Effect of CuO–Bi₂O₃ on low temperature sintered MnZn-ferrite by sol–gel auto-combustion method

A sol–gel auto-combustion method was investigated to incorporate small amounts of additives of Cu and Bi uniformly into soft magnetic MnZn-ferrite nanoparticles, which were prepared by Fe(NO₃)₃·9H₂O, Mn(NO₃)₂ and Zn(NO₃)₂·6H₂O dissolved in water and citric acid. The powder was characterized by the X-ray diffraction analysis and transmission electron microscope method. The effects of nano-particle sized powders in microstructure development and adding CuO–Bi₂O₃ into MnZn-ferrite on phase formation, densification process as well as magnetic properties were studied by scanning electron microscope and vibrating sample magnetometer techniques. The sample without additive can be sintered well at 930 °C, while the samples with a small amount of the additive can be sintered at less than 900 °C. Obviously, the micron-sized powders exhibited high sintering activity. It was also found that CuO–Bi₂O₃ additive promoted the growth of grains and improved magnetic properties. The permeability and the saturation magnetization were improved substantially by adding CuO–Bi₂O₃ into MnZn-ferrite and the sintering temperature was lowered to 875 °C, which may be associated with the redistribution of cations on the tetrahedral (A) sites and octahedral (B) sites within the spinel lattice.