Effect of different alkali carbonate on the microstructure and photoluminescent properties of YInGe2O7:Eu3+ phosphors

verfasst von: Huang-Yu Chen, Hsuan-Lin Lai, Ru-Yuan Yang, Shoou-Jinn Chang

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 3/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

For this study, different alkali carbonates (Li2CO3, Na2CO3, and K2CO3) were added to a Eu3+ activated YInGe2O7 phosphor synthesized using conventional sintering and microwave-assisted sintering. The morphology and photoluminescence properties of YInGe2O7:Eu3+ phosphors were investigated and discussed. When the alkali ions were introduced into YInGe2O7:Eu3+ phosphors, the excitation peaks of phosphors were shifted to a short wavelength because the addition of alkali ions may increase the oxygen vacancy in YInGe2O7:Eu3+ phosphors. Additionally, the best enhanced luminescent properties in YInGe2O7:Eu3+ phosphors were obtained through the addition of Li+ ion.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat S.D. Cheng, C.H. Kam, S. Buddhudu, Mater. Res. Bull. 36, 1131–1137 (2001)CrossRef S.D. Cheng, C.H. Kam, S. Buddhudu, Mater. Res. Bull. 36, 1131–1137 (2001)CrossRef
2.
Zurück zum Zitat S. Shionoya, W.M. Yen, Phosphor Handbook (CRC Press, Boca Raton, 1999) S. Shionoya, W.M. Yen, Phosphor Handbook (CRC Press, Boca Raton, 1999)
3.
Zurück zum Zitat S. Oshion, K. Kitamura, T. Shigeta et al., J. Electrochem. Soc. 146, 392–399 (1999)CrossRef S. Oshion, K. Kitamura, T. Shigeta et al., J. Electrochem. Soc. 146, 392–399 (1999)CrossRef
4.
Zurück zum Zitat R.Y. Yang, H.Y. Chen, C.M. Hsiung et al., Ceram. Int. 37(3), 749–752 (2011)CrossRef R.Y. Yang, H.Y. Chen, C.M. Hsiung et al., Ceram. Int. 37(3), 749–752 (2011)CrossRef
5.
Zurück zum Zitat R.Y. Yang, M.H. Weng, H.Y. Chen et al., J. Lumin. 132(2), 478–483 (2012)CrossRef R.Y. Yang, M.H. Weng, H.Y. Chen et al., J. Lumin. 132(2), 478–483 (2012)CrossRef
6.
7.
Zurück zum Zitat F. Duault, M. Junker, P. Grosseau et al., Powder Technol. 154(2), 132–137 (2005)CrossRef F. Duault, M. Junker, P. Grosseau et al., Powder Technol. 154(2), 132–137 (2005)CrossRef
8.
Zurück zum Zitat D. Haranath, P. Sharma, H. Chander et al., Mater. Chem. Phys. 101, 163–169 (2007)CrossRef D. Haranath, P. Sharma, H. Chander et al., Mater. Chem. Phys. 101, 163–169 (2007)CrossRef
9.
Zurück zum Zitat H.Y. Chen, R.Y. Yang, S.J. Chang, Adv. Mat. Res. 684(5), 274–278 (2013) H.Y. Chen, R.Y. Yang, S.J. Chang, Adv. Mat. Res. 684(5), 274–278 (2013)
10.
Zurück zum Zitat K. Uematsu, K. Toda, M. Sato, J. Alloys Compd. 389(1–2), 209–214 (2005)CrossRef K. Uematsu, K. Toda, M. Sato, J. Alloys Compd. 389(1–2), 209–214 (2005)CrossRef
11.
Zurück zum Zitat K. Ming, L. Jun, Y. Guangfu et al., Rare Met. 28(5), 439–444 (2009)CrossRef K. Ming, L. Jun, Y. Guangfu et al., Rare Met. 28(5), 439–444 (2009)CrossRef
13.
Zurück zum Zitat J.S. Bae, S.S. Park, T.E. Hong et al., Curr. Appl. Phys. 9, S241–S244 (2009)CrossRef J.S. Bae, S.S. Park, T.E. Hong et al., Curr. Appl. Phys. 9, S241–S244 (2009)CrossRef
14.
Zurück zum Zitat S.H. Byeon, K.G. Ko, J.C. Park, D.K. Kim, Chem. Mater. 14, 603–608 (2002)CrossRef S.H. Byeon, K.G. Ko, J.C. Park, D.K. Kim, Chem. Mater. 14, 603–608 (2002)CrossRef
15.
Zurück zum Zitat S.H. Sohn, D.G. Hun, A. Yamada, Y. Hamaka, Appl. Phys. Lett. 62, 991–993 (1993)CrossRef S.H. Sohn, D.G. Hun, A. Yamada, Y. Hamaka, Appl. Phys. Lett. 62, 991–993 (1993)CrossRef
Metadaten
Titel
Effect of different alkali carbonate on the microstructure and photoluminescent properties of YInGe2O7:Eu3+ phosphors
verfasst von
Huang-Yu Chen
Hsuan-Lin Lai
Ru-Yuan Yang
Shoou-Jinn Chang
Publikationsdatum
25.11.2015
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 3/2016
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-015-4116-7

Weitere Artikel der Ausgabe 3/2016

Journal of Materials Science: Materials in Electronics 3/2016 Zur Ausgabe

Neuer Inhalt