Characterization of low loss CoTiNb2O8 microwave dielectric ceramics based on the complex bond theory

verfasst von: H. J. Wang, J. X. Bi, H. T. Wu

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 2/2017

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The tetragonal-structured CoTiNb2O8 was prepared by the conventional solid-state method. Morphology, crystal structure and microwave dielectric properties of the ceramics were investigated by means of scanning electron microscope and X-ray diffraction. Single-phase CoTiNb2O8 could be obtained in the temperature range of 1100–1200 °C with the space group of P42/mnm. The dielectric constant and quality factors gradually increased with the increase of apparent density. The τ f values were shifted toward zero with the increase of sintering temperature. Complex bond theory was reported for the first time to characterize the correlations between crystal structure and microwave dielectric properties. Typically, the saturated samples sintered at 1150 °C exhibited excellent microwave properties with ε r value of 66.41, Q·f value of 10,153 GHz and τ f value of 25.56 ppm/°C.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat J.K. Plourde, D.F. Linn, H.M.J. O’Bryan, J.J. Thompson, J. Am. Ceram. Soc. 58, 418 (1975)CrossRef J.K. Plourde, D.F. Linn, H.M.J. O’Bryan, J.J. Thompson, J. Am. Ceram. Soc. 58, 418 (1975)CrossRef
2.
Zurück zum Zitat H.T. Wu, L.P. Zhao, J. Univ. Jinan 30, 177 (2016) H.T. Wu, L.P. Zhao, J. Univ. Jinan 30, 177 (2016)
3.
4.
Zurück zum Zitat H. Barzegar Bafrooei, E. Taheri Nassaj, T. Ebadzadeh, C.F. Hu, A. Sayyadi-Shahraki, T. Kolodiazhnyi, Ceram. Int. 42, 3296 (2016)CrossRef H. Barzegar Bafrooei, E. Taheri Nassaj, T. Ebadzadeh, C.F. Hu, A. Sayyadi-Shahraki, T. Kolodiazhnyi, Ceram. Int. 42, 3296 (2016)CrossRef
6.
Zurück zum Zitat Y. Zhang, Y.C. Zhang, M.Q. Xiang, S.Y. Liu, H. Liu, Ceram. Int. 42, 3542 (2016)CrossRef Y. Zhang, Y.C. Zhang, M.Q. Xiang, S.Y. Liu, H. Liu, Ceram. Int. 42, 3542 (2016)CrossRef
7.
Zurück zum Zitat Y. Zhang, Y.C. Zhang, M.Q. Xiang, J. Eur. Ceram. Soc. 36, 1945 (2016)CrossRef Y. Zhang, Y.C. Zhang, M.Q. Xiang, J. Eur. Ceram. Soc. 36, 1945 (2016)CrossRef
8.
9.
Zurück zum Zitat B.W. Hakki, P.D. Coleman, I.E.E.E. Trans, Microw. Theory Tech. 8, 402 (1960)CrossRef B.W. Hakki, P.D. Coleman, I.E.E.E. Trans, Microw. Theory Tech. 8, 402 (1960)CrossRef
10.
12.
13.
Zurück zum Zitat R.D. Shannon, G.R. Rossman, Am. Mineral. 77, 94 (1992) R.D. Shannon, G.R. Rossman, Am. Mineral. 77, 94 (1992)
16.
17.
19.
Zurück zum Zitat L. Glasser, H.D.B. Jenkins, J. Am. Ceram. Soc. 122, 632 (2000) L. Glasser, H.D.B. Jenkins, J. Am. Ceram. Soc. 122, 632 (2000)
20.
21.
Zurück zum Zitat S.D. Ramarao, S. Roopas Kiran, V.R.K. Murthy, Mater. Res. Bull. 56, 71 (2014)CrossRef S.D. Ramarao, S. Roopas Kiran, V.R.K. Murthy, Mater. Res. Bull. 56, 71 (2014)CrossRef
23.
Zurück zum Zitat R.T. Sandderson, Chemical Bonds and Bond Energy (Academic Press, New York, 1971) R.T. Sandderson, Chemical Bonds and Bond Energy (Academic Press, New York, 1971)
24.
Zurück zum Zitat R.T. Sandderson, J. Am. Ceram. Soc. 105, 2259 (1983) R.T. Sandderson, J. Am. Ceram. Soc. 105, 2259 (1983)
25.
Zurück zum Zitat Y.R. Luo, Comprehensive Handbook of Chemical Bond Energies (CRC Press, Boca Raton, 2007)CrossRef Y.R. Luo, Comprehensive Handbook of Chemical Bond Energies (CRC Press, Boca Raton, 2007)CrossRef
26.
Metadaten
Titel
Characterization of low loss CoTiNb2O8 microwave dielectric ceramics based on the complex bond theory
verfasst von
H. J. Wang
J. X. Bi
H. T. Wu
Publikationsdatum
12.10.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 2/2017
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5776-7

Weitere Artikel der Ausgabe 2/2017

Journal of Materials Science: Materials in Electronics 2/2017 Zur Ausgabe

Neuer Inhalt