Comparison of Thermal Shock Damage and Slag Corrosion in Castable Refractories

verfasst von: Ângelo Cristante, Fernando Vernilli

Erschienen in: Interceram - International Ceramic Review | Ausgabe 3/2021

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Abstract: This paper compares the thermal shock damage resistance and the slag corrosion resistance of a high-alumina and an alumina-containing andalusite refractory castable. Thermal shock damage resistance was analyzed through thermal cycling and thermal shock damage resistance parameters. Thermal shock cycling damage was analyzed using the dynamic modulus of elasticity (E) and the modulus of rupture (MOR) before and after the thermal shock cycles. The alumina-containing andalusite castable showed superior thermal shock damage resistance in both parameters. The high-alumina castable showed a higher resistance to slag corrosion. These results were linked to material selection for specific industry applications.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Interceram - International Ceramic Review

Interceram - Das internationale Fachmagazin für das gesamte Gebiet der keramischen sowie thematisch verwandter Technologien. Jetzt kostenlos testen!

Literatur
[1]
Zurück zum Zitat T. Vert, Refractory Material Selection for Steelmaking, John Wiley & Sons, Inc, Hoboken, New Jersey, 2016. T. Vert, Refractory Material Selection for Steelmaking, John Wiley & Sons, Inc, Hoboken, New Jersey, 2016.
[2]
Zurück zum Zitat D.P.H. HASSELMAN, Unified Theory of Thermal Shock Fracture Initiation and Crack Propagation in Brittle Ceramics, J. Am. Ceram. Soc. 52 (1969) 600-604. D.P.H. HASSELMAN, Unified Theory of Thermal Shock Fracture Initiation and Crack Propagation in Brittle Ceramics, J. Am. Ceram. Soc. 52 (1969) 600-604.
[3]
Zurück zum Zitat C.A. Schacht, Refractories Handbook, CRC Press, 2004. C.A. Schacht, Refractories Handbook, CRC Press, 2004.
[4]
Zurück zum Zitat J. Rodrigues, V.C. Pandolfelli, thermal treatment temperature and its influence on the thermal shock parameters of refractory castables, 51 (2002) 186-189. J. Rodrigues, V.C. Pandolfelli, thermal treatment temperature and its influence on the thermal shock parameters of refractory castables, 51 (2002) 186-189.
[5]
Zurück zum Zitat D.Y. Miyaji, T. Tonnesen, J.A. Rodrigues, Fracture energy and thermal shock damage resistance of refractory castables containing eutectic aggregates, Ceram. Int. 40 (2014) 15227-15239. D.Y. Miyaji, T. Tonnesen, J.A. Rodrigues, Fracture energy and thermal shock damage resistance of refractory castables containing eutectic aggregates, Ceram. Int. 40 (2014) 15227-15239.
[6]
Zurück zum Zitat Â. Cristante, L.A. Nascimento, E.S. Neves, F. Vernilli, Study of the castable selection for blast furnace blowpipe, Ceram. Int. 47 (2021) 19443-19454. Â. Cristante, L.A. Nascimento, E.S. Neves, F. Vernilli, Study of the castable selection for blast furnace blowpipe, Ceram. Int. 47 (2021) 19443-19454.
[7]
Zurück zum Zitat S. Zhang, W.E. Lee, Use of phase diagrams in studies of refractories corrosion, Int. Mater. Rev. 45 (2000) 41-58. S. Zhang, W.E. Lee, Use of phase diagrams in studies of refractories corrosion, Int. Mater. Rev. 45 (2000) 41-58.
[8]
Zurück zum Zitat J. Poirier, F. Qafssaoui, J.P. Ildefonse, M.L. Bouchetou, Analysis and interpretation of refractory microstructures in studies of corrosion mechanisms by liquid oxides, J. Eur. Ceram. Soc. 28 (2008) 1557-1568. J. Poirier, F. Qafssaoui, J.P. Ildefonse, M.L. Bouchetou, Analysis and interpretation of refractory microstructures in studies of corrosion mechanisms by liquid oxides, J. Eur. Ceram. Soc. 28 (2008) 1557-1568.
[9]
Zurück zum Zitat I. PERETZ, R.C. BRADT, Linear Thermal Expansion Coefficients of Mullite-Matrix Aluminosilicate Refractory Bodies, J. Am. Ceram. Soc. 66 (1983) 823-829. I. PERETZ, R.C. BRADT, Linear Thermal Expansion Coefficients of Mullite-Matrix Aluminosilicate Refractory Bodies, J. Am. Ceram. Soc. 66 (1983) 823-829.
[10]
Zurück zum Zitat V.R. Salvini, V.C. Pandolfelli, R.C. Bradt, Extension of Hasselman's thermal shock theory for crack/microstructure interactions in refractories, Ceram. Int. 38 (2012) 5369-5375. V.R. Salvini, V.C. Pandolfelli, R.C. Bradt, Extension of Hasselman's thermal shock theory for crack/microstructure interactions in refractories, Ceram. Int. 38 (2012) 5369-5375.
[11]
Zurück zum Zitat G.C. Ribeiro, W.S. Resende, J.A. Rodrigues, S. Ribeiro, Thermal shock resistance of a refractory castable containing andalusite aggregate, Ceram. Int. 42 (2016) 19167-19171. G.C. Ribeiro, W.S. Resende, J.A. Rodrigues, S. Ribeiro, Thermal shock resistance of a refractory castable containing andalusite aggregate, Ceram. Int. 42 (2016) 19167-19171.
[12]
Zurück zum Zitat J. NAKAYAMA, H. ABE, R.C. BRADT, Crack Stability in the Work-of-Fracture Test: Refractory Applications, J. Am. Ceram. Soc. 64 (1981) 671-675. J. NAKAYAMA, H. ABE, R.C. BRADT, Crack Stability in the Work-of-Fracture Test: Refractory Applications, J. Am. Ceram. Soc. 64 (1981) 671-675.
[13]
Zurück zum Zitat W.J. Lee, E.D. Case, Comparison of saturation behavior of thermal shock damage in a variety of brittle materials, Mater. Sci. Eng. A. 154 (1992) 1-9. W.J. Lee, E.D. Case, Comparison of saturation behavior of thermal shock damage in a variety of brittle materials, Mater. Sci. Eng. A. 154 (1992) 1-9.
[14]
Zurück zum Zitat N.M. Rendtorff, L.B. Garrido, E.F. Aglietti, Thermal shock resistance and fatigue of Zircon-Mullite composite materials, Ceram. Int. 37 (2011) 1427-1434. N.M. Rendtorff, L.B. Garrido, E.F. Aglietti, Thermal shock resistance and fatigue of Zircon-Mullite composite materials, Ceram. Int. 37 (2011) 1427-1434.
[15]
Zurück zum Zitat L.E.M. HF, Phase Diagrams for Ceramists, McGraw-Hill Companies, The, 1975. L.E.M. HF, Phase Diagrams for Ceramists, McGraw-Hill Companies, The, 1975.
Metadaten
Titel
Comparison of Thermal Shock Damage and Slag Corrosion in Castable Refractories
verfasst von
Ângelo Cristante
Fernando Vernilli
Publikationsdatum
01.09.2021
Verlag
Springer Fachmedien Wiesbaden
Erschienen in
Interceram - International Ceramic Review / Ausgabe 3/2021
Print ISSN: 0020-5214
Elektronische ISSN: 2523-8957
DOI
https://doi.org/10.1007/s42411-021-0462-z

Weitere Artikel der Ausgabe 3/2021

Interceram - International Ceramic Review 3/2021 Zur Ausgabe

Service

Books

Industries

Industries

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.