Effect of lithium doping on the photoluminescence of Sm:ZnO powders

ZnO co-doped with 2 at.% Sm and different Li concentration (0–7 at.%) powders were fabricated by the sol–gel method with 700 °C annealing. The effect of Li doping concentration on the structure and photoluminescence (PL) of ZnO powders doped with 2 at.% Sm was investigated. Based on the balance of structure and valence, with the help of Li doping (1, 2 at.%) into ZnO powders doped with 2 at.% Sm, Sm³⁺ ions enter ZnO crystal lattice and induce the characteristic Sm³⁺ emission peaks by the ultra-violet (UV) excitation (278 nm). Especially, when the Li doping concentration is 2 at.%, the sample has the most efficient Sm characteristic emission line. However, Li will hinder the substitution of zinc location by Sm³⁺ when the Li doping concentration is above 3 at.%, which results in the disappearance of the characteristic samarium emission lines.