Colloidal synthesis of Gd3+ doped ZrO2 based dielectrics and their structural and electrochemical property studies

verfasst von: P. Ilanchezhiyan, C. Siva, T. W. Kang, G. Mohan Kumar

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 6/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Solution processed wide band gap dielectrics have nowadays started to receive renewed interest for practical application in semiconductor electronics. In this regard, undoped and gadolinium (Gd) doped zirconia (ZrO2) nanocrystallites were colloidally processed and their potential for dielectric applications has been demonstrated. X-ray diffraction measurements revealed the effective crystallization of nanostructures and the successful substitution of Gd ions into the cubic ZrO2 matrix. The particulate-like characteristics of undoped and Gd doped ZrO2 nanostructures were examined through the electron microscopes, which hardly revealed any difference among them. The optical band gap of ZrO2 nanostructures was determined to be around 4.64–4.80 eV from the absorbance measurements. The potential of Gd doped ZrO2 nanostructures for dielectric functions were evaluated through electrochemical impedance spectroscopic measurements. The improved capacitance values estimated from the Nyquist plots suggests the potential of the investigated materials for low power and low voltage electronic applications.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
2.
Zurück zum Zitat R. Nechache, C. Harnagea, S. Li, L. Cargenas, W. Huang, J. Chakrabartty, F. Rosei, Nat. Photon. 9, 61–67 (2015)CrossRef R. Nechache, C. Harnagea, S. Li, L. Cargenas, W. Huang, J. Chakrabartty, F. Rosei, Nat. Photon. 9, 61–67 (2015)CrossRef
3.
Zurück zum Zitat Z. Liu, X. Jing, D. Chenb, G. Shen, Chem. Soc. Rev. 44, 161–192 (2015)CrossRef Z. Liu, X. Jing, D. Chenb, G. Shen, Chem. Soc. Rev. 44, 161–192 (2015)CrossRef
5.
Zurück zum Zitat J. Zhu, J. Kang, J. Kang, D. Jariwala, J.D. Wood, J.W.T. Seo, K.S. Chen, T.J. Marks, M.C. Hersam, Nano Lett. 15, 7029–7036 (2015)CrossRef J. Zhu, J. Kang, J. Kang, D. Jariwala, J.D. Wood, J.W.T. Seo, K.S. Chen, T.J. Marks, M.C. Hersam, Nano Lett. 15, 7029–7036 (2015)CrossRef
6.
Zurück zum Zitat W. Xu, H. Wang, F. Xie, J. Chen, H. Cao, J.-B. Xu, ACS Appl. Mater. Interfaces 7, 5803–5810 (2015)CrossRef W. Xu, H. Wang, F. Xie, J. Chen, H. Cao, J.-B. Xu, ACS Appl. Mater. Interfaces 7, 5803–5810 (2015)CrossRef
7.
Zurück zum Zitat A. Zhang, M. Li, G. Zhou, S. Wang, Y. Zhou, J. Phys. Chem. Solids 67, 2430–2434 (2006)CrossRef A. Zhang, M. Li, G. Zhou, S. Wang, Y. Zhou, J. Phys. Chem. Solids 67, 2430–2434 (2006)CrossRef
8.
Zurück zum Zitat T. Ninjbadgar, G. Garnweitner, A. Börger, L.M. Goldenberg, O.V. Sakhno, J. Stumpe, Adv. Funct. Mater. 19, 1819–1825 (2009)CrossRef T. Ninjbadgar, G. Garnweitner, A. Börger, L.M. Goldenberg, O.V. Sakhno, J. Stumpe, Adv. Funct. Mater. 19, 1819–1825 (2009)CrossRef
9.
Zurück zum Zitat K.E. Sickafus, L. Minervini, R.W. Grimes, J.A. Valdez, M. Ishimaru, F. Li, K.J. McClellan, T. Hartmann, Science 289, 748–751 (2000)CrossRef K.E. Sickafus, L. Minervini, R.W. Grimes, J.A. Valdez, M. Ishimaru, F. Li, K.J. McClellan, T. Hartmann, Science 289, 748–751 (2000)CrossRef
10.
Zurück zum Zitat K.J. Moreno, M.A. Guevara, A.F. Fuentes, J. Solid State Chem. 179, 928–934 (2006)CrossRef K.J. Moreno, M.A. Guevara, A.F. Fuentes, J. Solid State Chem. 179, 928–934 (2006)CrossRef
11.
Zurück zum Zitat R. Vassen, X. Cao, F. Tietz, D. Basu, D. Stöver, J. Am. Ceram. Soc. 83, 2023–2028 (2000)CrossRef R. Vassen, X. Cao, F. Tietz, D. Basu, D. Stöver, J. Am. Ceram. Soc. 83, 2023–2028 (2000)CrossRef
12.
Zurück zum Zitat I. Freris, P. Riello, F. Enrichi, D. Cristofori, A. Benedetti, Opt. Mater. 33, 1745–1752 (2011)CrossRef I. Freris, P. Riello, F. Enrichi, D. Cristofori, A. Benedetti, Opt. Mater. 33, 1745–1752 (2011)CrossRef
13.
Zurück zum Zitat T.S. Kalkur, Y.C. Lu, Thin Solid Films 193, 207 (1992) T.S. Kalkur, Y.C. Lu, Thin Solid Films 193, 207 (1992)
14.
Zurück zum Zitat G.D. Wilk, R.M. Wallace, Appl. Phys. Lett. 112, 76 (2000) G.D. Wilk, R.M. Wallace, Appl. Phys. Lett. 112, 76 (2000)
15.
Zurück zum Zitat T.S. Jeon, J.M. White, D.L. Kwong, Appl. Phys. Lett. 78, 368–370 (2001)CrossRef T.S. Jeon, J.M. White, D.L. Kwong, Appl. Phys. Lett. 78, 368–370 (2001)CrossRef
16.
Zurück zum Zitat M. He, H. Zhang, S. Zhang, J. Wan, J. Mater. Sci. Mater. Electron. 23, 1734–1738 (2012)CrossRef M. He, H. Zhang, S. Zhang, J. Wan, J. Mater. Sci. Mater. Electron. 23, 1734–1738 (2012)CrossRef
17.
Zurück zum Zitat C.W. Raubach, M.Z. Krolow, M.F. Mesko, S. Cava, M.L. Moreira, E. Longo, N.L.V. Carreno, CrystEngComm 14, 393–396 (2012)CrossRef C.W. Raubach, M.Z. Krolow, M.F. Mesko, S. Cava, M.L. Moreira, E. Longo, N.L.V. Carreno, CrystEngComm 14, 393–396 (2012)CrossRef
18.
Zurück zum Zitat C. Liu, S. Lee, D. Su, B. Lee, S. Lee, R.E. Winans, C. Yin, S. Vajda, L. Pfefferle, G.L. Haller, Langmuir 28, 17159–17167 (2012)CrossRef C. Liu, S. Lee, D. Su, B. Lee, S. Lee, R.E. Winans, C. Yin, S. Vajda, L. Pfefferle, G.L. Haller, Langmuir 28, 17159–17167 (2012)CrossRef
19.
Zurück zum Zitat H. Habazaki, S. Koyama, Y. Aoki, N. Sakaguchi, S. Nagata, ACS Appl. Mater. Interfaces 3, 2665–2670 (2011)CrossRef H. Habazaki, S. Koyama, Y. Aoki, N. Sakaguchi, S. Nagata, ACS Appl. Mater. Interfaces 3, 2665–2670 (2011)CrossRef
20.
Zurück zum Zitat E. De la Rosa, P. Salas, H. Desirena, C. Angeles, R.A. Rodríguez, Appl. Phys. Lett. 87, 241912 (2005)CrossRef E. De la Rosa, P. Salas, H. Desirena, C. Angeles, R.A. Rodríguez, Appl. Phys. Lett. 87, 241912 (2005)CrossRef
21.
Zurück zum Zitat D. Solís, T. López-Luke, E. De la Rosa, P. Salas, C. Angeles-Chavez, J. Lumin. 129, 449–455 (2009)CrossRef D. Solís, T. López-Luke, E. De la Rosa, P. Salas, C. Angeles-Chavez, J. Lumin. 129, 449–455 (2009)CrossRef
22.
Zurück zum Zitat J. Liao, D. Zhou, S. Liu, H.R. Wen, X. Qiu, J. Chen, Phys. B 436, 59–63 (2014)CrossRef J. Liao, D. Zhou, S. Liu, H.R. Wen, X. Qiu, J. Chen, Phys. B 436, 59–63 (2014)CrossRef
23.
Zurück zum Zitat J. Liao, D. Zhou, B. Yang, R. Liu, Q. Zhang, Opt. Mater. 35, 274–279 (2012)CrossRef J. Liao, D. Zhou, B. Yang, R. Liu, Q. Zhang, Opt. Mater. 35, 274–279 (2012)CrossRef
24.
Zurück zum Zitat L.A. Gómez, L.D.S. Menezes, C.B. de Araújo, R.R. Gonçalves, S.J.L. Ribeiro, Y. Messaddeq, J. Appl. Phys. 107, 113508 (2010)CrossRef L.A. Gómez, L.D.S. Menezes, C.B. de Araújo, R.R. Gonçalves, S.J.L. Ribeiro, Y. Messaddeq, J. Appl. Phys. 107, 113508 (2010)CrossRef
25.
Zurück zum Zitat E. De la Rosa, L.A. Diaz-Torres, P. Salas, R.A. Rodrıguez, Opt. Mater. 27, 1320–1325 (2005)CrossRef E. De la Rosa, L.A. Diaz-Torres, P. Salas, R.A. Rodrıguez, Opt. Mater. 27, 1320–1325 (2005)CrossRef
26.
Zurück zum Zitat A. Baéz-Rodríguez, O. Alvarez-Fragoso, M. García-Hipólito, J. Guzmán-Mendoza, C. Falcony, Ceram. Int. 41, 7197–7206 (2015)CrossRef A. Baéz-Rodríguez, O. Alvarez-Fragoso, M. García-Hipólito, J. Guzmán-Mendoza, C. Falcony, Ceram. Int. 41, 7197–7206 (2015)CrossRef
27.
Zurück zum Zitat V. Kiisk, A. Tamm, K. Utt, J. Kozlova, H. Mändar, L. Puust, J. Aarik, I. Sildos, Thin Solid Films 583, 70–75 (2015)CrossRef V. Kiisk, A. Tamm, K. Utt, J. Kozlova, H. Mändar, L. Puust, J. Aarik, I. Sildos, Thin Solid Films 583, 70–75 (2015)CrossRef
28.
Zurück zum Zitat H.Q. Cao, X. Qiu, B. Luo, Y. Liang, Y.H. Zhang, R.Q. Tan, M.J. Zhao, Q.M. Zhu, Adv. Funct. Mater. 14, 243–246 (2004)CrossRef H.Q. Cao, X. Qiu, B. Luo, Y. Liang, Y.H. Zhang, R.Q. Tan, M.J. Zhao, Q.M. Zhu, Adv. Funct. Mater. 14, 243–246 (2004)CrossRef
29.
30.
Zurück zum Zitat A. Patra, C.S. Friend, R. Kapoor, P.N. Prasad, J. Phys. Chem. B 106, 1909–1912 (2002)CrossRef A. Patra, C.S. Friend, R. Kapoor, P.N. Prasad, J. Phys. Chem. B 106, 1909–1912 (2002)CrossRef
31.
Zurück zum Zitat R.I. Merino, J.A. Pardo, J.I. Pena, G.F. De La Fuente, A. Larrea, V.M. Orera, Phys. Rev. B 56, 10907–10915 (1997)CrossRef R.I. Merino, J.A. Pardo, J.I. Pena, G.F. De La Fuente, A. Larrea, V.M. Orera, Phys. Rev. B 56, 10907–10915 (1997)CrossRef
32.
Zurück zum Zitat B. Savoini, J.E.M. Santiuste, R. Gonzalez, Phys. Rev. B 56, 5856–5865 (1997)CrossRef B. Savoini, J.E.M. Santiuste, R. Gonzalez, Phys. Rev. B 56, 5856–5865 (1997)CrossRef
33.
Zurück zum Zitat Z. Wang, B. Yang, Z. Fu, W. Dong, Y. Yang, W. Liu, Appl. Phys. A 81, 691–694 (2005)CrossRef Z. Wang, B. Yang, Z. Fu, W. Dong, Y. Yang, W. Liu, Appl. Phys. A 81, 691–694 (2005)CrossRef
34.
Zurück zum Zitat X. Bai, A. Pucci, V.T. Freitas, R.A.S. Ferreira, N. Pinna, Adv. Funct. Mater. 22, 4275–4283 (2012)CrossRef X. Bai, A. Pucci, V.T. Freitas, R.A.S. Ferreira, N. Pinna, Adv. Funct. Mater. 22, 4275–4283 (2012)CrossRef
35.
Zurück zum Zitat L. Kumari, W.Z. Li, J.M. Xu, R.M. Leblanc, D.Z. Wang, Y. Li, H. Guo, J. Zhang, Cryst. Growth Des. 9, 3874–3880 (2009)CrossRef L. Kumari, W.Z. Li, J.M. Xu, R.M. Leblanc, D.Z. Wang, Y. Li, H. Guo, J. Zhang, Cryst. Growth Des. 9, 3874–3880 (2009)CrossRef
36.
Zurück zum Zitat N.G. Petrik, D.P. Taylor, T.M. Orlando, J. Appl. Phys. 85, 6770–6776 (1999)CrossRef N.G. Petrik, D.P. Taylor, T.M. Orlando, J. Appl. Phys. 85, 6770–6776 (1999)CrossRef
37.
Zurück zum Zitat P.P. Murmu, R.J. Mendelsberg, J. Kennedy, D.A. Carder, B.J. Ruck, A. Markwitz, R.J. Reeves, P. Malar, T. Osipowicz, J. Appl. Phys. 110, 033534 (2011)CrossRef P.P. Murmu, R.J. Mendelsberg, J. Kennedy, D.A. Carder, B.J. Ruck, A. Markwitz, R.J. Reeves, P. Malar, T. Osipowicz, J. Appl. Phys. 110, 033534 (2011)CrossRef
38.
39.
Zurück zum Zitat A. Bewick, K. Kunimatsu, J.W. Russell, J. Electroanal. Chem. 276, 175–186 (1987) A. Bewick, K. Kunimatsu, J.W. Russell, J. Electroanal. Chem. 276, 175–186 (1987)
Metadaten
Titel
Colloidal synthesis of Gd3+ doped ZrO2 based dielectrics and their structural and electrochemical property studies
verfasst von
P. Ilanchezhiyan
C. Siva
T. W. Kang
G. Mohan Kumar
Publikationsdatum
09.02.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 6/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-4460-2

Weitere Artikel der Ausgabe 6/2016

Journal of Materials Science: Materials in Electronics 6/2016 Zur Ausgabe

Neuer Inhalt