Effect of Ladle Changeover Condition on Transient Three-Phase Flow in a Five-Strand Bloom Casting Tundish

verfasst von: Hua Zhang, Qing Fang, Ronghua Luo, Chao Liu, Yi Wang, Hongwei Ni

Erschienen in: Metallurgical and Materials Transactions B | Ausgabe 3/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The transient three-phase flow behavior in a five-strand bloom casting tundish during the ladle changeover process considering a constant casting speed was investigated by the VOF model, and the effect of ladle throughput rate, shroud immersion depth, turbulence inhibitor structure and ladle changeover time on the turbulent flow, and level fluctuations during the filling process were analyzed to optimize the flow pattern in the tundish during ladle changeover. The results showed that the exposed area of molten steel in the impact zone increases as the ladle throughput rate increases during the filling process and that the exposure of molten steel is eliminated when the ladle throughput rate is 1.5Qsteady. As the immersion depth of the shroud increases, a slight decrease in slag entrainment happens, while the exposed area of molten steel first decreases and then increases. The shroud immersion depth should be 310 mm. When the optimized turbulence inhibitor is used, the wave crests of the steel level are greatly reduced, the height of the level fluctuation is alleviated with the maximum value decreasing from 33 mm to approximately 10 mm, and the exposure of molten steel is eliminated. When the ladle changeover time is between 2 and 3 minutes, the exposed area of molten steel during the stable period of the filling process is in the range from 150 to 170 cm2, which is substantially less than the exposed area of 500 cm2 when the ladle changeover time is 4 minutes. Therefore, the ladle changeover time should be controlled within 3 minutes. The flaw detection disqualification rate caused by ladle changeover operation is decreased from 43.8 to 25.8 pct of the total disqualified steel rails after optimization.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat K. Chattopadhyay, M. Isac and R.I.L. Guthrie: ISIJ Int., 2010, vol. 50, pp. 331-348.CrossRef K. Chattopadhyay, M. Isac and R.I.L. Guthrie: ISIJ Int., 2010, vol. 50, pp. 331-348.CrossRef
2.
3.
Zurück zum Zitat S. Chatterjee, D. Li and K Chattopadhyay: Metall. Mater. Trans. B, 2018, vol. 49B, pp. 756-766.CrossRef S. Chatterjee, D. Li and K Chattopadhyay: Metall. Mater. Trans. B, 2018, vol. 49B, pp. 756-766.CrossRef
4.
Zurück zum Zitat A. Vakhrushev, M. Wu, A. Ludwig, G. Nitzl, Y. Tang, G. Hackl and R. Wincor: Steel Res. Int., 2017, vol. 88, 1600276.CrossRef A. Vakhrushev, M. Wu, A. Ludwig, G. Nitzl, Y. Tang, G. Hackl and R. Wincor: Steel Res. Int., 2017, vol. 88, 1600276.CrossRef
5.
6.
Zurück zum Zitat J. Zhang, S. Yang, M. Li, Z. Chen, Z. Jiang and J. Li: Ironmak. Steelmak., 2017, vol. 44, pp. 732-738.CrossRef J. Zhang, S. Yang, M. Li, Z. Chen, Z. Jiang and J. Li: Ironmak. Steelmak., 2017, vol. 44, pp. 732-738.CrossRef
7.
Zurück zum Zitat R. Bölling, H. Odenthal and H. Pfeifer: Steel Res. Int., 2005, vol. 76, pp. 71-80.CrossRef R. Bölling, H. Odenthal and H. Pfeifer: Steel Res. Int., 2005, vol. 76, pp. 71-80.CrossRef
8.
Zurück zum Zitat J.M.F. Oro, C.S. Morros, J.R. Somoano, and M.A. Ordieres: ASME fluids Engineering Division Summer Meeting, 2009, pp. 2183–94. J.M.F. Oro, C.S. Morros, J.R. Somoano, and M.A. Ordieres: ASME fluids Engineering Division Summer Meeting, 2009, pp. 2183–94.
9.
Zurück zum Zitat M.I.H. Siddiqui, P.K. Jha: Steel Res. Int., 2016, vol. 87, pp. 733-744.CrossRef M.I.H. Siddiqui, P.K. Jha: Steel Res. Int., 2016, vol. 87, pp. 733-744.CrossRef
10.
Zurück zum Zitat S. Kant, P.K. Jha and P. Kumar: Ironmak. Steelmak., 2011, vol. 38, pp. 391-397.CrossRef S. Kant, P.K. Jha and P. Kumar: Ironmak. Steelmak., 2011, vol. 38, pp. 391-397.CrossRef
11.
Zurück zum Zitat K. Takahashi, M. Ando and T. Ishii: ISIJ Int., 2014, vol. 54, pp. 304-310.CrossRef K. Takahashi, M. Ando and T. Ishii: ISIJ Int., 2014, vol. 54, pp. 304-310.CrossRef
12.
Zurück zum Zitat H. Ling, L. Zhang and H. Li: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2991-3012.CrossRef H. Ling, L. Zhang and H. Li: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2991-3012.CrossRef
13.
Zurück zum Zitat H. Ling, L. Zhang and H. Wang: Metall. Res. Technol., 2017, vol. 114, pp. 516.CrossRef H. Ling, L. Zhang and H. Wang: Metall. Res. Technol., 2017, vol. 114, pp. 516.CrossRef
15.
Zurück zum Zitat S. Garcia-Hernandez, R.D. Morales, D.J.B. Jose, I. Calderon-Ramos and E. Gutierrez: Steel Res. Int., 2016, vol. 87, pp. 1154-1167.CrossRef S. Garcia-Hernandez, R.D. Morales, D.J.B. Jose, I. Calderon-Ramos and E. Gutierrez: Steel Res. Int., 2016, vol. 87, pp. 1154-1167.CrossRef
16.
Zurück zum Zitat R.D. Morales, S. Garcia-Hernandez, J.D.J. Barreto, A. Ceballos-Huerta, I. Calderon-Ramos and E. Gutierrez: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2595-2606.CrossRef R.D. Morales, S. Garcia-Hernandez, J.D.J. Barreto, A. Ceballos-Huerta, I. Calderon-Ramos and E. Gutierrez: Metall. Mater. Trans. B, 2016, vol. 47B, pp. 2595-2606.CrossRef
17.
Zurück zum Zitat M. M. Machado-Lopez, J. A. Ramos-Banderas, E. Torres-Alonso, J. J. Barreto, S. Garcia-Hernandez: Ironmak. Steelmak., 2013, vol. 40, pp. 326-334.CrossRef M. M. Machado-Lopez, J. A. Ramos-Banderas, E. Torres-Alonso, J. J. Barreto, S. Garcia-Hernandez: Ironmak. Steelmak., 2013, vol. 40, pp. 326-334.CrossRef
18.
Zurück zum Zitat ANSYS Fluent 15.0 Theory Guide, Southpointe, 2013. ANSYS Fluent 15.0 Theory Guide, Southpointe, 2013.
Metadaten
Titel
Effect of Ladle Changeover Condition on Transient Three-Phase Flow in a Five-Strand Bloom Casting Tundish
verfasst von
Hua Zhang
Qing Fang
Ronghua Luo
Chao Liu
Yi Wang
Hongwei Ni
Publikationsdatum
12.04.2019
Verlag
Springer US
Erschienen in
Metallurgical and Materials Transactions B / Ausgabe 3/2019
Print ISSN: 1073-5615
Elektronische ISSN: 1543-1916
DOI
https://doi.org/10.1007/s11663-019-01572-6

Weitere Artikel der Ausgabe 3/2019

Metallurgical and Materials Transactions B 3/2019 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.