Creep behavior of INCOLOY alloy 617

verfasst von: Marcello Cabibbo, Elisabetta Gariboldi, Stefano Spigarelli, Dario Ripamonti

Erschienen in: Journal of Materials Science | Ausgabe 8/2008

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The microstructural features of INCOLOY alloy 617 in the solution annealed condition and after long-term creep tests at 700 and 800 °C were characterized and correlated with hardness and creep strength. Major precipitates included (Cr,Mo,Fe)23C6 carbides and the δ-Ni3Mo phase. M6C and MC carbides were also detected within the austenitic grains. However, minor precipitates particularly γ′-Ni3(Al,Ti) was found to play an important role. At different exposure temperatures, the microstructural features of the Ni–22Cr–12Co–9Mo alloy changed compared with the as-received condition. The presence of discontinuously precipitated (Cr,Mo,Fe)23C6 carbides and their coarsening until the formation of an intergranular film morphology could be responsible both for a reduction in rupture strength and for enhanced intergranular embrittlement. The fraction and morphology of the γ′-phase, precipitated during exposure to high temperature, also changed after 700 or 800 °C exposure. At the latter test temperature, a lower volume fraction of coarsened and more cubic γ′ precipitates were observed. These microstructural modifications, together with the presence of the δ-phase, detected only in specimens exposed to 700 °C, were clearly responsible for the substantially good creep response observed at 700 °C, compared with that found at 800 °C.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Blum R, Vanstone RW (2005) ParsonS 2003, 1st Int. Conf. super-high strength steels, 2–4 Nov. 2005, Rome Blum R, Vanstone RW (2005) ParsonS 2003, 1st Int. Conf. super-high strength steels, 2–4 Nov. 2005, Rome
2.
Zurück zum Zitat Viswanathan R, Hanry JF, Tanzosh J, Stanko G, Schlingledecker J (2005) In: Shibli IA, Holdsworth SR, Merckling G (eds) Proc Conf. creep & fracture at high temperature components, 12–14 Sept. 2005, DEStech Publications, Lancaster, PA, p 59 Viswanathan R, Hanry JF, Tanzosh J, Stanko G, Schlingledecker J (2005) In: Shibli IA, Holdsworth SR, Merckling G (eds) Proc Conf. creep & fracture at high temperature components, 12–14 Sept. 2005, DEStech Publications, Lancaster, PA, p 59
3.
Zurück zum Zitat Röster J, Götting M, Del Genovese D, Böttiger B, Kopp P, Wolske M, Shubert F, Pemkolla HJ, Seliga T, Thoma A, Sholz A, Berger C (2005) Adv Eng Mat 5:469 Röster J, Götting M, Del Genovese D, Böttiger B, Kopp P, Wolske M, Shubert F, Pemkolla HJ, Seliga T, Thoma A, Sholz A, Berger C (2005) Adv Eng Mat 5:469
4.
Zurück zum Zitat Donachie MJ, Donachie SJ (2002) Superalloys—a technical guide, 2nd edn. ASM International, Materials Park, OH, p 1 Donachie MJ, Donachie SJ (2002) Superalloys—a technical guide, 2nd edn. ASM International, Materials Park, OH, p 1
5.
6.
Zurück zum Zitat Cozar R, Pineau A (1973) Metall Mater Trans A4:47 Cozar R, Pineau A (1973) Metall Mater Trans A4:47
9.
Zurück zum Zitat Loomis WT, Freeman JW, Sponseller DL (1964) Metall Mater Trans A67:714 Loomis WT, Freeman JW, Sponseller DL (1964) Metall Mater Trans A67:714
10.
Zurück zum Zitat Jones RD, Kapoor S (1973) J Iron Steel Inst 211:226 Jones RD, Kapoor S (1973) J Iron Steel Inst 211:226
11.
Zurück zum Zitat Peters DT (1967) Trans TMS-AIME 239:1981 Peters DT (1967) Trans TMS-AIME 239:1981
12.
Zurück zum Zitat Allen D, Keustermans JP, Grijbels S, Bicego V (2004) Mater High Temp 21:53 Allen D, Keustermans JP, Grijbels S, Bicego V (2004) Mater High Temp 21:53
13.
14.
Zurück zum Zitat Rao GA, Prasad KS, Kumar M, Srinivas M, Sarma DS (2003) J Mater Sci Technol 19:1CrossRef Rao GA, Prasad KS, Kumar M, Srinivas M, Sarma DS (2003) J Mater Sci Technol 19:1CrossRef
15.
Zurück zum Zitat Rao GA, Kumar M, Srinivas M, Sarma DS (2003) Mater Sci Eng A355:114 Rao GA, Kumar M, Srinivas M, Sarma DS (2003) Mater Sci Eng A355:114
17.
Zurück zum Zitat Garzarotli F, Gerscha A, Francke FP (1969) Z Metallkunde 60:643 Garzarotli F, Gerscha A, Francke FP (1969) Z Metallkunde 60:643
18.
Zurück zum Zitat Sundararaman M, Mukhopadhyaya P, Benerjee S (1988) Mater Sci Forum 3:453 Sundararaman M, Mukhopadhyaya P, Benerjee S (1988) Mater Sci Forum 3:453
19.
20.
Zurück zum Zitat Sun WR, Guo SR, Lee JH, Park NK, Yoo YS, Choe SJ, Hu ZQ (1998) Mater Sci Eng A247:173 Sun WR, Guo SR, Lee JH, Park NK, Yoo YS, Choe SJ, Hu ZQ (1998) Mater Sci Eng A247:173
22.
Zurück zum Zitat Merrick HF (1995) Metall Mater Trans A7:505 Merrick HF (1995) Metall Mater Trans A7:505
23.
Zurück zum Zitat Valencia JJ, Spirko J, Schmees R (1997) In: Loria EA (ed) Superalloys 718, 625, 706 and various derivatives. TMS, Warredale, PA, p 753 Valencia JJ, Spirko J, Schmees R (1997) In: Loria EA (ed) Superalloys 718, 625, 706 and various derivatives. TMS, Warredale, PA, p 753
24.
Zurück zum Zitat Stoloff NS (1989) Int Mater Rev 34:153 Stoloff NS (1989) Int Mater Rev 34:153
25.
Zurück zum Zitat Marquez C, Esparane GL, Koul AK (1989) Int J Powder Met 25:301 Marquez C, Esparane GL, Koul AK (1989) Int J Powder Met 25:301
29.
Zurück zum Zitat Chen W, Chaturvedi M (1993) Can Metall Quart 32(4):363 Chen W, Chaturvedi M (1993) Can Metall Quart 32(4):363
30.
Zurück zum Zitat Campo E, Turco C, Catena V (1985) Metall Sci Tech, J. TEKSID, Italy, 3(1):16 Campo E, Turco C, Catena V (1985) Metall Sci Tech, J. TEKSID, Italy, 3(1):16
31.
Zurück zum Zitat Collins HE (1975) Metall Mater Trans 5:187 Collins HE (1975) Metall Mater Trans 5:187
32.
Zurück zum Zitat Kimball OF, Lai GY, Reynolds GH (1976) Metall Trans A 7:1951 Kimball OF, Lai GY, Reynolds GH (1976) Metall Trans A 7:1951
34.
Zurück zum Zitat Chen W, Chaturvedi M (1994) Mater Sci Eng A183:81 Chen W, Chaturvedi M (1994) Mater Sci Eng A183:81
35.
Zurück zum Zitat Xue H, Lijun W, Hui X, Runguang L, Shaogang W, Zhonglin C (2003) J Mater Proc Techn 137:17CrossRef Xue H, Lijun W, Hui X, Runguang L, Shaogang W, Zhonglin C (2003) J Mater Proc Techn 137:17CrossRef
36.
Zurück zum Zitat Betteridge W, Franklin AW (1957) J Inst Met 85:473 Betteridge W, Franklin AW (1957) J Inst Met 85:473
38.
Zurück zum Zitat Mathew MD, Sasikala G, Bhanu Sankara Rao K, Mannan SL (1991) Mater Sci Eng A148:253 Mathew MD, Sasikala G, Bhanu Sankara Rao K, Mannan SL (1991) Mater Sci Eng A148:253
39.
40.
Zurück zum Zitat Park C-J, Ahn M-K, Kwon H-S (2006) Mater Sci Eng A418:211 Park C-J, Ahn M-K, Kwon H-S (2006) Mater Sci Eng A418:211
41.
Zurück zum Zitat Dahotre NB, McCay MH, McCay TD, Hubbard CR, Porter WD, Cavin OB (1993) Scripta Metall Mater 28:1359CrossRef Dahotre NB, McCay MH, McCay TD, Hubbard CR, Porter WD, Cavin OB (1993) Scripta Metall Mater 28:1359CrossRef
42.
Zurück zum Zitat Evans ND, Maziasz PJ, Swindeman RW, Smith GD (2004) Scripta Mater 51:503CrossRef Evans ND, Maziasz PJ, Swindeman RW, Smith GD (2004) Scripta Mater 51:503CrossRef
43.
Zurück zum Zitat Zhao S, Xie X, Smith GD, Patel SJ (2003) Mater Sci Eng A355:96 Zhao S, Xie X, Smith GD, Patel SJ (2003) Mater Sci Eng A355:96
44.
Zurück zum Zitat Kindrachuk V, Wanderka N, Banhart J (2006) Mater Sci Eng A417:82 Kindrachuk V, Wanderka N, Banhart J (2006) Mater Sci Eng A417:82
45.
Zurück zum Zitat Murakumo T, Kobayashi T, Koizumi Y, Harada H (2004) Acta Mater 52:3737CrossRef Murakumo T, Kobayashi T, Koizumi Y, Harada H (2004) Acta Mater 52:3737CrossRef
46.
Zurück zum Zitat Shubert F, Bruch U, Cook R, Diehl H, Ennis PJ, Jakobeit W, Penkalla E, Ullrich G (1984) Nucl Technol 66:227 Shubert F, Bruch U, Cook R, Diehl H, Ennis PJ, Jakobeit W, Penkalla E, Ullrich G (1984) Nucl Technol 66:227
47.
Zurück zum Zitat Rai SK, Kumar A, Shankar V, Jayakurmar T, Rao KBS, Raj B (2004) Scripta Mater 51:59CrossRef Rai SK, Kumar A, Shankar V, Jayakurmar T, Rao KBS, Raj B (2004) Scripta Mater 51:59CrossRef
48.
Zurück zum Zitat Yuan H, Liu WC (2005) Mater Sci Eng A408:281 Yuan H, Liu WC (2005) Mater Sci Eng A408:281
49.
Zurück zum Zitat Liu L, Zhai C, Lu C, Ding W, Hirose A, Kobayashi KF (2005) Corros Sci 47:255 Liu L, Zhai C, Lu C, Ding W, Hirose A, Kobayashi KF (2005) Corros Sci 47:255
Metadaten
Titel
Creep behavior of INCOLOY alloy 617
verfasst von
Marcello Cabibbo
Elisabetta Gariboldi
Stefano Spigarelli
Dario Ripamonti
Publikationsdatum
01.04.2008
Verlag
Springer US
Erschienen in
Journal of Materials Science / Ausgabe 8/2008
Print ISSN: 0022-2461
Elektronische ISSN: 1573-4803
DOI
https://doi.org/10.1007/s10853-007-1803-7

Weitere Artikel der Ausgabe 8/2008

Journal of Materials Science 8/2008 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.