Comparing molybdenum oxide thin films prepared by magnetron sputtering and thermal evaporation applied in organic solar cells

verfasst von: Jianbin Sun, Qiao Zheng, Shuying Cheng, Haifang Zhou, Yunfeng Lai, Jinling Yu

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 4/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

We have presented an organic polymer-fullerene solar cell with molybdenum oxide (MoOx) film prepared by direct current magnetron sputtering (sMoOx) and thermal evaporation (eMoOx) as a hole transport layer (HTL), respectively. The result shows that best power conversion efficiency (PCE) of the device using sMoOx as HTL is 3.84 %, while the PCE of the devices with eMoOx film is 3.33 %. The intrinsic mechanisms behind the PCE difference were studied by analyzing the morphology, electrical and optical properties of MoOx thin films prepared by the different methods. The higher PCE obtained in the cells with sMoOx may be due to the smoother interface and higher absorption of the active layer.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat P.-Y. Ho, J.-Y. Sun, S.-H. Kao, C.-Y. Kao, S.-H. Lin, S. Lan, W.-H. Tseng, C.-I. Wu, C.-F. Lin, Sol. Energy Mater. Sol. Cells 119, 235 (2013)CrossRef P.-Y. Ho, J.-Y. Sun, S.-H. Kao, C.-Y. Kao, S.-H. Lin, S. Lan, W.-H. Tseng, C.-I. Wu, C.-F. Lin, Sol. Energy Mater. Sol. Cells 119, 235 (2013)CrossRef
2.
3.
4.
Zurück zum Zitat M.A. Green, K. Emery, Y. Hishikawa, W. Warta, E.D. Dunlop, Prog. Photovolt. Res. Appl. 5, 606 (2012)CrossRef M.A. Green, K. Emery, Y. Hishikawa, W. Warta, E.D. Dunlop, Prog. Photovolt. Res. Appl. 5, 606 (2012)CrossRef
5.
Zurück zum Zitat S. Chen, J.R. Manders, S.W. Tsang, F. So, J. Mater. Chem. 46, 24202 (2012)CrossRef S. Chen, J.R. Manders, S.W. Tsang, F. So, J. Mater. Chem. 46, 24202 (2012)CrossRef
6.
Zurück zum Zitat A. Hadipour, D. Cheyns, P. Heremans, B.P. Rand, Adv. Energy Mater. 5, 930 (2011)CrossRef A. Hadipour, D. Cheyns, P. Heremans, B.P. Rand, Adv. Energy Mater. 5, 930 (2011)CrossRef
7.
Zurück zum Zitat W. Qiu, A. Hadipour, R. Muller, B. Conings, H.G. Boyen, P. Heremans, L. Froyen, ACS Appl. Mater. Interfaces 6, 3581 (2015) W. Qiu, A. Hadipour, R. Muller, B. Conings, H.G. Boyen, P. Heremans, L. Froyen, ACS Appl. Mater. Interfaces 6, 3581 (2015)
8.
Zurück zum Zitat P. Sakthivel, K. Kranthiraja, C. Saravanan, K. Gunasekar, H.I. Kim, W.S. Shin, J.-E. Jeong, H.Y. Woo, S.-H. Jin, J. Mater. Chem. A 19, 6916 (2014)CrossRef P. Sakthivel, K. Kranthiraja, C. Saravanan, K. Gunasekar, H.I. Kim, W.S. Shin, J.-E. Jeong, H.Y. Woo, S.-H. Jin, J. Mater. Chem. A 19, 6916 (2014)CrossRef
9.
10.
Zurück zum Zitat P. Qin, G. Fang, F. Cheng, W. Ke, H. Lei, H. Wang, X. Zhao, ACS Appl. Mater. Interfaces 4, 2963 (2014)CrossRef P. Qin, G. Fang, F. Cheng, W. Ke, H. Lei, H. Wang, X. Zhao, ACS Appl. Mater. Interfaces 4, 2963 (2014)CrossRef
11.
Zurück zum Zitat C. Girotto, E. Voroshazi, D. Cheyns, P. Heremans, B.P. Rand, ACS Appl. Mater. Interfaces 9, 3244 (2014) C. Girotto, E. Voroshazi, D. Cheyns, P. Heremans, B.P. Rand, ACS Appl. Mater. Interfaces 9, 3244 (2014)
12.
Zurück zum Zitat W.J. Dong, G.H. Jung, J.-L. Lee, Sol. Energy Mater. Sol. Cells 116, 94 (2013)CrossRef W.J. Dong, G.H. Jung, J.-L. Lee, Sol. Energy Mater. Sol. Cells 116, 94 (2013)CrossRef
13.
Zurück zum Zitat S. Wilken, V. Wilkens, D. Scheunemann, R.E. Nowak, K. von Maydell, J. Parisi, H. Borchert, ACS Appl. Mater. Interfaces 1, 287 (2015)CrossRef S. Wilken, V. Wilkens, D. Scheunemann, R.E. Nowak, K. von Maydell, J. Parisi, H. Borchert, ACS Appl. Mater. Interfaces 1, 287 (2015)CrossRef
14.
Zurück zum Zitat W. Qiu, A. Hadipour, R. Muller, B. Conings, H. G. Boyen, P. Heremans, L. Froyen, ACS Appl. Mater. Interfaces 18, 16335 (2013) W. Qiu, A. Hadipour, R. Muller, B. Conings, H. G. Boyen, P. Heremans, L. Froyen, ACS Appl. Mater. Interfaces 18, 16335 (2013)
15.
Zurück zum Zitat N.K. Elumalai, A. Saha, C. Vijila, R. Jose, Z. Jie, S. Ramakrishna, Phys. Chem. Chem. Phys. 18, 6831 (2013)CrossRef N.K. Elumalai, A. Saha, C. Vijila, R. Jose, Z. Jie, S. Ramakrishna, Phys. Chem. Chem. Phys. 18, 6831 (2013)CrossRef
16.
Zurück zum Zitat W.J. Dong, G.H. Jung, J.-L. Lee, Org. Electron. 1, 29 (2014) W.J. Dong, G.H. Jung, J.-L. Lee, Org. Electron. 1, 29 (2014)
17.
Zurück zum Zitat S. Balendhran, J. Deng, J.Z. Ou, S. Walia, J. Scott, J. Tang, K.L. Wang, M.R. Field, S. Russo, S. Zhuiykov, M.S. Strano, N. Medhekar, S. Sriram, M. Bhaskaran, K. Kalantar-zadeh, Adv. Mater. 1, 109 (2013)CrossRef S. Balendhran, J. Deng, J.Z. Ou, S. Walia, J. Scott, J. Tang, K.L. Wang, M.R. Field, S. Russo, S. Zhuiykov, M.S. Strano, N. Medhekar, S. Sriram, M. Bhaskaran, K. Kalantar-zadeh, Adv. Mater. 1, 109 (2013)CrossRef
18.
Zurück zum Zitat X. Fan, G. Fang, P. Qin, N. Sun, N. Liu, Q. Zheng, F. Cheng, L. Yuan, X. Zhao, J. Phys. D Appl. Phys. 4, 045101 (2011)CrossRef X. Fan, G. Fang, P. Qin, N. Sun, N. Liu, Q. Zheng, F. Cheng, L. Yuan, X. Zhao, J. Phys. D Appl. Phys. 4, 045101 (2011)CrossRef
19.
Zurück zum Zitat A.K.K. Kyaw, X.W. Sun, C.Y. Jiang, G.Q. Lo, D.W. Zhao, D.L. Kwong, Appl. Phys. Lett. 22, 221107 (2008)CrossRef A.K.K. Kyaw, X.W. Sun, C.Y. Jiang, G.Q. Lo, D.W. Zhao, D.L. Kwong, Appl. Phys. Lett. 22, 221107 (2008)CrossRef
20.
Zurück zum Zitat S. Jenatsch, R. Hany, A.C. Véron, M. Neukom, S. Züfle, A. Borgschulte, B. Ruhstaller, F. Nüesch, J. Phys. Chem. C 30, 17036 (2014)CrossRef S. Jenatsch, R. Hany, A.C. Véron, M. Neukom, S. Züfle, A. Borgschulte, B. Ruhstaller, F. Nüesch, J. Phys. Chem. C 30, 17036 (2014)CrossRef
21.
Zurück zum Zitat Y. Kinoshita, R. Takenaka, H. Murata, Appl. Phys. Lett. 24, 243309 (2008)CrossRef Y. Kinoshita, R. Takenaka, H. Murata, Appl. Phys. Lett. 24, 243309 (2008)CrossRef
23.
Zurück zum Zitat A. Hojabri, F. Hajakbari, A.E. Meibodi, J. Theor. Appl. Phys. 1, 67 (2015)CrossRef A. Hojabri, F. Hajakbari, A.E. Meibodi, J. Theor. Appl. Phys. 1, 67 (2015)CrossRef
Metadaten
Titel
Comparing molybdenum oxide thin films prepared by magnetron sputtering and thermal evaporation applied in organic solar cells
verfasst von
Jianbin Sun
Qiao Zheng
Shuying Cheng
Haifang Zhou
Yunfeng Lai
Jinling Yu
Publikationsdatum
08.12.2015
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 4/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-015-4151-4

Weitere Artikel der Ausgabe 4/2016

Journal of Materials Science: Materials in Electronics 4/2016 Zur Ausgabe

Neuer Inhalt