2015 | OriginalPaper | Buchkapitel

8. Coalescence and Growth of Two Semi-Elliptical Coplanar Cracks in API-5L Grade B Steel

verfasst von : Abdallah Al Tamimi, Mohammad Modarres

Erschienen in: Fracture, Fatigue, Failure, and Damage Evolution, Volume 5

Verlag: Springer International Publishing

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config

KI-gestützte Suche

Aus

Abstract

The purpose of this research is to investigate the interaction of two adjacent cracks under cyclic loading. A series of tests at different loads and frequencies were conducted under uniaxial constant amplitude fatigue loads on API-5L grade B steel samples. Crack growth rate of two initial semi-elliptical cracks was investigated. Marker band testing technique was employed to study the crack growth rate before and after interaction. Real time optical microscopy was used to observe crack coalescence on the specimens’ surface. Moreover, SEM analysis of the fracture surface was performed for comprehensive understanding of cracks behavior.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

über 102.000 Bücher
über 537 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Finance + Banking
Management + Führung
Marketing + Vertrieb
Maschinenbau + Werkstoffe
Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

über 67.000 Bücher
über 390 Zeitschriften

aus folgenden Fachgebieten:

Automobil + Motoren
Bauwesen + Immobilien
Business IT + Informatik
Elektrotechnik + Elektronik
Energie + Nachhaltigkeit
Maschinenbau + Werkstoffe

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Vorheriges Kapitel Through Thickness Fracture Behavior of Transversely Graded Ti/TiB Material

Nächstes Kapitel Measurement of Crack Tip Displacement Field in Desiccating Paste

NTSB (2002) Rupture of enbridge pipeline and release of crude oil near Cohasset. NTSB/PAR-04/01, Washington, DC

Bayley C (1997) Parametric investigation on the coalescence of coplanar fatigue cracks. Masters’ thesis, Carleton University, Ottawa

Harrington D (1995) Fatigue crack coalescence and shape development and experimental investigation. Masters Thesis, Carleton University, Department of Mechanical and Aerospace Engineering

Leek T, Howard I (1994) Rules for the assessment of interacting surface cracks under mode I load. Int J Press Vessel Pip 60:323–339CrossRef

Leek T, Howard I (1996) An examination of methods of assessing interacting surface cracks by comparison with experimental data. Int J Press Vessel Pip 68:181–201CrossRef

Leek T (1990) The interaction and growth of two surface cracks under fatigue loading. PhD Thesis, University of Sheffield, UK

Soboyejo W, Knott J (1990) Fatigue crack propagation of coplanar semi-elliptical cracks in pure bending. Eng Fract Mech 37(2):323–340CrossRef

Kishimoto K, Soboyejo W, Smith R, Knott J (1989) A numerical investigation of the interaction and coalescence of twin coplanar semi elliptical fatigue cracks. Int J Fatigue 11(2):91–96CrossRef

Twaddle J, Hancock B (1988) The development of cracks by defect coalescence. Engineering Materials Advisory Service, Warrington, pp 185–198

10.

O’Donoghure T, Nishioka P, Atluris N (1984) Multiple surface cracks in pressure vessels. Eng Fract Mech 20(3):545–560CrossRef

11.

DeBartolo E, Hillberry B (1998) Effects of constituent particle clusters on fatigue behavior of 2024-T3 aluminum alloy. Int J Fatigue 20: 727–735CrossRef

12.

Terrell J (1988) Effect of cyclic frequency on the fatigue life of ASME SA-106-B piping steel in BWR environments. J Mater Eng 10:193–203CrossRef

13.

Willard SA (1997) Use of marker bands for determination of fatigue crack growth rates and crack front shapes in pre-corroded coupons. NASA, Hampton, VA

14.

Ritchie R (1999) Mechanisms of fatigue-crack propagation in ductile and brittle solids. Int J Fract 100:55–83CrossRef

Titel: Coalescence and Growth of Two Semi-Elliptical Coplanar Cracks in API-5L Grade B Steel
verfasst von: Abdallah Al Tamimi
Mohammad Modarres
Verlag: Springer International Publishing
Buch: Fracture, Fatigue, Failure, and Damage Evolution, Volume 5
Print ISBN: 978-3-319-06976-0

Electronic ISBN: 978-3-319-06977-7

Copyright-Jahr: 2015
DOI: https://doi.org/10.1007/978-3-319-06977-7_8

Premium Partner

Marktübersichten

Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.

Zur Marktübersicht