Effect of Grain Boundary Character Distribution on the Adiabatic Shear Susceptibility

verfasst von: Yang Yang, Lihong Jiang, Shuhong Luo, Haibo Hu, Tiegang Tang, Qingming Zhang

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 11/2016

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The adiabatic shear susceptibility of AISI321 stainless steels with different grain boundary character distributions (GBCDs) was investigated by means of split-Hopkinson pressure bar. The results indicate that the width of the adiabatic shear band of the specimen after thermomechanical processing (TMP) treatment is narrower. The comparison of the stress collapse time, the critical stress, and the adiabatic shear forming energy suggests that the TMP specimens have lower adiabatic shear susceptibility than that of the solution-treated samples under the same loading condition. GBCD and grain size affected the adiabatic shear susceptibility. The high-angle boundary network of the TMP specimens was interrupted or replaced by the special grain boundary, and smaller grain size hindered the adiabatic shearing.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat K. Sun, X.D. Yu, C.W. Tan, H. L. Ma, F.C. Wang and H.N. Cai: Mater. Sci. Eng. A, 2014, vol.595, pp 247–256. CrossRef K. Sun, X.D. Yu, C.W. Tan, H. L. Ma, F.C. Wang and H.N. Cai: Mater. Sci. Eng. A, 2014, vol.595, pp 247–256. CrossRef
2.
Zurück zum Zitat Z.P. Wan, Y.E. Zhu, H.W. Liu and Y .Tang: Mater. Sci. Eng. A, 2012, vol.531, pp155-163. CrossRef Z.P. Wan, Y.E. Zhu, H.W. Liu and Y .Tang: Mater. Sci. Eng. A, 2012, vol.531, pp155-163. CrossRef
3.
Zurück zum Zitat Y. Yang, B.F. Wang, J. Xiong, Y. Zeng, Z. P. Chen and X. Y. Yang: Mater. Lett., 2006, vol.60, pp2198-2202. CrossRef Y. Yang, B.F. Wang, J. Xiong, Y. Zeng, Z. P. Chen and X. Y. Yang: Mater. Lett., 2006, vol.60, pp2198-2202. CrossRef
4.
Zurück zum Zitat W. C. Lee, C.F. Lin, T. H. Chen and W. Z. Luo: J. Nucl. Mater., 2012, vol. 420, pp226–234. CrossRef W. C. Lee, C.F. Lin, T. H. Chen and W. Z. Luo: J. Nucl. Mater., 2012, vol. 420, pp226–234. CrossRef
5.
Zurück zum Zitat M.A. Meyers, Y.B. Xu, Q. Xue, M.T. Pérez-Prado and T.R. McNelley: Acta Mater., 2003, vol.51, pp 1307-1325. CrossRef M.A. Meyers, Y.B. Xu, Q. Xue, M.T. Pérez-Prado and T.R. McNelley: Acta Mater., 2003, vol.51, pp 1307-1325. CrossRef
6.
Zurück zum Zitat B.F. Wang, Z.L. Liu, X.Y. Wang and Z.Z. Li: Mater. Sci. Eng. A, 2014, vol.610, pp301–308. CrossRef B.F. Wang, Z.L. Liu, X.Y. Wang and Z.Z. Li: Mater. Sci. Eng. A, 2014, vol.610, pp301–308. CrossRef
7.
Zurück zum Zitat Q. Xue, X.Z. Liao, Y.T. Zhu and G.T. Gray III: Mater. Sci. Eng. A, 2005, vol.410, pp 252–256. CrossRef Q. Xue, X.Z. Liao, Y.T. Zhu and G.T. Gray III: Mater. Sci. Eng. A, 2005, vol.410, pp 252–256. CrossRef
8.
Zurück zum Zitat L.H. Dai, L.F. Liu and Y.L. Bai: Mater. Lett., 2004, vol.58, pp 1773-1776. CrossRef L.H. Dai, L.F. Liu and Y.L. Bai: Mater. Lett., 2004, vol.58, pp 1773-1776. CrossRef
9.
Zurück zum Zitat J.X. Liu, S.K. Li, A.L. Fan and H.C. Sun: Mater. Sci. Eng. A 2008, vol. 487, pp 235-242. CrossRef J.X. Liu, S.K. Li, A.L. Fan and H.C. Sun: Mater. Sci. Eng. A 2008, vol. 487, pp 235-242. CrossRef
10.
Zurück zum Zitat Y. Yang, X.M. Li, X.L. Tong, Q.M. Zhang, C.Y. Xu: Mater. Sci. Eng. A, 2010, vol. 528, pp 3130-3133. CrossRef Y. Yang, X.M. Li, X.L. Tong, Q.M. Zhang, C.Y. Xu: Mater. Sci. Eng. A, 2010, vol. 528, pp 3130-3133. CrossRef
11.
Zurück zum Zitat B.B. Singh, G. Sukumar, A. Bhattacharjee, K.S. Kumar, T.B. Bhat, A.K. Gogia: Mater Design, 2012, vol. 36, pp 640-649. CrossRef B.B. Singh, G. Sukumar, A. Bhattacharjee, K.S. Kumar, T.B. Bhat, A.K. Gogia: Mater Design, 2012, vol. 36, pp 640-649. CrossRef
12.
Zurück zum Zitat Z.G. Wei, J.L. Yu, J.R. Li, Y.C. Li and S.S. Hu: Int. J. Impact Eng., 2001, vol.26, pp 843-852. CrossRef Z.G. Wei, J.L. Yu, J.R. Li, Y.C. Li and S.S. Hu: Int. J. Impact Eng., 2001, vol.26, pp 843-852. CrossRef
13.
Zurück zum Zitat W.S. Lee, T.H.Chen and G.T. Lu: Mater. Sci. Tech., 2010, vol.26, pp 720-725. CrossRef W.S. Lee, T.H.Chen and G.T. Lu: Mater. Sci. Tech., 2010, vol.26, pp 720-725. CrossRef
14.
Zurück zum Zitat X.Y. Wang, P.F. Yu, C. L. Tan: Mater. Sci. Tech., 2014, vol.30, pp 1966-1972. CrossRef X.Y. Wang, P.F. Yu, C. L. Tan: Mater. Sci. Tech., 2014, vol.30, pp 1966-1972. CrossRef
15.
Zurück zum Zitat B. D. Alexandreanua, B. H. Sencera, V. Thaveeprungsripornb and G.S. Was: Acta Mater.,2003, vol.51, pp3831-3848. CrossRef B. D. Alexandreanua, B. H. Sencera, V. Thaveeprungsripornb and G.S. Was: Acta Mater.,2003, vol.51, pp3831-3848. CrossRef
16.
Zurück zum Zitat M. Shimada, H. Kokawa, Z. J. Wang, Y.S. Sato and I. Karibe: Acta Mater., 2002, vol.50, pp 2331-2341. CrossRef M. Shimada, H. Kokawa, Z. J. Wang, Y.S. Sato and I. Karibe: Acta Mater., 2002, vol.50, pp 2331-2341. CrossRef
17.
Zurück zum Zitat B.M. Guyot and N.L. Richards: Mater. Sci. Eng. A, 2005, vol.395, pp 87-97. CrossRef B.M. Guyot and N.L. Richards: Mater. Sci. Eng. A, 2005, vol.395, pp 87-97. CrossRef
18.
19.
Zurück zum Zitat U. Andrade, M.A. Meyers, K.S. Vecchio and A.H. Chokshi: Acta Metall. Mater.,1994, vol.42, pp3183-3195. CrossRef U. Andrade, M.A. Meyers, K.S. Vecchio and A.H. Chokshi: Acta Metall. Mater.,1994, vol.42, pp3183-3195. CrossRef
21.
Zurück zum Zitat Q. Li, P. Zmudzki, S. Alameeri, M.N. Bassim: Mater. Sci. Tech., 2004, vol.20, pp676-678. CrossRef Q. Li, P. Zmudzki, S. Alameeri, M.N. Bassim: Mater. Sci. Tech., 2004, vol.20, pp676-678. CrossRef
22.
Zurück zum Zitat S.P. Timothy and I.M. Hutchings: Acta Metall., 1985, vol.33, pp 667-676. CrossRef S.P. Timothy and I.M. Hutchings: Acta Metall., 1985, vol.33, pp 667-676. CrossRef
23.
Zurück zum Zitat M. El Wahabi, L. Gavard, J.M. Cabrera, J.M. Prado, F. Montheillet: Mater. Sci. Eng. A 2005, vol.393, pp 83–90. CrossRef M. El Wahabi, L. Gavard, J.M. Cabrera, J.M. Prado, F. Montheillet: Mater. Sci. Eng. A 2005, vol.393, pp 83–90. CrossRef
Metadaten
Titel
Effect of Grain Boundary Character Distribution on the Adiabatic Shear Susceptibility
verfasst von
Yang Yang
Lihong Jiang
Shuhong Luo
Haibo Hu
Tiegang Tang
Qingming Zhang
Publikationsdatum
17.08.2016
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 11/2016
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-016-3721-2

Weitere Artikel der Ausgabe 11/2016

Metallurgical and Materials Transactions A 11/2016 Zur Ausgabe

Symposium: New Steels for Applications under Extreme Conditions

Nano-precipitation Strengthened G91 by Thermo-mechanical Treatment Optimization

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.