Characterization of damage in forward rod extruded parts

verfasst von: Oliver Hering, Anthony Dunlap, A. Erman Tekkaya, Anke Aretz, Alexander Schwedt

Erschienen in: International Journal of Material Forming | Ausgabe 6/2020

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In addition to strain hardening and residual stress, damage influences the product performance of forward rod extruded parts. Damage is usually neglected and difficult to quantify. The evolution of ductile damage in metal forming is closely correlated to the load path. An experimental approach using automated energy dispersive X-ray spectroscopy (EDX) particle analysis in scanning electron microscopy (SEM) is used to successfully quantify the void area fraction and obtain information on ductile damage. The method is performed on forward rod extruded 16MnCrS5 workpieces with varying extrusion strains and shoulder opening angles (and thus varying underlying load paths). The quantified damage is directly correlated to the load path, which can be described by the stress triaxiality evolution during forming. Density measurements were performed to further validate the results. By observing the change of strain-weighted stress triaxiality and maximum stress triaxiality, it is shown, that the maximum stress triaxiality is the decisive parameter enabling void nucleation.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Anhänge
Nur mit Berechtigung zugänglich
Literatur
1.
Zurück zum Zitat Lange K, Kammerer M, Pöhlandt K, Schöck J (2008) Fließpressen. Springer, HeidelbergCrossRef Lange K, Kammerer M, Pöhlandt K, Schöck J (2008) Fließpressen. Springer, HeidelbergCrossRef
2.
Zurück zum Zitat Jennison HC (1930) Certain types of defects in copper wire caused by improper dies and drawing practice. AIME Trans 89:121–139 Jennison HC (1930) Certain types of defects in copper wire caused by improper dies and drawing practice. AIME Trans 89:121–139
6.
Zurück zum Zitat Zimerman Z, Darlington H, Kottcamp EH (1971) Selection of operating parameters to prevent central bursting defects during cold extrusion. In: Metal forming: interrelation between theory and practice. Springer US, Boston, MA, pp 47–62CrossRef Zimerman Z, Darlington H, Kottcamp EH (1971) Selection of operating parameters to prevent central bursting defects during cold extrusion. In: Metal forming: interrelation between theory and practice. Springer US, Boston, MA, pp 47–62CrossRef
18.
Zurück zum Zitat Laskin A, JPJAC C (2001) Automated single-particle SEM/EDX analysis of submicrometer particles down to 0.1 μm. Anal Chem 73(5):1023–1029CrossRef Laskin A, JPJAC C (2001) Automated single-particle SEM/EDX analysis of submicrometer particles down to 0.1 μm. Anal Chem 73(5):1023–1029CrossRef
19.
Zurück zum Zitat Mohr D (2015) Basic notions of fracture mechanics - ductile fracture [WWW Document]. ETH Zurich, Dep. Mech. Process Eng. Comput. Model. Mater. Manuf Mohr D (2015) Basic notions of fracture mechanics - ductile fracture [WWW Document]. ETH Zurich, Dep. Mech. Process Eng. Comput. Model. Mater. Manuf
21.
22.
Zurück zum Zitat Nadolski D (2018) Einfluss des Herstellungsverfahrens und der Wärmebehandlung auf das Verzugsverhalten unterschiedlicher Bauteilgeometrien. Shaker, Aachen Nadolski D (2018) Einfluss des Herstellungsverfahrens und der Wärmebehandlung auf das Verzugsverhalten unterschiedlicher Bauteilgeometrien. Shaker, Aachen
Metadaten
Titel
Characterization of damage in forward rod extruded parts
verfasst von
Oliver Hering
Anthony Dunlap
A. Erman Tekkaya
Anke Aretz
Alexander Schwedt
Publikationsdatum
27.11.2019
Verlag
Springer Paris
Erschienen in
International Journal of Material Forming / Ausgabe 6/2020
Print ISSN: 1960-6206
Elektronische ISSN: 1960-6214
DOI
https://doi.org/10.1007/s12289-019-01525-z

Weitere Artikel der Ausgabe 6/2020

International Journal of Material Forming 6/2020 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.