Analysis of Microstructure Effects on Edge Crack of Thin Strip During Cold Rolling

verfasst von: Haibo Xie, Zhengyi Jiang, W. Y. Daniel Yuen

Erschienen in: Metallurgical and Materials Transactions B | Ausgabe 6/2011

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Edge cracks in cold rolling of the thin strip affect the strip quality and productivity significantly. In this study, an experimental and mechanical investigation on microstructures has been carried out to study the edge crack formation during cold rolling of the thin strip. The effects of the feed material microstructures on the edge crack evolution were studied employing optical microscopy and scanning electron microscopy (SEM). Experimental observation indicates that fine grain occurs in hot-rolled microstructure and coarse grain is produced in ferritic rolled microstructure. Different grain sizes affect significantly the formation mechanics of the microcrack, crack initiation, and orientation of crack extension. The grain size and grain boundaries effects on crack retardation are discussed also during edge crack initiation. During the crack growth in coarse grain, most edge crack tips will blunt, which improves the crack toughness by causing less stress concentration. Overall, the fine microstructure shows a good crack initiation resistance, whereas the coarse microstructure has a better resistance to crack propagation. This research provides additional understanding of the mechanism of microstructure influence on edge crack evolution of cold strip rolling, which could be helpful for developing defect-free thin strip.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
2.
Zurück zum Zitat T. Zhai, A.J. Wilkinson, and J.W. Martin: Acta Mater., 2000, vol. 48, pp. 4917-27.CrossRef T. Zhai, A.J. Wilkinson, and J.W. Martin: Acta Mater., 2000, vol. 48, pp. 4917-27.CrossRef
3.
Zurück zum Zitat M.M. Al-Mousawi, A.M. Daragheh, S.K. Ghosh, and D.K. Harrison: J. Mater. Process. Tech., 1992, vol. 32, pp. 461-70.CrossRef M.M. Al-Mousawi, A.M. Daragheh, S.K. Ghosh, and D.K. Harrison: J. Mater. Process. Tech., 1992, vol. 32, pp. 461-70.CrossRef
4.
5.
Zurück zum Zitat T. Wierzbicki, Y.B. Bao, Y-W Lee, and Y.L. Bai: Int. J. Mech. Sci., 2005, vol. 47, pp. 719-43.CrossRef T. Wierzbicki, Y.B. Bao, Y-W Lee, and Y.L. Bai: Int. J. Mech. Sci., 2005, vol. 47, pp. 719-43.CrossRef
6.
Zurück zum Zitat Y.D. Wang, H.B. Tian, A. Stoica, X.L. Wang, P.K. Liaw, and J.W. Richardson: Nat. Mater., 2003, vol. 2, pp. 101-06.CrossRef Y.D. Wang, H.B. Tian, A. Stoica, X.L. Wang, P.K. Liaw, and J.W. Richardson: Nat. Mater., 2003, vol. 2, pp. 101-06.CrossRef
8.
9.
Zurück zum Zitat N. Ishikawa, D.M. Parks, and M. Kurihara: ISIJ Int., 2001, vol. 41, pp. 76-85.CrossRef N. Ishikawa, D.M. Parks, and M. Kurihara: ISIJ Int., 2001, vol. 41, pp. 76-85.CrossRef
10.
Zurück zum Zitat L. Zhen, Y.X. Cui, W.Z. Shao, and D.Z. Yang: Mater. Sci. Eng. A, 2002, vol. 336, pp. 135-42.CrossRef L. Zhen, Y.X. Cui, W.Z. Shao, and D.Z. Yang: Mater. Sci. Eng. A, 2002, vol. 336, pp. 135-42.CrossRef
11.
Zurück zum Zitat S. Daly, A. Miller, G. Ravichandran, and K. Bhattacharya: Acta Mater., 2007, vol. 55, pp. 6322-30.CrossRef S. Daly, A. Miller, G. Ravichandran, and K. Bhattacharya: Acta Mater., 2007, vol. 55, pp. 6322-30.CrossRef
12.
Zurück zum Zitat F.C. Campbell: Elements of Metallurgy and Engineering Alloys, ASM International, Materials Park, OH, 2008, pp. 120-25. F.C. Campbell: Elements of Metallurgy and Engineering Alloys, ASM International, Materials Park, OH, 2008, pp. 120-25.
13.
14.
Zurück zum Zitat J. Konishi, M. Milizer, J.K. Brimacombe, and I.V. Samarasekera: Metall. Mater. Trans. B, 2002, vol. 33B, pp. 413-23.CrossRef J. Konishi, M. Milizer, J.K. Brimacombe, and I.V. Samarasekera: Metall. Mater. Trans. B, 2002, vol. 33B, pp. 413-23.CrossRef
15.
Zurück zum Zitat F. Czetinski, A. Brodtka, J.Y. Cho, A. Zielinska-Lipiec, J.H. Sunwoo, and J.A. Szpunar: Scripta Mater., 1997, vol. 37, pp. 1231-35.CrossRef F. Czetinski, A. Brodtka, J.Y. Cho, A. Zielinska-Lipiec, J.H. Sunwoo, and J.A. Szpunar: Scripta Mater., 1997, vol. 37, pp. 1231-35.CrossRef
16.
Zurück zum Zitat M.H. Han, S. Lee, N.J. Kim, K.J. Lee, T. Chung, and G. Byun: Mater. Sci. Eng. A, 1999, vol. 264, pp. 47-59.CrossRef M.H. Han, S. Lee, N.J. Kim, K.J. Lee, T. Chung, and G. Byun: Mater. Sci. Eng. A, 1999, vol. 264, pp. 47-59.CrossRef
17.
Zurück zum Zitat H. Riedel, F. Andrieux, T. Walde, and K.-F. Karhausen: Steel Res. Int., 2007, vol. 78, pp. 818-24. H. Riedel, F. Andrieux, T. Walde, and K.-F. Karhausen: Steel Res. Int., 2007, vol. 78, pp. 818-24.
18.
Zurück zum Zitat P.F. Thomson and N.M. Burman: Mater. Sci. Eng., 1980, vol. 45, pp. 95-107.CrossRef P.F. Thomson and N.M. Burman: Mater. Sci. Eng., 1980, vol. 45, pp. 95-107.CrossRef
19.
Zurück zum Zitat N. Narasaiah and K.K. Ray: Mater. Sci. Eng. A, 2005, vol. 392, pp. 269-77.CrossRef N. Narasaiah and K.K. Ray: Mater. Sci. Eng. A, 2005, vol. 392, pp. 269-77.CrossRef
20.
Zurück zum Zitat H. Somekawa, T. Inoue, and T. Mukai: Mater. Sci. Eng. A, 2010, vol. 527, pp. 1761-68.CrossRef H. Somekawa, T. Inoue, and T. Mukai: Mater. Sci. Eng. A, 2010, vol. 527, pp. 1761-68.CrossRef
21.
Zurück zum Zitat Y. Nakai and K. Tanaka: Eng. Fract. Mech., 1961, vol. 15, pp. 291-302.CrossRef Y. Nakai and K. Tanaka: Eng. Fract. Mech., 1961, vol. 15, pp. 291-302.CrossRef
23.
24.
Zurück zum Zitat D.A. Curry and J.F. Knott: Met. Sci., 1976, vol. 1, pp. 1-6. D.A. Curry and J.F. Knott: Met. Sci., 1976, vol. 1, pp. 1-6.
25.
Zurück zum Zitat C. Mercer and W.O. Soboyejo: Scripta Mater., 1996, vol. 35, pp. 17-22.CrossRef C. Mercer and W.O. Soboyejo: Scripta Mater., 1996, vol. 35, pp. 17-22.CrossRef
26.
Zurück zum Zitat Z.H.J. Gu and W.Y.D. Yuen: Proc. SEAISI2007 Conference 2007, Session 12, Paper 1, 2007, Bali, Indonesia. Z.H.J. Gu and W.Y.D. Yuen: Proc. SEAISI2007 Conference 2007, Session 12, Paper 1, 2007, Bali, Indonesia.
27.
28.
Zurück zum Zitat S. Mall, S.A. Namjoshi, and W.J. Porter: Mater. Sci. Eng. A, 2004, vol. 383, pp. 334-40.CrossRef S. Mall, S.A. Namjoshi, and W.J. Porter: Mater. Sci. Eng. A, 2004, vol. 383, pp. 334-40.CrossRef
Metadaten
Titel
Analysis of Microstructure Effects on Edge Crack of Thin Strip During Cold Rolling
verfasst von
Haibo Xie
Zhengyi Jiang
W. Y. Daniel Yuen
Publikationsdatum
01.12.2011
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions B / Ausgabe 6/2011
Print ISSN: 1073-5615
Elektronische ISSN: 1543-1916
DOI
https://doi.org/10.1007/s11663-011-9540-3

Weitere Artikel der Ausgabe 6/2011

Metallurgical and Materials Transactions B 6/2011 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.