Effect of Bi and Li co-substituted SrTiO3 ceramics on structural and dielectric properties
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 9/2016
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
Polycrystalline Sr(1–x)(Bi, Li)xTiO3 ceramics (x = 0 and 0.02) are prepared by a microwave processing method. The effect of co-substitution on structural, dielectric properties and ac-conductivity were investigated. The XRD of ceramics shows single phase with cubic structure. The lattice parameter of the compounds is estimated from the XRD patterns which confirm the incorporation of Bi and Li in SrTiO3 ceramics. Studies revealed that the dielectric constant and dielectric loss increased with an increase of temperature and decreased with an increase in frequency. The maximum dielectric constant obtained at room temperature is around 570 and increased to around 104 at 600 °C measured at 1 kHz frequency whereas the maximum dielectric loss measured was 0.048 at 600 °C and the loss measured at room temperature is 0.02. The activation energy of the samples were investigated using Arrhenius plots.