network of large borides. The final microstructure of the IS mixtures consisted of a continuous matrix of solid solution Ni, with isolated and dispersed borides.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat O.A. Ojo, N.L. Richards and M.C. Charturvedi: Sci. Technol. Weld. Joining, 2004, vol. 9, pp. 209-220.CrossRef O.A. Ojo, N.L. Richards and M.C. Charturvedi: Sci. Technol. Weld. Joining, 2004, vol. 9, pp. 209-220.CrossRef
2.
Zurück zum Zitat C.E. Campbell and W.J. Boettinger: Metall. Trans. A, 2000, vol. 31A, pp. 2835-2847.CrossRef C.E. Campbell and W.J. Boettinger: Metall. Trans. A, 2000, vol. 31A, pp. 2835-2847.CrossRef
3.
Zurück zum Zitat M.A. Arafin, M. Medraj, D.P. Turner and P. Bocher, Mat. Sci. Eng. A, 2007, vol. 447A, pp. 125-133.CrossRef M.A. Arafin, M. Medraj, D.P. Turner and P. Bocher, Mat. Sci. Eng. A, 2007, vol. 447A, pp. 125-133.CrossRef
4.
Zurück zum Zitat O.A. Idawu, N.L. Richards, and M.C. Charturvedi: Mater. Sci. Eng. A, 2005, vol. 397, pp. 98–112. O.A. Idawu, N.L. Richards, and M.C. Charturvedi: Mater. Sci. Eng. A, 2005, vol. 397, pp. 98–112.
5.
Zurück zum Zitat X. Huang, and W. Miglietti: J. Eng. Gas Turbines Power, 2012, vol. 134, Article No. 010801-1. X. Huang, and W. Miglietti: J. Eng. Gas Turbines Power, 2012, vol. 134, Article No. 010801-1.
6.
Zurück zum Zitat S. Schoonbaert, X. Huang, S. Yandt, and P. Au: J. Eng. Gas Turbines Power, 2008, vol. 130, Article No. 032101-1. S. Schoonbaert, X. Huang, S. Yandt, and P. Au: J. Eng. Gas Turbines Power, 2008, vol. 130, Article No. 032101-1.
7.
Zurück zum Zitat N.C. Sheng, J.D. Liu, T. Jin, X.F. Sun, and Z.Q. Hu: Metall. Mater. Trans. A, 2013, vol. 44A, pp. 1793-1804.CrossRef N.C. Sheng, J.D. Liu, T. Jin, X.F. Sun, and Z.Q. Hu: Metall. Mater. Trans. A, 2013, vol. 44A, pp. 1793-1804.CrossRef
8.
Zurück zum Zitat X.W. Wu, R.S. Schandel, H.P. Seow and H. Li: J. Mater. Process. Technol., 2001, vol. 113, pp. 215-221.CrossRef X.W. Wu, R.S. Schandel, H.P. Seow and H. Li: J. Mater. Process. Technol., 2001, vol. 113, pp. 215-221.CrossRef
9.
Zurück zum Zitat X. Huang, D. Nagy, and W. Chen: Proc. ASME Turbo Expo: Power Land, Sea, Air, 2009, pp. 721–29. X. Huang, D. Nagy, and W. Chen: Proc. ASME Turbo Expo: Power Land, Sea, Air, 2009, pp. 721–29.
10.
Zurück zum Zitat X. Huang, S. Yandt, D. Nagy, and M. Yao: Proc. ASME Turbo Expo: Power Land, Sea, Air, 2007, pp. 25–33. X. Huang, S. Yandt, D. Nagy, and M. Yao: Proc. ASME Turbo Expo: Power Land, Sea, Air, 2007, pp. 25–33.
11.
Zurück zum Zitat D. M. Turriff and S.F. Corbin: Metall. Mater. Trans. A, 2008, vol. 39A, pp. 28-38.CrossRef D. M. Turriff and S.F. Corbin: Metall. Mater. Trans. A, 2008, vol. 39A, pp. 28-38.CrossRef
Metadaten
Titel
Analysis of Diffusional Solidification in a Wide-Gap Brazing Powder Mixture Using Differential Scanning Calorimetry
verfasst von
Stephen F. Corbin
D. Clark Murray
Alain Bouthillier
Publikationsdatum
14.10.2016
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 12/2016
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-016-3799-6

Weitere Artikel der Ausgabe 12/2016

Metallurgical and Materials Transactions A 12/2016 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.