Effect of Milling on the Magnetic Properties of the Fe7S8 and Fe7Se8 Compounds

verfasst von: D. F. Akramov, N. V. Selezneva, P. N. G. Ibrahim, V. V. Maikov, E. M. Sherokalova, D. K. Kuznetsov, N. V. Baranov

Erschienen in: Physics of Metals and Metallography | Ausgabe 3/2022

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstratct

—X-ray diffraction, scanning electron microscopy, and magnetic measurements are used to study the structure and magnetic properties of layered ferrimagnetic Fe7S8 and Fe7Se8 compounds depending on the milling time in a ball mill. The milling is shown to lead to the abrupt decrease in the coherent domain size, increase in microstresses, suppression of magnetization anomalies related to low-temperature phase transformations, substantial decrease in the resulting magnetization, and nonmonotonic change in the coercive force. The observed changes in the behavior of magnetization are discussed taking into account the possible redistribution of vacancies in the cation layer in the course of mechanical treatment.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat N. V. Baranov, E. G. Gerasimov, and N. V. Mushnikov, “Magnetism of compounds with a layered crystal structure,” Phys. Met. Metallogr. 112, 711–744 (2011). N. V. Baranov, E. G. Gerasimov, and N. V. Mushnikov, “Magnetism of compounds with a layered crystal structure,” Phys. Met. Metallogr. 112, 711–744 (2011).
2.
Zurück zum Zitat N. V. Baranov, N. V. Selezneva, and V. A. Kazantsev, “Magnetism and superconductivity of transition metal chalcogenides,” Phys. Met. Metallogr. 119, 1301–1304 (2018). CrossRef N. V. Baranov, N. V. Selezneva, and V. A. Kazantsev, “Magnetism and superconductivity of transition metal chalcogenides,” Phys. Met. Metallogr. 119, 1301–1304 (2018). CrossRef
3.
Zurück zum Zitat E. Morosan, H. W. Zandbergen, Li. Lu, Lee. Minhyea, J. G. Checkelsky, M. Heinrich, T. Siegrist, N. P. Ong, and R. J. Cava, “Sharp switching of the magnetization in Fe 1/4TaS 2,” Phys. Rev. B 75, 104401 (2009). CrossRef E. Morosan, H. W. Zandbergen, Li. Lu, Lee. Minhyea, J. G. Checkelsky, M. Heinrich, T. Siegrist, N. P. Ong, and R. J. Cava, “Sharp switching of the magnetization in Fe 1/4TaS 2,” Phys. Rev. B 75, 104401 (2009). CrossRef
4.
Zurück zum Zitat Y. J. Choi, S. B. Kim, T. Asada, S. Park, Wu. Weida, Y. Horibe, and S.-W. Cheong, “Giant magnetic coercivity and ionic superlattice nano-domains in Fe 0.25TaS 2,” Europhys. Lett. 86, 37012 (2009). CrossRef Y. J. Choi, S. B. Kim, T. Asada, S. Park, Wu. Weida, Y. Horibe, and S.-W. Cheong, “Giant magnetic coercivity and ionic superlattice nano-domains in Fe 0.25TaS 2,” Europhys. Lett. 86, 37012 (2009). CrossRef
5.
Zurück zum Zitat C.-W. Chen, S. Chikara, V. S. Zapf, and E. Morosan, “Correlations of crystallographic defects and anisotropy with magnetotransport properties in Fe xTaS 2 single crystals (0.23 < x < 0.35),” Phys. Rev. B 94, No. 5, 054406 (2016). CrossRef C.-W. Chen, S. Chikara, V. S. Zapf, and E. Morosan, “Correlations of crystallographic defects and anisotropy with magnetotransport properties in Fe xTaS 2 single crystals (0.23 < x < 0.35),” Phys. Rev. B 94, No. 5, 054406 (2016). CrossRef
6.
Zurück zum Zitat H. Negishi, A. Shoube, H. Takahashi, Y. Ueda, M. Sasaki, and M. Inoue, “Magnetic properties of intercalation compounds M xTiS 2 (M = 3 d transition metal),” J. Magn. Magn. Mater. 67, 179–186 (1987). CrossRef H. Negishi, A. Shoube, H. Takahashi, Y. Ueda, M. Sasaki, and M. Inoue, “Magnetic properties of intercalation compounds M xTiS 2 (M = 3 d transition metal),” J. Magn. Magn. Mater. 67, 179–186 (1987). CrossRef
7.
Zurück zum Zitat N. V. Baranov, E. M. Sherokalova, N. V. Selezneva, A. V. Proshkin, A. F. Gubkin, L. Keller, A. S. Volegov, and E. P. Proskurina, “Magnetic order, field-induced phase transitions and magnetoresistance in the intercalated compound Fe 0.5TiS 2,” J. Phys.: Condens. Matter 25, 066004 (2013). N. V. Baranov, E. M. Sherokalova, N. V. Selezneva, A. V. Proshkin, A. F. Gubkin, L. Keller, A. S. Volegov, and E. P. Proskurina, “Magnetic order, field-induced phase transitions and magnetoresistance in the intercalated compound Fe 0.5TiS 2,” J. Phys.: Condens. Matter 25, 066004 (2013).
8.
Zurück zum Zitat N. V. Baranov, N. V. Selezneva, E. M. Sherokalova, Y. A. Baglaeva, A. S. Ovchinnikov, A. A. Tereshcheno, D. I. Gorbunov, and A. S. Volegov, “ Magnetic phase transitions, metastable states, and magnetic hysteresis in the antiferromagnetic compounds Fe 0.5TiS 2 – ySe y,” Phys. Rev. B 100, 024430 (2019). CrossRef N. V. Baranov, N. V. Selezneva, E. M. Sherokalova, Y. A. Baglaeva, A. S. Ovchinnikov, A. A. Tereshcheno, D. I. Gorbunov, and A. S. Volegov, “ Magnetic phase transitions, metastable states, and magnetic hysteresis in the antiferromagnetic compounds Fe 0.5TiS 2 – ySe y,” Phys. Rev. B 100, 024430 (2019). CrossRef
9.
Zurück zum Zitat N. V. Selezneva, E. M. Sherokalova, A. S. Volegov, D. A. Shishkin, and N. V. Baranov, “Crystal structure, magnetic state and electrical resistivity of Fe 2/3Ti(S,Se) 2 as affected by anionic substitutions,” Mater. Res. Exp. 4, 106102 (2017). CrossRef N. V. Selezneva, E. M. Sherokalova, A. S. Volegov, D. A. Shishkin, and N. V. Baranov, “Crystal structure, magnetic state and electrical resistivity of Fe 2/3Ti(S,Se) 2 as affected by anionic substitutions,” Mater. Res. Exp. 4, 106102 (2017). CrossRef
10.
Zurück zum Zitat N. V. Selezneva, N. V. Baranov, E. M. Sherokalova, A. S. Volegov, and A. A. Sherstobitov, “Multiple magnetic states and irreversibilities in the Fe xTiS 2 system,” Phys. Rev. B 104, 064411 (2021). CrossRef N. V. Selezneva, N. V. Baranov, E. M. Sherokalova, A. S. Volegov, and A. A. Sherstobitov, “Multiple magnetic states and irreversibilities in the Fe xTiS 2 system,” Phys. Rev. B 104, 064411 (2021). CrossRef
11.
Zurück zum Zitat N. V. Selezneva, N. V. Baranov, E. M. Sherokalova, A. S. Volegov, and A. A. Sherstobitov, “Remnant magnetoresistance and virgin magnetic state in Fe 0.25TiS 2,” J. Magn. Magn. Mater. 519, 167480 (2021). CrossRef N. V. Selezneva, N. V. Baranov, E. M. Sherokalova, A. S. Volegov, and A. A. Sherstobitov, “Remnant magnetoresistance and virgin magnetic state in Fe 0.25TiS 2,” J. Magn. Magn. Mater. 519, 167480 (2021). CrossRef
12.
Zurück zum Zitat H. Wang and I. Salveson, “A review on the mineral chemistry of the non-stoichiometric iron sulfide, Fe 1 ‒ xS (0 ≤ x ≤ 0.125): Polymorphs, phase relations and transitions, electronic and magnetic structures,” Phase Transitions 78, 547–567 (2005). CrossRef H. Wang and I. Salveson, “A review on the mineral chemistry of the non-stoichiometric iron sulfide, Fe 1 ‒ xS (0 ≤ x ≤ 0.125): Polymorphs, phase relations and transitions, electronic and magnetic structures,” Phase Transitions 78, 547–567 (2005). CrossRef
13.
Zurück zum Zitat M. S. Bishwas, R. Das, and P. Poddar, “Large increase in the energy product of Fe 3Se 4 by Fe-site doping,” J. Phys. Chem. C 118, 4016–4022 (2014). CrossRef M. S. Bishwas, R. Das, and P. Poddar, “Large increase in the energy product of Fe 3Se 4 by Fe-site doping,” J. Phys. Chem. C 118, 4016–4022 (2014). CrossRef
14.
Zurück zum Zitat I. Radelytskyi, P. Aleshkevych, D. J. Gawryluk, M. Berkowski, T. Zajarniuk, A. Szewczyk, M. Gutowska, L. Hawelek, P. Wlodarczyk, J. Fink-Finowicki, R. Minikayev, R. Diduszko, Y. Konopelnyk, M. Kozłowski, R. Puz’niak, and H. Szymczak, “Structural, magnetic, and magnetocaloric properties of Fe 7Se 8 single crystals,” J. Appl. Phys. 124, 143902 (2018). CrossRef I. Radelytskyi, P. Aleshkevych, D. J. Gawryluk, M. Berkowski, T. Zajarniuk, A. Szewczyk, M. Gutowska, L. Hawelek, P. Wlodarczyk, J. Fink-Finowicki, R. Minikayev, R. Diduszko, Y. Konopelnyk, M. Kozłowski, R. Puz’niak, and H. Szymczak, “Structural, magnetic, and magnetocaloric properties of Fe 7Se 8 single crystals,” J. Appl. Phys. 124, 143902 (2018). CrossRef
15.
Zurück zum Zitat I. Letard, P. Sainctavit, and C. Deudon, “XMCD at Fe L 2, 3 edges, Fe and S K edges on Fe 7S 8,” Phys. Chem. Miner. 34, 113–120 (2007). CrossRef I. Letard, P. Sainctavit, and C. Deudon, “XMCD at Fe L 2, 3 edges, Fe and S K edges on Fe 7S 8,” Phys. Chem. Miner. 34, 113–120 (2007). CrossRef
16.
Zurück zum Zitat A. V. Powell, P. Vaqueiro, K. S. Knight, L. C. Chapon, and R. D. Sánchez, “Structure and magnetism in synthetic pyrrhotite Fe 7S 8: A powder neutron-diffraction study,” Phys. Rev. B 70, 014415 (2004). CrossRef A. V. Powell, P. Vaqueiro, K. S. Knight, L. C. Chapon, and R. D. Sánchez, “Structure and magnetism in synthetic pyrrhotite Fe 7S 8: A powder neutron-diffraction study,” Phys. Rev. B 70, 014415 (2004). CrossRef
17.
Zurück zum Zitat A. F. Andresen and J. Leciejewicz, “A neutron diffraction study of Fe 7Se 8,” J. Phys. (Paris) 25, 574–578 (1964). CrossRef A. F. Andresen and J. Leciejewicz, “A neutron diffraction study of Fe 7Se 8,” J. Phys. (Paris) 25, 574–578 (1964). CrossRef
18.
Zurück zum Zitat D. Koulialias, B. Lesniak, M. Schwotzer, P. G. Weidler, J. F. Löffler, and A. U. Gehring, “The Besnus transition in single-domain 4C pyrrhotite,” Geochem., Geophys., Geosyst. 20, No. 11, 5216–5224 (2019). CrossRef D. Koulialias, B. Lesniak, M. Schwotzer, P. G. Weidler, J. F. Löffler, and A. U. Gehring, “The Besnus transition in single-domain 4C pyrrhotite,” Geochem., Geophys., Geosyst. 20, No. 11, 5216–5224 (2019). CrossRef
19.
Zurück zum Zitat C. R. S. Haines, S. E. Dutton, M. W. R. Volk, and M. A. Carpenter, “Magnetoelastic properties and behaviour of 4C pyrrhotite, Fe 7S 8, through the Besnus transition,” J. Phys.: Condens. Matter 32, 405401 (2020). C. R. S. Haines, S. E. Dutton, M. W. R. Volk, and M. A. Carpenter, “Magnetoelastic properties and behaviour of 4C pyrrhotite, Fe 7S 8, through the Besnus transition,” J. Phys.: Condens. Matter 32, 405401 (2020).
20.
Zurück zum Zitat D. Koulialias, E. Canevet, M. Charilaou, P. G. Weidler, J. F. Loffler, and A. U. Gehring, “The relation between local structural distortion and the low-temperature magnetic anomaly in Fe 7S 8,” J. Phys.: Condens. Matter 30, 425803 (2018). D. Koulialias, E. Canevet, M. Charilaou, P. G. Weidler, J. F. Loffler, and A. U. Gehring, “The relation between local structural distortion and the low-temperature magnetic anomaly in Fe 7S 8,” J. Phys.: Condens. Matter 30, 425803 (2018).
21.
Zurück zum Zitat T. Kamimura, “On the Spin Axis Transition in Fe 7Se 8 (3c),” J. Phys. Soc. Jpn. 43, 1594–1599 (1977). CrossRef T. Kamimura, “On the Spin Axis Transition in Fe 7Se 8 (3c),” J. Phys. Soc. Jpn. 43, 1594–1599 (1977). CrossRef
22.
Zurück zum Zitat Y. Konopelnyk, I. Radelytskyi, P. Iwanowski, D. J. Gawryluk, M. Berkowski, R. Diduszko, J. Fink-Finowicki, H. Szymczak, and R. Puzniak, “Combined pressure and magnetic-field induced caloric effects in Fe 7Se 8 single crystals,” J. Magn. Magn. 543, 168626 (2021). CrossRef Y. Konopelnyk, I. Radelytskyi, P. Iwanowski, D. J. Gawryluk, M. Berkowski, R. Diduszko, J. Fink-Finowicki, H. Szymczak, and R. Puzniak, “Combined pressure and magnetic-field induced caloric effects in Fe 7Se 8 single crystals,” J. Magn. Magn. 543, 168626 (2021). CrossRef
23.
Zurück zum Zitat H. Zhang, G. Long, D. Li, R. Sabirianov, and H. Zeng, “Fe 3Se 4 nanostructures with giant coercivity synthesized by solution chemistry,” Chem. Mater. 23, 3769–3774 (2011). CrossRef H. Zhang, G. Long, D. Li, R. Sabirianov, and H. Zeng, “Fe 3Se 4 nanostructures with giant coercivity synthesized by solution chemistry,” Chem. Mater. 23, 3769–3774 (2011). CrossRef
24.
Zurück zum Zitat G. Long, H. Zhang, D. Li, R. Sabirianov, Z. Zhang, and H. Zeng, “Magnetic anisotropy and coercivity of Fe 3Se 4 nanostructures,” Appl. Phys. Lett. 99, 202103 (2011). CrossRef G. Long, H. Zhang, D. Li, R. Sabirianov, Z. Zhang, and H. Zeng, “Magnetic anisotropy and coercivity of Fe 3Se 4 nanostructures,” Appl. Phys. Lett. 99, 202103 (2011). CrossRef
25.
Zurück zum Zitat D. A. Clark, “Hysteresis properties of sized dispersed monoclinic pyrrhotite grains,” Geophys. Res. Lett. 11, No. 3, 173–176 (1984). CrossRef D. A. Clark, “Hysteresis properties of sized dispersed monoclinic pyrrhotite grains,” Geophys. Res. Lett. 11, No. 3, 173–176 (1984). CrossRef
26.
Zurück zum Zitat W. O’Reilly, V. Hoffmann, A. C. Chouker, H. C. Soffel, and A. Menyeh, “Magnetic properties of synthetic analogues of pyrrhotite ore in the grain size range 1–24 μm,” Geophys. J. Int. 142, 669–683 (2000). CrossRef W. O’Reilly, V. Hoffmann, A. C. Chouker, H. C. Soffel, and A. Menyeh, “Magnetic properties of synthetic analogues of pyrrhotite ore in the grain size range 1–24 μm,” Geophys. J. Int. 142, 669–683 (2000). CrossRef
27.
Zurück zum Zitat A. Menyeh and W. O’Reily, “The coercive force of fine particles of monoclinic pyrrhotite (Fe 7S 8) studied at elevated temperature,” Phys. Earth Planet. Inter. 89, 51–62 (1995). CrossRef A. Menyeh and W. O’Reily, “The coercive force of fine particles of monoclinic pyrrhotite (Fe 7S 8) studied at elevated temperature,” Phys. Earth Planet. Inter. 89, 51–62 (1995). CrossRef
28.
Zurück zum Zitat S. B. Harris and R. P. Camata, “X-ray diffraction data and analysis to support phase identification in FeSe and Fe 7Se 8 epitaxial thin films,” J. Cryst. Growth 27, 104778 (2019). S. B. Harris and R. P. Camata, “X-ray diffraction data and analysis to support phase identification in FeSe and Fe 7Se 8 epitaxial thin films,” J. Cryst. Growth 27, 104778 (2019).
29.
Zurück zum Zitat G. K. Williamson and W. H. Hall, “X-Ray line broadening from filed aluminium and wolfram,” Acta Metall. 1, 22–31 (1953). CrossRef G. K. Williamson and W. H. Hall, “X-Ray line broadening from filed aluminium and wolfram,” Acta Metall. 1, 22–31 (1953). CrossRef
30.
Zurück zum Zitat M. J. Dekkers, “Grain-size dependence of the magnetic behavior of pyrrhotite during its low-temperature transition at 34 K,” Geophys. Res. Lett. 16, 855–858 (2014). CrossRef M. J. Dekkers, “Grain-size dependence of the magnetic behavior of pyrrhotite during its low-temperature transition at 34 K,” Geophys. Res. Lett. 16, 855–858 (2014). CrossRef
31.
Zurück zum Zitat I. S. Lyubutin, C. R. Lin, K. O. Funtov, T. V. Dmitrieva, S. S. Starchikov, Y. J. Siao, and M. L. Chen, “Structural, magnetic, and electronic properties of iron selenide Fe6-7Se8 nanoparticles obtained by thermal decomposition in high-temperature organic solvents,” J. Chem. Phys. 141, 044704 (2014). CrossRef I. S. Lyubutin, C. R. Lin, K. O. Funtov, T. V. Dmitrieva, S. S. Starchikov, Y. J. Siao, and M. L. Chen, “Structural, magnetic, and electronic properties of iron selenide Fe6-7Se8 nanoparticles obtained by thermal decomposition in high-temperature organic solvents,” J. Chem. Phys. 141, 044704 (2014). CrossRef
Metadaten
Titel
Effect of Milling on the Magnetic Properties of the Fe7S8 and Fe7Se8 Compounds
verfasst von
D. F. Akramov
N. V. Selezneva
P. N. G. Ibrahim
V. V. Maikov
E. M. Sherokalova
D. K. Kuznetsov
N. V. Baranov
Publikationsdatum
01.03.2022
Verlag
Pleiades Publishing
Erschienen in
Physics of Metals and Metallography / Ausgabe 3/2022
Print ISSN: 0031-918X
Elektronische ISSN: 1555-6190
DOI
https://doi.org/10.1134/S0031918X22030024

Weitere Artikel der Ausgabe 3/2022

Physics of Metals and Metallography 3/2022 Zur Ausgabe