Automobile Corrosion Mechanism and Cases Analysis

verfasst von : Dapeng Zhao, Minglei Liu, Guofeng Li, Chunyan Tan, Bo Feng

Erschienen in: Proceedings of the 19th Asia Pacific Automotive Engineering Conference & SAE-China Congress 2017: Selected Papers

Verlag: Springer Singapore

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

This paper mainly details failure causes and characteristics of micro-difference corrosion, pitting, crevice corrosion, galvanic corrosion, stress corrosion cracking and corrosion fatigue from the perspective of electrochemical corrosion theory. Furthermore, with reference to exterior environment factor and automobile own factor in combination with actual road intensified corrosion test, corrosion reasons are analyzed in details and corresponding anticorrosion measures are proposed.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Six-Sigma Robust Optimization on the NVH Performance of the CRFM Based on Isight

Nächstes Kapitel Capacity Allocation of Driving System and Braking System for Distributed Drive Electric Vehicle

Cao C (2008) Principles of electrochemistry of corrosion. Chemical Industry Press, Beijing, pp 12–31

Perez (2003) Electrochemistry and corrosion science. Chemical Industry Press, Beijing, 68–73

Li H, Jiang Z (2013) Corrosion behavior of ferritic stainless steel with 15wt% chromium for the automobile exhaust system. Metall Mater 20(9):850–859

Tzanakis I, Bolzoni L, Eskin DG, Hadfield M (2017) Evaluation of cavitation erosion behavior of commercial steel grades used in the design of fluid machinery. Metall Mater Trans A 5:2193–2206CrossRef

Xiaohong Z, Quanzhong G (2015) Galvanic corrosion behavior of couples of hot rolled steel SS400 and cold rolled steel ST12 with two coating. J Chin Soc Corrosion Prot 1:86–90

Zhao J, Chevil K, Eadie R (2017) Crack growth modeling and life prediction of pipeline steels exposed to near-neutral pH environments: dissolution crack growth and occurrence of crack dormancy in stage I. Metall Mater Trans A 4:1629–1640CrossRef

Burgstaller W, Schimo G, Hassel AW (2017) J Solid State Electrochem, 1–12

Shi Y, Liang P, Liu F (2014) Automobile zinc galvanized steel corrosion behavior in deicing salt solution. Mater Prot 47(3):53–55

Ning S, Shi Y, Liang P, Lin L (2015) The corrosion behavior of automobile steel in the snow water with snow melting salt. J Liaoning Shihua Univ 35(1):58–61

10.

Serebryakov An V, Shulin EL, Serebryakov Al V, Bogatov AA (2004) Metallurgist (9):487–490

11.

Leng A, Streekel H, Stratmann M (1999) The delamination of polymeric coating from steel. Part 2: First stage of determination, effect of type and concerntration of cations on delamination. Corros Sci 41:579CrossRef

12.

Choi Y-S, Kim J-G, Kim Y-S, Huh J-Y (2008) Corrosion characteristics of coated automotive parts subjected to field and proving ground tests. Int J Automotive Technology, 2008, No.5 p. 625–631CrossRef

13.

Wapner K, Stratmann M, Grundermier G (2006) Electrochim Acta 51(16):3303–3315CrossRef

14.

Zhao D (2014) Study on hydrogen permeation and hydrogen Embrittlement of X80 Pipeline Steel and its HAZ Caused by Cathodic Protection. Master 3–12

15.

Zhu X, Chen X (2013) Dacromet fastener corrosion analysis and improvement measure. Locomotive & Rolling Stock Technology 41–42

16.

Wang Y, Cai Y (2013) Discussion of common corrosions from vehicel corrosion test and anti-corrosive optimization. In: The 7th Sino-American Academic Symposium on environmental corrosion and degradation tests of material, 2013, May 20–21, Guanzhou, pp 31–37

17.

Jie W-z, Peng W, Zhao Z (2015) Representative corrosion problems analysis of automobile accelerated corrosion test. Experience Exchange 7(29):43–45

Titel: Automobile Corrosion Mechanism and Cases Analysis
verfasst von: Dapeng Zhao
Minglei Liu
Guofeng Li
Chunyan Tan
Bo Feng
Verlag: Springer Singapore
Buch: Proceedings of the 19th Asia Pacific Automotive Engineering Conference & SAE-China Congress 2017: Selected Papers
Print ISBN: 978-981-10-8505-5

Electronic ISBN: 978-981-10-8506-2

Copyright-Jahr: 2019
DOI: https://doi.org/10.1007/978-981-10-8506-2_18

Springer Professional

Abstract

Bitte loggen Sie sich ein, um Zugang zu Ihrer Lizenz zu erhalten.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Springer Professional "Technik"

Premium Partner