29.03.2019 | Communication

Comparison of Microstructure and Mechanical Properties of Sintered γ-(Fe-Ni-P) Alloys with Abundant P Doping

verfasst von: Runjian Jiang, Ai Li, Guodong Cui, Chengsong Zhang

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 6/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The γ-(Fe-Ni-P) alloy with a high phosphorus content was obtained by spark plasma sintering. A supersaturated phosphorus solid solution has been developed and the precipitation of phosphide is suppressed in this γ-(Fe-Ni-P) alloy. This new structure of the γ-(Fe-Ni-P) alloy attains a higher yield strength (1067 MPa) without sacrificing plasticity. Its formation and strengthening mechanism are clarified by a comparison with the alloy obtained via conventional sintering.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H. Kotan, M. Saber, C.C. Koch, R.O. Scattergood: Mater. Sci. Eng. A, 2012, vol. 552, pp. 310-315.CrossRef H. Kotan, M. Saber, C.C. Koch, R.O. Scattergood: Mater. Sci. Eng. A, 2012, vol. 552, pp. 310-315.CrossRef
2.
Zurück zum Zitat M. van Schilfgaarde, I.A. Abrikosov, B. Johansson: Nat., 1999, vol. 400, pp. 46–49. M. van Schilfgaarde, I.A. Abrikosov, B. Johansson: Nat., 1999, vol. 400, pp. 46–49.
3.
Zurück zum Zitat Shuangyu Liu, Hong Zhang, Jiandong Hu: Mater. Design, 2011, vol. 32, pp. 3686-3691.CrossRef Shuangyu Liu, Hong Zhang, Jiandong Hu: Mater. Design, 2011, vol. 32, pp. 3686-3691.CrossRef
4.
Zurück zum Zitat Changshuai Wang, Yongan Guo, Jianting Guo, Lanzhang Zhou: Mater. Sci. Eng. A, 2016, vol. 675, pp. 314-322.CrossRef Changshuai Wang, Yongan Guo, Jianting Guo, Lanzhang Zhou: Mater. Sci. Eng. A, 2016, vol. 675, pp. 314-322.CrossRef
6.
Zurück zum Zitat Krzysztof Ziewiec, Artur Błachowski, Krzysztof Ruebenbauer, Aneta Ziewiec, Krystian Prusik, Jerzy Latuch, Marcin Zieba, Krzysztof Bryła: J. Alloys Compd., 2014, vol. 615, pp. S29-S34.CrossRef Krzysztof Ziewiec, Artur Błachowski, Krzysztof Ruebenbauer, Aneta Ziewiec, Krystian Prusik, Jerzy Latuch, Marcin Zieba, Krzysztof Bryła: J. Alloys Compd., 2014, vol. 615, pp. S29-S34.CrossRef
7.
Zurück zum Zitat J.I. Kim, J.H. Pak, K.-S. Park, J.H. Jang, D.-W. Suh, H.K.D.H. Bhadeshia: Int. J. Mater. Res., 2014, vol. 105, pp. 1166–72. J.I. Kim, J.H. Pak, K.-S. Park, J.H. Jang, D.-W. Suh, H.K.D.H. Bhadeshia: Int. J. Mater. Res., 2014, vol. 105, pp. 1166–72.
8.
Zurück zum Zitat Pavel Lejcek, Mojmir Sob, Vaclav Paidar: Prog. Mater. Sci., 2017, vol. 87, pp. 83-139.CrossRef Pavel Lejcek, Mojmir Sob, Vaclav Paidar: Prog. Mater. Sci., 2017, vol. 87, pp. 83-139.CrossRef
9.
Zurück zum Zitat Alfiia Akhatova, Frederic Christien, Vincent Barnier, Bertrand Radiguet, Emmanuel Cadel, Fabien Cuvilly, Philippe Pareige: Appl. Surf. Sci., 2019, vol. 463, pp. 203-210.CrossRef Alfiia Akhatova, Frederic Christien, Vincent Barnier, Bertrand Radiguet, Emmanuel Cadel, Fabien Cuvilly, Philippe Pareige: Appl. Surf. Sci., 2019, vol. 463, pp. 203-210.CrossRef
10.
Zurück zum Zitat S.F. Chen, T.S. Lui, L.H. Chen: Metall. Mater. Trans. A, 1994, vol. 25, pp. 557-561.CrossRef S.F. Chen, T.S. Lui, L.H. Chen: Metall. Mater. Trans. A, 1994, vol. 25, pp. 557-561.CrossRef
11.
Zurück zum Zitat Wuqian Chai, Randall M. German, Eugene A. Olevsky, Xialu Wei, Runjian Jiang, Guodong Cui: Adv. Eng. Mater., 2016, vol. 18, pp. 1889-1896.CrossRef Wuqian Chai, Randall M. German, Eugene A. Olevsky, Xialu Wei, Runjian Jiang, Guodong Cui: Adv. Eng. Mater., 2016, vol. 18, pp. 1889-1896.CrossRef
12.
Zurück zum Zitat A. Muthuchamy, R. Kumar, A. Raja Annamalai, D.K. Agrawal, A. Upadhyaya: Mater. Charact., 2016, vol. 114, pp. 122–35. A. Muthuchamy, R. Kumar, A. Raja Annamalai, D.K. Agrawal, A. Upadhyaya: Mater. Charact., 2016, vol. 114, pp. 122–35.
13.
Zurück zum Zitat B. Weglinski, J. Kaczmar: Powder Metall., 1980, vol. 23, pp. 210–216.CrossRef B. Weglinski, J. Kaczmar: Powder Metall., 1980, vol. 23, pp. 210–216.CrossRef
14.
Zurück zum Zitat Runjian Jiang, Ai Li, Guodong Cui, Chengsong Zhang, Hongtao Chen, Yixue Wang: Mater. Sci. Eng. A, 2017, vol. 707, pp. 1-11.CrossRef Runjian Jiang, Ai Li, Guodong Cui, Chengsong Zhang, Hongtao Chen, Yixue Wang: Mater. Sci. Eng. A, 2017, vol. 707, pp. 1-11.CrossRef
15.
Zurück zum Zitat Tienyin Chan, Shuntian Lin: J. Mater. Process Tech., 1999, vol. 89-90, pp. 165-170.CrossRef Tienyin Chan, Shuntian Lin: J. Mater. Process Tech., 1999, vol. 89-90, pp. 165-170.CrossRef
16.
17.
18.
Zurück zum Zitat Yuanyuan Cui, Yunfei Jia, Fuzhen Xuan: Sci. Rep., 2016, vol. 8, pp. 6199.CrossRef Yuanyuan Cui, Yunfei Jia, Fuzhen Xuan: Sci. Rep., 2016, vol. 8, pp. 6199.CrossRef
19.
Zurück zum Zitat Bevis Hutchinson, Pete Bate, David Lindell, Amer Malik, Matthew Barnett, Peter Lynch: Acta Mater., 2018, vol. 152, pp. 239-247.CrossRef Bevis Hutchinson, Pete Bate, David Lindell, Amer Malik, Matthew Barnett, Peter Lynch: Acta Mater., 2018, vol. 152, pp. 239-247.CrossRef
Metadaten
Titel
Comparison of Microstructure and Mechanical Properties of Sintered γ-(Fe-Ni-P) Alloys with Abundant P Doping
verfasst von
Runjian Jiang
Ai Li
Guodong Cui
Chengsong Zhang
Publikationsdatum
29.03.2019
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 6/2019
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-019-05199-9

Weitere Artikel der Ausgabe 6/2019

Metallurgical and Materials Transactions A 6/2019 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.