Effect of Hydrogen on the Substructure of Lenticular Martensite in Fe-31Ni Alloy

verfasst von: Akinobu Shibata, Masanori Enoki, Nahoko Saji, Hirotaka Tai, Motomichi Koyama, Hiroshi Ohtani, Nobuhiro Tsuji, Kaneaki Tsuzaki

Erschienen in: Metallurgical and Materials Transactions A | Ausgabe 9/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

This study investigated the effect of hydrogen on the substructure of martensite in Fe-31Ni alloy. In both the hydrogen-charged and uncharged specimens, typical lenticular martensite plates formed after subzero cooling. However, we found that the fraction of twinned region (including the area of midrib) in lenticular martensite plate increased with increasing hydrogen content. In addition, the width of individual twins in the hydrogen-charged specimen was slightly smaller than that in the uncharged specimen. These results indicated that the existence of hydrogen facilitated twinning deformation as a lattice invariant deformation. We presented a comprehensive discussion about the reason why hydrogen enhanced twinning deformation. Even though tetragonality of martensite in the hydrogen-charged specimen could not be confirmed by X-ray diffraction, the transmission electron microscopy observations and the first-principles calculations suggested that hydrogen might increase the tetragonality of martensite. We proposed that solid solution hardening and an increase in the tetragonality of martensite by the existence of hydrogen were the possible reasons for facilitating twinning deformation as a lattice invariant deformation in martensitic transformation.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Fußnoten
1
JEOL is a trademark of Japan Electron Optics Ltd., Tokyo.
 
Literatur
2.
Zurück zum Zitat 2.I.A. Robertson, P. Sofronis, A. Nagao, M.L. Martin, S. Wang, D.W. Gross, and K.E. Nygren: Metall. Mater. Trans. B, 2015, vol. 46B, pp. 1085–1103.CrossRef 2.I.A. Robertson, P. Sofronis, A. Nagao, M.L. Martin, S. Wang, D.W. Gross, and K.E. Nygren: Metall. Mater. Trans. B, 2015, vol. 46B, pp. 1085–1103.CrossRef
3.
Zurück zum Zitat 3.M. Dadfarnia, A. Nagao, S. Wang, M.L. Martin, B.P. Somerday, and P. Sofronis: Int. J. Fract., 2015, vol. 196, pp. 223–43.CrossRef 3.M. Dadfarnia, A. Nagao, S. Wang, M.L. Martin, B.P. Somerday, and P. Sofronis: Int. J. Fract., 2015, vol. 196, pp. 223–43.CrossRef
4.
5.
Zurück zum Zitat 5.P.J. Ferreira, I.M. Robertson, and H.K. Birnbaum: Acta Mater., 1998, vol. 46, pp. 1749–57.CrossRef 5.P.J. Ferreira, I.M. Robertson, and H.K. Birnbaum: Acta Mater., 1998, vol. 46, pp. 1749–57.CrossRef
6.
7.
Zurück zum Zitat 7.P. Sofronis and I.M. Robertson: Philos. Mag. A, 2002, vol. 82, pp. 3405–13.CrossRef 7.P. Sofronis and I.M. Robertson: Philos. Mag. A, 2002, vol. 82, pp. 3405–13.CrossRef
8.
Zurück zum Zitat 8.M. Tanino, H. Komatsu, and S. Fukai: Phys. Colloq., 1982, vol. 43 (C4), pp. 503–08. 8.M. Tanino, H. Komatsu, and S. Fukai: Phys. Colloq., 1982, vol. 43 (C4), pp. 503–08.
9.
Zurück zum Zitat 9.M.L. Martin, J.A. Fenske, G.S. Liu, P. Sofronis, and I.M. Robertson: Acta Mater., 2011, vol. 59, pp. 1601–06.CrossRef 9.M.L. Martin, J.A. Fenske, G.S. Liu, P. Sofronis, and I.M. Robertson: Acta Mater., 2011, vol. 59, pp. 1601–06.CrossRef
10.
Zurück zum Zitat 10.Y.H. Kim and J.W. Morris, Jr.: Metall. Trans. A, 1983, vol. 14A, pp. 1883–88.CrossRef 10.Y.H. Kim and J.W. Morris, Jr.: Metall. Trans. A, 1983, vol. 14A, pp. 1883–88.CrossRef
11.
Zurück zum Zitat 11.Y.H. Kim, H.J. Kim, and J.W. Morris, Jr.: Metall. Trans. A, 1986, vol. 17A, pp. 1157–64.CrossRef 11.Y.H. Kim, H.J. Kim, and J.W. Morris, Jr.: Metall. Trans. A, 1986, vol. 17A, pp. 1157–64.CrossRef
12.
Zurück zum Zitat 12.A. Nagao, C.D. Smith, M. Dadfarnia, P. Sofronis, and I.M. Robertson: Acta Mater., 2012, vol. 60, pp. 5182–89.CrossRef 12.A. Nagao, C.D. Smith, M. Dadfarnia, P. Sofronis, and I.M. Robertson: Acta Mater., 2012, vol. 60, pp. 5182–89.CrossRef
13.
Zurück zum Zitat 13.A. Shibata, T. Murata, H. Takahashi, T. Matsuoka, and N. Tsuji: Metall. Mater. Trans. A, 2015, vol. 46A, pp. 5685–96.CrossRef 13.A. Shibata, T. Murata, H. Takahashi, T. Matsuoka, and N. Tsuji: Metall. Mater. Trans. A, 2015, vol. 46A, pp. 5685–96.CrossRef
14.
Zurück zum Zitat 14.Q. Yang and J.L. Luo: Mater. Sci. Eng. A, 2000, vol. A238, pp. 75–83.CrossRef 14.Q. Yang and J.L. Luo: Mater. Sci. Eng. A, 2000, vol. A238, pp. 75–83.CrossRef
15.
Zurück zum Zitat 15.Y. Murakami, T. Kanezaki, Y. Mine, and S. Matsuoka: Metall. Mater. Trans. A, 2008, vol. 39A, pp. 1327–39.CrossRef 15.Y. Murakami, T. Kanezaki, Y. Mine, and S. Matsuoka: Metall. Mater. Trans. A, 2008, vol. 39A, pp. 1327–39.CrossRef
16.
Zurück zum Zitat 16.T. Kanezaki, C. Narazaki, Y. Mine, S. Matsuoka, and Y. Murakami: Int. J. Hydrogen Energy, 2008, vol. 33, pp. 2604–19.CrossRef 16.T. Kanezaki, C. Narazaki, Y. Mine, S. Matsuoka, and Y. Murakami: Int. J. Hydrogen Energy, 2008, vol. 33, pp. 2604–19.CrossRef
17.
Zurück zum Zitat 17.T. Maki: Mater Sci. Forum, 1990, vols. 56–58, pp. 157–68. 17.T. Maki: Mater Sci. Forum, 1990, vols. 56–58, pp. 157–68.
18.
Zurück zum Zitat 18.R.L. Patterson and C.M. Wayman: Acta Metall., 1966, vol. 14, pp. 347–69.CrossRef 18.R.L. Patterson and C.M. Wayman: Acta Metall., 1966, vol. 14, pp. 347–69.CrossRef
19.
Zurück zum Zitat 19.A. Shibata, S. Morito, T. Furuhara, and T. Maki: Scripta Mater., 2005, vol. 53, pp. 597–602.CrossRef 19.A. Shibata, S. Morito, T. Furuhara, and T. Maki: Scripta Mater., 2005, vol. 53, pp. 597–602.CrossRef
20.
Zurück zum Zitat 20.A. Shibata, S. Morito, T. Furuhara, and T. Maki: Acta Mater., 2009, vol. 57, pp. 483–92.CrossRef 20.A. Shibata, S. Morito, T. Furuhara, and T. Maki: Acta Mater., 2009, vol. 57, pp. 483–92.CrossRef
21.
Zurück zum Zitat K.D. Zilnyk, D.R. A. Junior, H.R.Z. Sandim, P.R. Rios, and D. Raabe: Acta Mater., 2018, vol. 143, pp. 227–36.CrossRef K.D. Zilnyk, D.R. A. Junior, H.R.Z. Sandim, P.R. Rios, and D. Raabe: Acta Mater., 2018, vol. 143, pp. 227–36.CrossRef
22.
Zurück zum Zitat 22.H.J Neuhauser and W. Pitsch: Acta Metall., 1971, vol. 19, pp. 337–44.CrossRef 22.H.J Neuhauser and W. Pitsch: Acta Metall., 1971, vol. 19, pp. 337–44.CrossRef
23.
Zurück zum Zitat 23.T. Kakeshita, K. Shimizu, T. Maki, and I. Tamura: Scripta Metall., 1980, vol. 14, pp. 1067–70.CrossRef 23.T. Kakeshita, K. Shimizu, T. Maki, and I. Tamura: Scripta Metall., 1980, vol. 14, pp. 1067–70.CrossRef
24.
Zurück zum Zitat 24.A. Shibata, T. Murakami, S. Morito, T. Furuhara, and T. Maki: Mater. Trans., 2008, vol. 49, pp. 1242–48.CrossRef 24.A. Shibata, T. Murakami, S. Morito, T. Furuhara, and T. Maki: Mater. Trans., 2008, vol. 49, pp. 1242–48.CrossRef
25.
Zurück zum Zitat 25.M. Koyama, T. Ogawa, D. Yan, Y. Matsumoto, C.C. Tasan, K. Takai, and K. Tsuzaki: Int. J. Hydrogen Energy, 2017, vol. 42, pp. 26423–26435.CrossRef 25.M. Koyama, T. Ogawa, D. Yan, Y. Matsumoto, C.C. Tasan, K. Takai, and K. Tsuzaki: Int. J. Hydrogen Energy, 2017, vol. 42, pp. 26423–26435.CrossRef
26.
Zurück zum Zitat 26.G. Kresse and J. Furthmüller: Phys. Rev. B, 1996, vol. 54, pp. 11169–11186.CrossRef 26.G. Kresse and J. Furthmüller: Phys. Rev. B, 1996, vol. 54, pp. 11169–11186.CrossRef
27.
Zurück zum Zitat 27.G. Kresse and D. Joubert: Phys. Rev. B, 1999, vol. 59, pp. 1758–75.CrossRef 27.G. Kresse and D. Joubert: Phys. Rev. B, 1999, vol. 59, pp. 1758–75.CrossRef
28.
29.
Zurück zum Zitat 29.H.C. Herper, E. Hoffmann, and P. Entel: Phys. Rev. B, 1999, vol. 60, pp. 3839–48.CrossRef 29.H.C. Herper, E. Hoffmann, and P. Entel: Phys. Rev. B, 1999, vol. 60, pp. 3839–48.CrossRef
30.
Zurück zum Zitat 30.H. Ohtsuka, V.A. Dinh, T. Ohno, K. Tsuzaki, K. Tsuchiya, R. Sahara, H. Kitazawa, and T. Nakamura: ISIJ Int., 2015, vol. 55, pp. 2483–91.CrossRef 30.H. Ohtsuka, V.A. Dinh, T. Ohno, K. Tsuzaki, K. Tsuchiya, R. Sahara, H. Kitazawa, and T. Nakamura: ISIJ Int., 2015, vol. 55, pp. 2483–91.CrossRef
31.
Zurück zum Zitat R.F. Bunshah and R.F. Mehl: Trans. AIME, 1953, vol. 197, pp. 1251–58. R.F. Bunshah and R.F. Mehl: Trans. AIME, 1953, vol. 197, pp. 1251–58.
32.
Zurück zum Zitat 32.H.K. Birnbaum and P. Sofronis: Mater. Sci. Eng. A, 1994, vol. 176A, pp. 191–202.CrossRef 32.H.K. Birnbaum and P. Sofronis: Mater. Sci. Eng. A, 1994, vol. 176A, pp. 191–202.CrossRef
33.
Zurück zum Zitat 33.Y. Tobe and W.R. Tyson: Scripta Metall., 1977, vol. 11, pp. 849–52.CrossRef 33.Y. Tobe and W.R. Tyson: Scripta Metall., 1977, vol. 11, pp. 849–52.CrossRef
34.
Zurück zum Zitat 34.M. Umemoto, K. Minoda, and I. Tamura: Metallography, 1982, vol. 15, pp. 177–91.CrossRef 34.M. Umemoto, K. Minoda, and I. Tamura: Metallography, 1982, vol. 15, pp. 177–91.CrossRef
35.
Zurück zum Zitat 35.T. Maki, S. Shimooka, S. Fujiwara, and T. Tamura: Trans. JIM, 1975, vol. 16, pp. 35–41.CrossRef 35.T. Maki, S. Shimooka, S. Fujiwara, and T. Tamura: Trans. JIM, 1975, vol. 16, pp. 35–41.CrossRef
36.
Zurück zum Zitat 36.S. Kajiwara and W.S. Owen: Scripta Metall., 1977, vol. 11, pp. 137–42.CrossRef 36.S. Kajiwara and W.S. Owen: Scripta Metall., 1977, vol. 11, pp. 137–42.CrossRef
37.
Zurück zum Zitat 37.R.G. Davies and C.L. Magee: Metall. Trans., 1970, vol. 1, pp. 2927–31. 37.R.G. Davies and C.L. Magee: Metall. Trans., 1970, vol. 1, pp. 2927–31.
38.
Zurück zum Zitat 38.C.L. Magee and R.G. Davies: Acta Metall., 1972, vol. 20, pp. 1031–43.CrossRef 38.C.L. Magee and R.G. Davies: Acta Metall., 1972, vol. 20, pp. 1031–43.CrossRef
39.
Zurück zum Zitat 39.A. Shibata, H. Yonezawa, K. Yabuuchi, S. Morito, T. Furuhara, and T. Maki: Mater. Sci. Eng. A, 2006, vols. 438–440, pp. 241–45.CrossRef 39.A. Shibata, H. Yonezawa, K. Yabuuchi, S. Morito, T. Furuhara, and T. Maki: Mater. Sci. Eng. A, 2006, vols. 438–440, pp. 241–45.CrossRef
40.
Zurück zum Zitat 40.M. Koyama, Y. Abe, K. Saito, E. Akiyama, K. Takai, and K. Tsuzaki: Scripta Mater., 2016, vol. 122, pp. 50–53.CrossRef 40.M. Koyama, Y. Abe, K. Saito, E. Akiyama, K. Takai, and K. Tsuzaki: Scripta Mater., 2016, vol. 122, pp. 50–53.CrossRef
41.
Zurück zum Zitat T. Maki and C.M. Wayman: Proc. 1st JIM Int. Symp. on New Aspects of Martensitic Transformation, Suppl. Trans. JIM, 1976. vol. 17, pp. 69–74. T. Maki and C.M. Wayman: Proc. 1st JIM Int. Symp. on New Aspects of Martensitic Transformation, Suppl. Trans. JIM, 1976. vol. 17, pp. 69–74.
42.
Zurück zum Zitat 42.Z. Nishiyama: Martensitic Transformation, Academic Press, Inc., New York, NY, 1978, pp. 2–6. 42.Z. Nishiyama: Martensitic Transformation, Academic Press, Inc., New York, NY, 1978, pp. 2–6.
Metadaten
Titel
Effect of Hydrogen on the Substructure of Lenticular Martensite in Fe-31Ni Alloy
verfasst von
Akinobu Shibata
Masanori Enoki
Nahoko Saji
Hirotaka Tai
Motomichi Koyama
Hiroshi Ohtani
Nobuhiro Tsuji
Kaneaki Tsuzaki
Publikationsdatum
26.06.2019
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions A / Ausgabe 9/2019
Print ISSN: 1073-5623
Elektronische ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-019-05320-y

Weitere Artikel der Ausgabe 9/2019

Metallurgical and Materials Transactions A 9/2019 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.