Corrosion and Creep Properties of Weld Beads Produced on AA5083-H111 Alloy Sheets Using SpinArc GMAW Process

verfasst von: V. Poonguzhali, M. Umar, P. Sathiya

Erschienen in: Metals and Materials International | Ausgabe 1/2020

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

In this work, the corrosion and creep properties of weld beads produced on AA5083-H111 alloy using SpinArc gas metal arc welding process were analyzed. For that, bead on plate welding was carried out considering welding current, filler spin diameter and filler rotation speed as input parameters. It is evident from the microstructures that change in filler spin diameter and filler rotation speed altered the shape of weld bead irrespective of welding current. Also, porosities were formed at both side walls where the columnar dendrites grow upward while the equiaxed dendrites zone contains comparatively fewer porosities. On comparing the left and a right side wall, a higher density of porosities are observed at the right side wall and the direction of rotation was expected to be responsible for this occurrence. The pitting morphology of both side walls was not similar due to the variance in concentration of Mg and a higher amount of Mg exists on the right side wall led to the precipitation of Mg-rich rich particles result in severe corrosion. A welding current of 130 Amps, the filler rotation speed of 1050 rpm and filler spin diameter of 2 mm produced a high density of dislocations and a higher number of Fe and Mn-rich intermetallics at grain interiors as well as grain boundaries, thereby, results in improved corrosion and creep properties of weld. The weld contains larger porosities results in poor corrosion and creep properties.

Graphic Abstract

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat G. Yi, B. Sun, J.D. Poplawsky, Y. Zhu, M.L. Free, J. Alloy. Compd. 740, 461 (2018)CrossRef G. Yi, B. Sun, J.D. Poplawsky, Y. Zhu, M.L. Free, J. Alloy. Compd. 740, 461 (2018)CrossRef
2.
Zurück zum Zitat S.L. Xia, M. Ma, J.X. Zhang, W.X. Wang, W.C. Liu, Mater. Sci. Eng., A 609, 168 (2014)CrossRef S.L. Xia, M. Ma, J.X. Zhang, W.X. Wang, W.C. Liu, Mater. Sci. Eng., A 609, 168 (2014)CrossRef
3.
Zurück zum Zitat R. Bauri, D. Yadav, C.N. Shyam Kumar, B. Balaji, Mater. Sci. Eng., A 620, 67 (2015)CrossRef R. Bauri, D. Yadav, C.N. Shyam Kumar, B. Balaji, Mater. Sci. Eng., A 620, 67 (2015)CrossRef
5.
Zurück zum Zitat Y. Liu, W. Wang, J. Xie, S. Sun, L. Wang, Y. Qian, Y. Meng, Y. Wei, Mater. Sci. Eng., A 549, 7 (2012)CrossRef Y. Liu, W. Wang, J. Xie, S. Sun, L. Wang, Y. Qian, Y. Meng, Y. Wei, Mater. Sci. Eng., A 549, 7 (2012)CrossRef
6.
Zurück zum Zitat L. Huang, X. Hua, W. Dongsheng, Z. Jiang, F. Li, H. Wang, S. Shi, Int. J. Adv. Manuf. Technol. 93, 1809 (2017)CrossRef L. Huang, X. Hua, W. Dongsheng, Z. Jiang, F. Li, H. Wang, S. Shi, Int. J. Adv. Manuf. Technol. 93, 1809 (2017)CrossRef
7.
Zurück zum Zitat A.R. Koushki, M. Goodarzi, M. Paidar, Int. J. Min. Met. Mater. 23(12), 1416 (2016)CrossRef A.R. Koushki, M. Goodarzi, M. Paidar, Int. J. Min. Met. Mater. 23(12), 1416 (2016)CrossRef
8.
Zurück zum Zitat J.C. Dutra, RHG eSilva. BM Savi, C Marques, OE Alarcon, Weld World 59, 797 (2015)CrossRef J.C. Dutra, RHG eSilva. BM Savi, C Marques, OE Alarcon, Weld World 59, 797 (2015)CrossRef
9.
10.
Zurück zum Zitat L. Huang, W. Dongsheng, X. Hua, S. Liu, Z. Jiang, F. Li, H. Wang, S. Shi, J. Manuf. Process. 31, 514 (2018)CrossRef L. Huang, W. Dongsheng, X. Hua, S. Liu, Z. Jiang, F. Li, H. Wang, S. Shi, J. Manuf. Process. 31, 514 (2018)CrossRef
11.
Zurück zum Zitat X. Guoxiang, L. Li, J. Wang, J. Zhu, P. Li, Int. J. Adv. Manuf. Technol. 96, 1905 (2018)CrossRef X. Guoxiang, L. Li, J. Wang, J. Zhu, P. Li, Int. J. Adv. Manuf. Technol. 96, 1905 (2018)CrossRef
12.
Zurück zum Zitat J.Y. Wang, Y.S. Ren, F. Yang, H.B. Guo, Sci. Technol. Weld. Joi. 12(6), 505 (2007)CrossRef J.Y. Wang, Y.S. Ren, F. Yang, H.B. Guo, Sci. Technol. Weld. Joi. 12(6), 505 (2007)CrossRef
13.
Zurück zum Zitat C.L. Yang, N. Guo, S.B. Lin, C.L. Fan, Y.Q. Zhang, Sci. Technol. Weld. Joi. 14(2), 172 (2009)CrossRef C.L. Yang, N. Guo, S.B. Lin, C.L. Fan, Y.Q. Zhang, Sci. Technol. Weld. Joi. 14(2), 172 (2009)CrossRef
14.
Zurück zum Zitat C. Zhu, X. Tang, Y. He, L. Fenggui, H. Cui, Int. J. Adv. Manuf. Technol. 90, 2513 (2017)CrossRef C. Zhu, X. Tang, Y. He, L. Fenggui, H. Cui, Int. J. Adv. Manuf. Technol. 90, 2513 (2017)CrossRef
15.
Zurück zum Zitat C. Zhu, J. Cheon, X. Tang, S.-J. Na, L. Fenggui, H. Cui, J. Mater. Process. Technol. 259, 243 (2018)CrossRef C. Zhu, J. Cheon, X. Tang, S.-J. Na, L. Fenggui, H. Cui, J. Mater. Process. Technol. 259, 243 (2018)CrossRef
16.
Zurück zum Zitat C. Zhu, X. Tang, Y. He, L. Fenggui, H. Cui, J. Mater. Process. Technol. 238, 274 (2016)CrossRef C. Zhu, X. Tang, Y. He, L. Fenggui, H. Cui, J. Mater. Process. Technol. 238, 274 (2016)CrossRef
17.
Zurück zum Zitat Y. He, X. Tang, C. Zhu, L. Fenggui, H. Cui, Int. J. Adv. Manuf. Technol. 92, 4303 (2017)CrossRef Y. He, X. Tang, C. Zhu, L. Fenggui, H. Cui, Int. J. Adv. Manuf. Technol. 92, 4303 (2017)CrossRef
18.
Zurück zum Zitat M. Umar, P. Sathiya, Adv. Eng. Mater. 1701147 (2018) M. Umar, P. Sathiya, Adv. Eng. Mater. 1701147 (2018)
19.
Zurück zum Zitat S.-J. Kim, S.-K. Kim, J.-C. Park, Surf. Coat. Technol. 205, S73 (2010)CrossRef S.-J. Kim, S.-K. Kim, J.-C. Park, Surf. Coat. Technol. 205, S73 (2010)CrossRef
20.
21.
Zurück zum Zitat U. Mustafa, M. Chandra, S. Paulraj, Trans. Ind. Inst. Met. 71(8), 1975 (2018)CrossRef U. Mustafa, M. Chandra, S. Paulraj, Trans. Ind. Inst. Met. 71(8), 1975 (2018)CrossRef
22.
Zurück zum Zitat Y. Huang, Y. Li, Yu. Zhengbing Xiao, Y.H. Liu, X. Ren, J. Alloy. Compd. 673, 73 (2016)CrossRef Y. Huang, Y. Li, Yu. Zhengbing Xiao, Y.H. Liu, X. Ren, J. Alloy. Compd. 673, 73 (2016)CrossRef
23.
Zurück zum Zitat A. Alizadeh, A. Abdollahi, H. Biukani, J. Alloy. Compd. 650, 783 (2015)CrossRef A. Alizadeh, A. Abdollahi, H. Biukani, J. Alloy. Compd. 650, 783 (2015)CrossRef
24.
Zurück zum Zitat M.A. García-Bernal, R.S. Mishra, R. Verma, D. Hernández-Silva, Mater. Sci. Eng., A 636, 326 (2015)CrossRef M.A. García-Bernal, R.S. Mishra, R. Verma, D. Hernández-Silva, Mater. Sci. Eng., A 636, 326 (2015)CrossRef
25.
Zurück zum Zitat Z. Zhang, B.Q. Han, Y. Zhou, E.J. Lavernia, Mater. Sci. Eng., A 493, 221 (2008)CrossRef Z. Zhang, B.Q. Han, Y. Zhou, E.J. Lavernia, Mater. Sci. Eng., A 493, 221 (2008)CrossRef
Metadaten
Titel
Corrosion and Creep Properties of Weld Beads Produced on AA5083-H111 Alloy Sheets Using SpinArc GMAW Process
verfasst von
V. Poonguzhali
M. Umar
P. Sathiya
Publikationsdatum
11.06.2019
Verlag
The Korean Institute of Metals and Materials
Erschienen in
Metals and Materials International / Ausgabe 1/2020
Print ISSN: 1598-9623
Elektronische ISSN: 2005-4149
DOI
https://doi.org/10.1007/s12540-019-00313-3

Weitere Artikel der Ausgabe 1/2020

Metals and Materials International 1/2020 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.