01.02.2013 | Original Paper | Ausgabe 2/2013

Journal of Polymer Research 2/2013

Apparent kinetics of nonisothermal high temperature oxidative degradation of ethylene homopolymers: effects of residual catalyst surface chemistry and structure

Zeitschrift:
Journal of Polymer Research > Ausgabe 2/2013
Autoren:
Muhammad Atiqullah, Mohammad M. Hossain, Syed Masiur Rahman, Khurshid Alam, Hasan A. Al-Muallem, Abdulrahman F. Alharbi, Ikram Hussain, Anwar Hossaen

Abstract

The effects of two supported residual catalysts—one Ziegler-Natta and another metallocene—on the nonisothermal thermooxidative degradation of the resulting ethylene homopolymers were investigated using TGA experiments and kinetic modeling. The rigorous constitutive kinetic model (developed in this study), unlike the analytical Horowitz and Metzger model, fitted very well to the entire TGA curve, without distribution of activation energy E a , for n (overall degradation order) = 1 for both polymers. Neither n nor E a varied as a function of fractional weight loss of the polymer. Hence, the proposed unified molecular level concept of surface chemistry and structure of the residual catalysts held all through the degradation process. The above feature of n and E a also indicates the suitability of the model formulation and the effectiveness of the parameter-estimation algorithm. Random polymer chain scission, with the cleavage of the −C−C− and the −O−O− (hydroperoxide) bonds, prevailed. The types of residual catalyst surface chemistry and structure varied the bond cleavage process. The metallocene Zr residual catalyst caused more thermooxidative degradation in MetCat HomoPE than what the Ti one did in Z-N HomoPE. The rigorous constitutive model-predicted apparent kinetic energy E a , and frequency factor Z also support this finding. The proposed degradation mechanism suggests that the Zr residual catalyst more (i) decreased the activation energy required to decompose the −C−C− and the −O−O− bonds, and (ii) eliminated β-hydrogen (by the carbonyl functionalities) from the polymer chains. These findings were attributed to the differences in surface chemistry and structure of the residual catalysts. Therefore, the current study presents a rigorous constitutive kinetic model that duly illustrates the influence of the characteristic surface chemistry and structure of the residual catalysts on the high temperature oxidative degradation of polyethylenes.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 2/2013

Journal of Polymer Research 2/2013 Zur Ausgabe

Premium Partner

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen. 

    Bildnachweise