Crystal phase, microstructure and microwave properties of Ba2VxO7 (1.85 ≤ x ≤ 2.05) ceramics
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2020
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Crystal phase, microstructure and microwave properties of Ba2VxO7 (1.85 ≤ x ≤ 2.05) ceramics were researched. XRD results revealed that the single-phase Ba2V2O7 was formed when x ≥ 2, while the second-phase Ba3V2O8 was observed with 1.85 ≤ x < 2. Rietveld refinement demonstrated that the amount of Ba3V2O8 increased with the decline of vanadium content. Further, HRTEM observation verified that the co-existence of Ba3V2O8 and Ba2V2O7 in the sample for x = 1.9. Meanwhile, SAED pattern confirmed the triclinic structure of Ba2V2O7. The τf value presented a tendency of shifting to zero with the augment of Ba3V2O8. FWHM of the highest peak 884 cm−1 in Raman spectra proved that an appropriately absent vanadium ions improved the quality factor. The satisfied microwave properties of εr = 10.89, Q × f = 55,047 GHz (at 10 GHz), and τf = − 43.4 ppm/°C were achieved for Ba2V1.9O7 ceramic.