Deposition and characterization of Cu2ZnSnS4 thin films for photovoltaic applications

verfasst von: A. Vasuhi, R. John Xavier

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 12/2016

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Cu2ZnSnS4 thin films were successfully deposited on glass substrates by a chemical bath deposition method for as-deposited and annealed films with different temperatures in sulphur atmosphere at 250 and 350 °C. The changes in structural and the optical phenomenon of as -deposited and annealed films have been studied. The powder X-ray diffraction (XRD) spectra show the tetragonal crystal structure of Cu2ZnSnS4(CZTS) thin films. The average crystallite size varies from 19.437 to 17.937 and 10.41 nm respectively, when the film was as-deposited and annealed at 250 and 350 °C. The surface morphologies of the as-grown surface show some voids with agglomerated particles. After sulphurization at 250 and 350 °C, the morphologies of the samples become dense. The band gap is estimated to be about 1.11 eV for the as-deposited film and 1.42 and 1.5 eV for the annealed films.
Vorheriger Artikel Role of rhodamine-B dye encapsulated mesoporous SiO2 in color tuning of SrAl2O4:Eu2+,Dy3+ composite long lasting phosphor
Nächster Artikel An intense single-component warm-white-light Sr3Lu(PO4)3:Dy3+ phosphor for white UV-LEDs

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Jetzt informieren

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Jetzt informieren
Literatur
1.
P. Song, Y. Li, F. Ma, T. Pullerits, M. Sun, Chem. Rec. 16, 734 (2010)CrossRef
2.
3.
P. Song, Y. Li, F. Ma, T. Pullerits, M. Sun, J. Phys. Chem. C 117, 15879 (2013)CrossRef
4.
Y. Li, T. Pullerits, M. Zhao, M. Sun, J. Phys. Chem. C 115, 21865 (2011)CrossRef
5.
6.
7.
K. Akimoto, S. Ishizuka, M. Yanagita, Y. Nawa, G.K. Paul, T. Sakurai, Sol. Energy 80, 715 (2006)CrossRef
8.
K.V. Gurav, J.H. Yun, S.M. Pawar, S.W. Shin, M.P. Suryawanshi, Y.K. Kim, G.L. Agawane, P.S. Patil, J.H. Kim, Mater. Lett. 108, 316 (2013)CrossRef
9.
S.S. Mali, P.S. Shinde, C.A. Betty, P.N. Bhosale, Y.W. Oh, P.S. Patil, J. Phys. Chem. Solids 73, 735 (2012)CrossRef
10.
M.A. Majeed Khan, S. Kumar, M. Alhoshan, A.S. Al Dwayyan, Opt. Laser Technol. 49, 196 (2013)CrossRef
11.
M. Cao, L. Li, B.L. Zhang, J. Huang, L.J. Wang, Y. Shen, Y. Sun, J.C. Jiang, G.J. Hu, Sol. Energy Matar. Sol. Cell 117, 81 (2013)CrossRef
12.
S. Kahraman, S. Cetinkaya, M. Podlogar, S. Bernik, H.A. Cetinkara, H.S. Guder, Ceram. Int. 39, 9285 (2013)CrossRef
13.
14.
S. Ahmed, K.B. Reuter, O. Gunawan, L. Guo, L.T. Romankiw, H. Deligianni, Adv. Energy Mater. 2, 253 (2011)CrossRef
15.
A.T. Ravichandran, K. Dhanabalan, S. Valanarasu, A. Vasuhi, A. Kathalingam, J. Mater. Sci. Mater. Electron. 26, 921 (2015)CrossRef
16.
K. Ravichandran, G. Muruganantham, B. Sakthivel, Phys. B 404, 4299 (2009)CrossRef
17.
18.
A.T. Ravichandran, K. Dhanabalan, A. Vasuhi, R. Chandramohan, S. Mantha, IEEE Trans. Nanotechnol. 1, 108 (2015)CrossRef
19.
20.
S. Suwanboon, P. Amornpitoksuk, A. Haidoux, J.C. Tedenac, J. Alloy. Compd. 462, 335 (2008)CrossRef
21.
V. Kheraj, K.K. Patel, S.J. Patel, D.V. Shah, J. Cryst. Growth 362, 174 (2013)CrossRef
22.
R.B. Bylsma, W.M. Becker, J. Kossut, U. Debska, D. Yoder-Short, Phys. Rev. B 33, 8207 (1986)CrossRef
23.
S. Suwanboon, T. Ratana, T. Ratana, J Sci Tech. 4, 111 (2007)
24.
V.G. Rajeshmon, C.S. Kartha, K.P. Vijayakumar, C. Sanjeeviraja, T. Abe, Y. Kashiwab, Sol. Energy 85, 249 (2011)CrossRef
25.
A.T. Ravichandran, K. Dhanabalan, R. Chandramohan, A. Vasuhi, P. Parameswaran, IJIRR. 1, 007 (2014)
26.
Metadaten
Titel
Deposition and characterization of Cu2ZnSnS4 thin films for photovoltaic applications
verfasst von
A. Vasuhi
R. John Xavier
Publikationsdatum
08.08.2016
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 12/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-016-5469-2

Weitere Artikel der Ausgabe 12/2016

Room-temperature ferromagnetic and optical properties of Cr-doped CdS nanoparticles via a solvothermal preparation

Investigation of the structural, optical and magnetic properties of Eu2(WO4)3 nanoparticles synthesized via a wet chemical route

Facile synthesis of Ag@AgBr nanospheres as highly efficient, recyclable and sunlight photocatalyst

(K0.5Na0.5)0.96Li0.04Nb0.86Ta0.1Sb0.04O3–SrZrO3 ceramics with good fatigue-resistance and temperature-stable piezoelectric properties

Strength and its prediction models based on fracture mechanics of thin layers copper cladding steel wires under different amount of deformation

Signature of multiferroicity and impedance analysis of Co1−xZnxFe2−xLaxO4 nanoparticles