Controlled synthesis of SnO2 nanoneedles using one-step template-free hydrothermal method

verfasst von: Wenlong Zhang, Bin Yang, Jingquan Liu

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 11/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

SnO2 single-crystalline nanoneedles that were assembled into different morphologies were successfully synthesized via one-step template-free hydrothermal method, which provided a facile and low cost way for researchers to produce the 1-D (1-dimensionality) SnO2 nanostructures. The size and morphology of the product have been controlled accurately. It was proved that the nanoneedle SnO2 fabricated using hydrothermal method possessed a higher response value of 4.75 to ethanol than reported response value of 2 of SnO2 nanoneedles synthesized by other methods. The fabricated sensor also exhibited an extremely short recovery time of 2 s, which was far shorter than common 8–10 s. Moreover, a possible growth mechanism was further proposed.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat H. Wang, Q.Q. Liang, W.J. Wang, Y.R. An, J.H. Li, L. Guo, Cryst. Growth Des. 11, 2942 (2011)CrossRef H. Wang, Q.Q. Liang, W.J. Wang, Y.R. An, J.H. Li, L. Guo, Cryst. Growth Des. 11, 2942 (2011)CrossRef
2.
3.
5.
Zurück zum Zitat L. Li, K. Yu, J. Wu, Y. Wang, Z.Q. Zhu, Cryst. Res. Technol. 45, 539 (2010)CrossRef L. Li, K. Yu, J. Wu, Y. Wang, Z.Q. Zhu, Cryst. Res. Technol. 45, 539 (2010)CrossRef
6.
Zurück zum Zitat W.L. Zhang, W. Zeng, BinMiao, Z.C. Wang, Appl. Surf. Sci. 355, 631 (2015)CrossRef W.L. Zhang, W. Zeng, BinMiao, Z.C. Wang, Appl. Surf. Sci. 355, 631 (2015)CrossRef
7.
Zurück zum Zitat Y. Guan, D.W. Wang, X. Zhou, P. Sun, H.Y. Wang, J. Ma, G.Y. Lu, Sens. Actuators B 191, 45 (2014)CrossRef Y. Guan, D.W. Wang, X. Zhou, P. Sun, H.Y. Wang, J. Ma, G.Y. Lu, Sens. Actuators B 191, 45 (2014)CrossRef
8.
Zurück zum Zitat J.Z. Li, K. Yu, Y.H. Tan, H. Fu, Q.F. Zhang, W.T. Cong, C.Q. Song, H.H. Yin, Z.Q. Zhu, Dalton T. 43, 13136 (2014)CrossRef J.Z. Li, K. Yu, Y.H. Tan, H. Fu, Q.F. Zhang, W.T. Cong, C.Q. Song, H.H. Yin, Z.Q. Zhu, Dalton T. 43, 13136 (2014)CrossRef
9.
10.
Zurück zum Zitat N.H. Zhao, G.J. Wang, Y. Huang, B. Wang, B.D. Yao, Y.P. Wu, Chem. Mater. 20, 2612 (2008)CrossRef N.H. Zhao, G.J. Wang, Y. Huang, B. Wang, B.D. Yao, Y.P. Wu, Chem. Mater. 20, 2612 (2008)CrossRef
11.
Zurück zum Zitat B. Cheng, J.M. Russell, W. Sheng, L. Zhang, E.T. Samulski, J. Am. Chem. Soc. 126, 5972 (2004)CrossRef B. Cheng, J.M. Russell, W. Sheng, L. Zhang, E.T. Samulski, J. Am. Chem. Soc. 126, 5972 (2004)CrossRef
12.
Zurück zum Zitat L. Shi, Y.M. Xu, S.K. Hark, Y. Liu, S. Wang, L.M. Peng, K.W. Wong, Q. Li, Nano Lett. 7, 3559 (2007)CrossRef L. Shi, Y.M. Xu, S.K. Hark, Y. Liu, S. Wang, L.M. Peng, K.W. Wong, Q. Li, Nano Lett. 7, 3559 (2007)CrossRef
13.
Zurück zum Zitat X. Wang, W. Liu, H. Yang, X. Li, N. Li, R. Shi, H. Zhao, J. Yu, Acta Mater. 59, 1291 (2011)CrossRef X. Wang, W. Liu, H. Yang, X. Li, N. Li, R. Shi, H. Zhao, J. Yu, Acta Mater. 59, 1291 (2011)CrossRef
14.
Zurück zum Zitat X.B. Li, X.W. Wang, Q. Shen, J. Zheng, W.H. Liu, H. Zhao, F. Yang, H.Q. Yang, ACS Appl. Mater. Interfaces. 5, 3033 (2013)CrossRef X.B. Li, X.W. Wang, Q. Shen, J. Zheng, W.H. Liu, H. Zhao, F. Yang, H.Q. Yang, ACS Appl. Mater. Interfaces. 5, 3033 (2013)CrossRef
16.
Zurück zum Zitat Z.L. Zhu, X.L. Zheng, Y. Bai, T. Zhang, Z.L. Wang, S. Xiao, S.H. Yang, Phys. Chem. Chem. Phys. 28, 18265 (2015)CrossRef Z.L. Zhu, X.L. Zheng, Y. Bai, T. Zhang, Z.L. Wang, S. Xiao, S.H. Yang, Phys. Chem. Chem. Phys. 28, 18265 (2015)CrossRef
17.
Zurück zum Zitat H. Huang, H. Gong, C.L. Chow, J. Guo, T.J. White, M.S. Tse, O.K. Tan, Adv. Funct. Mater. 21, 2680 (2011)CrossRef H. Huang, H. Gong, C.L. Chow, J. Guo, T.J. White, M.S. Tse, O.K. Tan, Adv. Funct. Mater. 21, 2680 (2011)CrossRef
18.
Zurück zum Zitat H.M. Pavelko, R.G. Pavelkob, N. Barsana, U. Weimara, Sens. Actuators B 154, 264 (2011)CrossRef H.M. Pavelko, R.G. Pavelkob, N. Barsana, U. Weimara, Sens. Actuators B 154, 264 (2011)CrossRef
19.
20.
21.
Zurück zum Zitat X.H. Ding, D.W. Zeng, C.S. Xie, Sens. Actuators B 149, 336 (2010)CrossRef X.H. Ding, D.W. Zeng, C.S. Xie, Sens. Actuators B 149, 336 (2010)CrossRef
22.
Zurück zum Zitat X.F. Liu, J. Iqbal, Z.B. Wu, B. He, R.H. Yu, J. Phys. Chem. C. 114, 4790 (2010)CrossRef X.F. Liu, J. Iqbal, Z.B. Wu, B. He, R.H. Yu, J. Phys. Chem. C. 114, 4790 (2010)CrossRef
23.
Zurück zum Zitat P. Sun, L. You, Y. Sun, N. Chen, X. Li, H. Sun, J. Ma, G. Lu, Cryst. Eng. Commun. 14, 1701 (2012)CrossRef P. Sun, L. You, Y. Sun, N. Chen, X. Li, H. Sun, J. Ma, G. Lu, Cryst. Eng. Commun. 14, 1701 (2012)CrossRef
24.
Zurück zum Zitat C. Wang, G.H. Du, K. Ståhl, H.X. Huang, Y.J. Zhong, J.Z. Jiang, J. Phys. Chem. C 116, 4000 (2012)CrossRef C. Wang, G.H. Du, K. Ståhl, H.X. Huang, Y.J. Zhong, J.Z. Jiang, J. Phys. Chem. C 116, 4000 (2012)CrossRef
26.
Zurück zum Zitat J.F. Banfield, S.A. Welch, H.Z. Zhang, T.T. Ebert, R.L. Penn, Science 289, 751 (2000)CrossRef J.F. Banfield, S.A. Welch, H.Z. Zhang, T.T. Ebert, R.L. Penn, Science 289, 751 (2000)CrossRef
27.
Zurück zum Zitat L.W. Wang, S.R. Wang, Y.S. Wang, H.X. Zhang, Y.F. Kang, W.P. Huang, Sens. Actuators B. 188, 85 (2013)CrossRef L.W. Wang, S.R. Wang, Y.S. Wang, H.X. Zhang, Y.F. Kang, W.P. Huang, Sens. Actuators B. 188, 85 (2013)CrossRef
28.
Zurück zum Zitat T.K. Jia, W.M. Wang, F. Long, Z.Y. Fu, H. Wang, Q.J. Zhang, J. Phys. Chem. C 113, 9071 (2009)CrossRef T.K. Jia, W.M. Wang, F. Long, Z.Y. Fu, H. Wang, Q.J. Zhang, J. Phys. Chem. C 113, 9071 (2009)CrossRef
Metadaten
Titel
Controlled synthesis of SnO2 nanoneedles using one-step template-free hydrothermal method
verfasst von
Wenlong Zhang
Bin Yang
Jingquan Liu
Publikationsdatum
02.07.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 11/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5283-x

Weitere Artikel der Ausgabe 11/2016

Journal of Materials Science: Materials in Electronics 11/2016 Zur Ausgabe

Neuer Inhalt