Crystallography of Martensite in Friction-Stir-Welded 12Cr Heat-Resistant Steel
Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 7/2019
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
In this work, electron backscatter diffraction (EBSD) was applied for examination of the crystallography of the martensitic structure produced during friction-stir welding (FSW) of 12Cr heat-resistant steel. The martensitic transformation was found to be governed by the Kurdjumov–Sachs (K-S) relation, viz. {111}γ || {110}α′ and 〈110〉γ || 〈111〉α′, was characterized by substantial variant selection and led to considerable orientation spread within the martensite variants. Due to the latter effect, the K-S model was found to be ineffective for the reconstruction of prior-austenite grain structure. Instead, the mixed orientation relation, viz. {111}γ || {110}α′, 〈110〉γ || 〈111〉α′, and 〈112〉γ || 〈110〉α′, was shown to be more suitable for this purpose.