Erschienen in: Journal of Materials Engineering and Performance 12/2013

01.12.2013

Effect of Oxide Buffer Layer on the Thermochromic Properties of VO2 Thin Films

verfasst von: Hyun Koo, Lu Xu, Kyeong-Eun Ko, Seunghyun Ahn, Se-Hong Chang, Chan Park

Erschienen in: Journal of Materials Engineering and Performance | Ausgabe 12/2013

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

VO2 thin films were deposited on soda lime glass substrates with ZnO, TiO2, SnO2, and CeO2 thin films applied as buffer layers between the VO2 films and the substrates in order to investigate the effect of buffer layer on the formation and the thermochromic properties of VO2 film. Buffer layers with thicknesses over 50 nm were found to affect the formation of VO2 film, which was confirmed by XRD spectra. By using ZnO, TiO2, and SnO2 buffer layers, monoclinic VO2 (VO2(M)) film was successfully fabricated on soda lime glass at 370 °C. On the contrary, films of VO2(B), which is known to have no phase transition near room temperature, were formed rather than VO2(M) when the film was deposited on CeO2 buffer layer at the same film deposition temperature. The excellent thermochromic properties of the films deposited on ZnO, TiO2, and SnO2 buffer layers were confirmed from the temperature dependence of electrical resistivity from room temperature to 80 °C. Especially, due to the tendency of ZnO thin film to grow with a high degree of preferred orientation on soda lime glass at low temperature, the VO2 film deposited on ZnO buffer layer exhibits the best thermochromic properties compared to those on other buffer layer materials used in this study. These results suggest that deposition of VO2 films on soda lime glass at low temperature with excellent thermochromic properties can be achieved by considering the buffer layer material having structural similarity with VO2. Moreover, the degree of crystallization of buffer layer is also related with that of VO2 film, and thus ZnO can be one of the most effective buffer layer materials.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat B. O’Regan and M. Grätzel, A Low-Cost, High-Efficiency Solar Cell Based on Dye-Sensitized Colloidal TiO2 Films, Nature, 1991, 353, p 737CrossRef B. O’Regan and M. Grätzel, A Low-Cost, High-Efficiency Solar Cell Based on Dye-Sensitized Colloidal TiO2 Films, Nature, 1991, 353, p 737CrossRef
2.
Zurück zum Zitat O.J. Kwon, W. Jo, S. Yoon, D. Shin, H. You, K. Choi, J.S. Kim, and C. Park, Relation Between Seebeck Coefficient and Lattice Parameters of (Ca2y Sr y CoO3) x CoO2, J. Electron. Mater., 2012, 41, p 1513–1518CrossRef O.J. Kwon, W. Jo, S. Yoon, D. Shin, H. You, K. Choi, J.S. Kim, and C. Park, Relation Between Seebeck Coefficient and Lattice Parameters of (Ca2y Sr y CoO3) x CoO2, J. Electron. Mater., 2012, 41, p 1513–1518CrossRef
3.
Zurück zum Zitat H.W. Heuer, R. Wehrmann, and S. Kirchmeyer, Electrochromic Window Based on Conducting Poly(3,4-ethylenedioxythiophene) ± Poly(Styrene Sulfonate), Adv. Funct. Mater., 2002, 12, p 89–94CrossRef H.W. Heuer, R. Wehrmann, and S. Kirchmeyer, Electrochromic Window Based on Conducting Poly(3,4-ethylenedioxythiophene) ± Poly(Styrene Sulfonate), Adv. Funct. Mater., 2002, 12, p 89–94CrossRef
4.
Zurück zum Zitat K.I. Jensen, J.M. Schultz, and F.H. Kristiansen, Development of Windows Based on Highly Insulating Aerogel Glazings, J. Non Cryst. Sol., 2004, 350, p 351–357CrossRef K.I. Jensen, J.M. Schultz, and F.H. Kristiansen, Development of Windows Based on Highly Insulating Aerogel Glazings, J. Non Cryst. Sol., 2004, 350, p 351–357CrossRef
5.
Zurück zum Zitat J. Wu, X. Wei, N.P. Padture, P.G. Klemens, M. Gell, E. Garcia, P. Miranzo, and M.I. Osendi, Low-Thermal-Conductivity Rare-Earth Zirconates for Potential Thermal-Barrier-Coating Applications, J. Am. Ceram. Soc., 2002, 85, p 3031–3035CrossRef J. Wu, X. Wei, N.P. Padture, P.G. Klemens, M. Gell, E. Garcia, P. Miranzo, and M.I. Osendi, Low-Thermal-Conductivity Rare-Earth Zirconates for Potential Thermal-Barrier-Coating Applications, J. Am. Ceram. Soc., 2002, 85, p 3031–3035CrossRef
6.
Zurück zum Zitat F.J. Morin, Oxides Which Show a Metal-to-Insulator Transition at the Neel Temperature, Phys. Rev. Lett., 1959, 3, p 34CrossRef F.J. Morin, Oxides Which Show a Metal-to-Insulator Transition at the Neel Temperature, Phys. Rev. Lett., 1959, 3, p 34CrossRef
7.
Zurück zum Zitat J.B. Goodenough, The Two Components of the Crystallographic Transition in VO2, J. Solid State Chem., 1971, 3, p 490CrossRef J.B. Goodenough, The Two Components of the Crystallographic Transition in VO2, J. Solid State Chem., 1971, 3, p 490CrossRef
8.
Zurück zum Zitat C.H. Griffiths and H.K. Eastwood, Influence of Stoichiometry on the Metal-Semiconductor Transition in Vanadium dioxide, J. Appl. Phys., 1974, 45, p 2201CrossRef C.H. Griffiths and H.K. Eastwood, Influence of Stoichiometry on the Metal-Semiconductor Transition in Vanadium dioxide, J. Appl. Phys., 1974, 45, p 2201CrossRef
9.
Zurück zum Zitat E.E. Chain, The Influence of Deposition Temperature on the Structure and Optical Properties of Vanadium Oxide Films, J. Vac. Sci. Technol., 1986, A4, p 432 E.E. Chain, The Influence of Deposition Temperature on the Structure and Optical Properties of Vanadium Oxide Films, J. Vac. Sci. Technol., 1986, A4, p 432
10.
Zurück zum Zitat A. Razavi, L. Bobyak, and P. Fallon, The Effects of Biasing and Annealing on the Optical Properties of Radio-Frequency Sputtered VO2, J. Vac. Sci. Technol., 1990, A8, p 1391 A. Razavi, L. Bobyak, and P. Fallon, The Effects of Biasing and Annealing on the Optical Properties of Radio-Frequency Sputtered VO2, J. Vac. Sci. Technol., 1990, A8, p 1391
11.
Zurück zum Zitat M. Fukuma, S. Zembutsu, and S. Miyazawa, Preparation of VO2 Thin Film and Its Direct Optical Bit Recording Characteristics, Appl. Opt., 1983, 22, p 265CrossRef M. Fukuma, S. Zembutsu, and S. Miyazawa, Preparation of VO2 Thin Film and Its Direct Optical Bit Recording Characteristics, Appl. Opt., 1983, 22, p 265CrossRef
12.
Zurück zum Zitat I.P. Parkin and T.D. Manning, Intelligent Thermochromic Windows, J. Chem. Educ., 2006, 83, p 3 I.P. Parkin and T.D. Manning, Intelligent Thermochromic Windows, J. Chem. Educ., 2006, 83, p 3
13.
Zurück zum Zitat C. Tang, P. Georgopoulos, M.E. Fine, J.B. Cohen, M. Nygren, G.S. Knapp, and A. Aldred, Local Atomic and Electronic Arrangements in W x V1−x O2, Phys. Rev. B, 1985, 31, p 1000CrossRef C. Tang, P. Georgopoulos, M.E. Fine, J.B. Cohen, M. Nygren, G.S. Knapp, and A. Aldred, Local Atomic and Electronic Arrangements in W x V1−x O2, Phys. Rev. B, 1985, 31, p 1000CrossRef
14.
Zurück zum Zitat H. Koo, S. Yoon, O.J. Kwon, K.E. Ko, D. Shin, S.H. Bae, S.H. Chang, and C. Park, Effect of Lattice Misfit on the Transition Temperature of VO2 Thin Film, J. Mater. Sci., 2012, 47, p 6397CrossRef H. Koo, S. Yoon, O.J. Kwon, K.E. Ko, D. Shin, S.H. Bae, S.H. Chang, and C. Park, Effect of Lattice Misfit on the Transition Temperature of VO2 Thin Film, J. Mater. Sci., 2012, 47, p 6397CrossRef
15.
Zurück zum Zitat L. Dai, C. Cao, Y.-F. Gao, and H.J. Luo, Synthesis and Phase Transition Behavior of Undoped VO2 with a Strong Nano-Size Effect, Sol. Energy Mater. Sol. Cells, 2011, 95, p 712–715CrossRef L. Dai, C. Cao, Y.-F. Gao, and H.J. Luo, Synthesis and Phase Transition Behavior of Undoped VO2 with a Strong Nano-Size Effect, Sol. Energy Mater. Sol. Cells, 2011, 95, p 712–715CrossRef
16.
Zurück zum Zitat G. Xu et al., Optimization of Antireflection Coating for VO2-Based Energy Efficient Window, Sol. Energy Mater. Sol. Cells, 2004, 83, p 29–37CrossRef G. Xu et al., Optimization of Antireflection Coating for VO2-Based Energy Efficient Window, Sol. Energy Mater. Sol. Cells, 2004, 83, p 29–37CrossRef
17.
Zurück zum Zitat P. Jin et al., Design, Formation and Characterization of a Novel Multifunctional Window with VO2 and TiO2 Coatings, Appl. Phys., 2003, A77, p 455–459 P. Jin et al., Design, Formation and Characterization of a Novel Multifunctional Window with VO2 and TiO2 Coatings, Appl. Phys., 2003, A77, p 455–459
18.
Zurück zum Zitat G. Xu, P. Jin, M. Tazawa, and K. Yoshimura, Thickness Dependence of Optical Properties of VO2 Thin Films Epitaxially Grown on Sapphire (0001), Appl. Surf. Sci., 2005, 244, p 449CrossRef G. Xu, P. Jin, M. Tazawa, and K. Yoshimura, Thickness Dependence of Optical Properties of VO2 Thin Films Epitaxially Grown on Sapphire (0001), Appl. Surf. Sci., 2005, 244, p 449CrossRef
19.
Zurück zum Zitat L. Kang, Y.-F. Gao, Z. Chen, J. Du, Z. Zhang, and H.J. Luo, Nanoporous Thermochromic VO2 Films with Low Optical Constants, Enhanced Luminous Transmittance and Thermochromic Properties, ACS Appl. Mater. Interfaces, 2011, 3, p 135–138CrossRef L. Kang, Y.-F. Gao, Z. Chen, J. Du, Z. Zhang, and H.J. Luo, Nanoporous Thermochromic VO2 Films with Low Optical Constants, Enhanced Luminous Transmittance and Thermochromic Properties, ACS Appl. Mater. Interfaces, 2011, 3, p 135–138CrossRef
20.
Zurück zum Zitat J. Du, Y.-F. Gao, H.J. Luo, Z. Zhang, L. Kang, and Z. Chen, The Formation and Metal-to-Insulator-Transition Properties of VO2-ZrV2O7 Composite Films by Polymer-Assisted Deposition, Sol. Energy Mater. Sol. Cells, 2011, 95, p 1604–1609CrossRef J. Du, Y.-F. Gao, H.J. Luo, Z. Zhang, L. Kang, and Z. Chen, The Formation and Metal-to-Insulator-Transition Properties of VO2-ZrV2O7 Composite Films by Polymer-Assisted Deposition, Sol. Energy Mater. Sol. Cells, 2011, 95, p 1604–1609CrossRef
21.
Zurück zum Zitat Z. Zhang, Y.-F. Gao, Z. Chen, J. Du, C. Cao, L.-T. Kang, and H.J. Luo, Thermochromic VO2 Thin Films: Solution-Based Processing, Improved Optical Properties and Lowered Phase Transformation Temperature, Langmuir, 2010, 26, p 10738–10744CrossRef Z. Zhang, Y.-F. Gao, Z. Chen, J. Du, C. Cao, L.-T. Kang, and H.J. Luo, Thermochromic VO2 Thin Films: Solution-Based Processing, Improved Optical Properties and Lowered Phase Transformation Temperature, Langmuir, 2010, 26, p 10738–10744CrossRef
22.
Zurück zum Zitat L.-T. Kang, Y.-F. Gao, and H.-J. Luo, A Novel Solution Process for the Synthesis of VO2 Thin Films with Excellent Thermochromic Properties, ACS Appl. Mater. Interfaces, 2009, 1, p 2211–2218CrossRef L.-T. Kang, Y.-F. Gao, and H.-J. Luo, A Novel Solution Process for the Synthesis of VO2 Thin Films with Excellent Thermochromic Properties, ACS Appl. Mater. Interfaces, 2009, 1, p 2211–2218CrossRef
23.
Zurück zum Zitat Y.-F. Gao, S. Wang, H. Luo, L. Dai, C. Cao, Y. Liu, Z. Chen, and M. Kanehira, Enhanced Chemical Stability of VO2 Nanoparticles by the Formation of SiO2/VO2 Core/Shell Structures and the Application to Transparent and Flexible VO2-Based Composite Foils with Excellent Thermochromic Properties for Solar Heat Control, Energy Environ. Sci., 2012, 5, p 6104–6110CrossRef Y.-F. Gao, S. Wang, H. Luo, L. Dai, C. Cao, Y. Liu, Z. Chen, and M. Kanehira, Enhanced Chemical Stability of VO2 Nanoparticles by the Formation of SiO2/VO2 Core/Shell Structures and the Application to Transparent and Flexible VO2-Based Composite Foils with Excellent Thermochromic Properties for Solar Heat Control, Energy Environ. Sci., 2012, 5, p 6104–6110CrossRef
24.
Zurück zum Zitat Y.-F. Gao, S. Wang, L. Kang, Z. Chen, J. Du, X. Liu, H. Luo, and M. Kanehira, VO2-Sb:SnO2 Composite Thermochromic Smart Glass Foil, Energy Environ. Sci., 2012, 5, p 8234–8237CrossRef Y.-F. Gao, S. Wang, L. Kang, Z. Chen, J. Du, X. Liu, H. Luo, and M. Kanehira, VO2-Sb:SnO2 Composite Thermochromic Smart Glass Foil, Energy Environ. Sci., 2012, 5, p 8234–8237CrossRef
25.
Zurück zum Zitat Y.-F. Gao, H. Luo, Z. Zhang, L. Kang, Z. Chen, J. Du, M. Kanehira, and C. Cao, Nanoceramic VO2 Thermochromic Smart Glass: A Review on Progress in Solution Processing, Nano Energy, 2012, 1, p 221–246CrossRef Y.-F. Gao, H. Luo, Z. Zhang, L. Kang, Z. Chen, J. Du, M. Kanehira, and C. Cao, Nanoceramic VO2 Thermochromic Smart Glass: A Review on Progress in Solution Processing, Nano Energy, 2012, 1, p 221–246CrossRef
26.
Zurück zum Zitat Y.-F. Gao, X. Cao, L. Dai, H. Luo, M. Kanehira, Y. Ding, and Z.L. Wang, Phase and Shape Controlled VO2 Nanostructures by Antimony Doping, Energy Environ. Sci., 2012, 5, p 8708–8715CrossRef Y.-F. Gao, X. Cao, L. Dai, H. Luo, M. Kanehira, Y. Ding, and Z.L. Wang, Phase and Shape Controlled VO2 Nanostructures by Antimony Doping, Energy Environ. Sci., 2012, 5, p 8708–8715CrossRef
27.
Zurück zum Zitat G. Guzman, R. Morineau, and J. Livage, Synthesis of Vanadium dioxide Thin Films from Vanadium Alkoxides, Mater. Res. Bull., 1994, 29, p 509CrossRef G. Guzman, R. Morineau, and J. Livage, Synthesis of Vanadium dioxide Thin Films from Vanadium Alkoxides, Mater. Res. Bull., 1994, 29, p 509CrossRef
28.
Zurück zum Zitat J.V. Fitzgerald, Anelasticity of Glass: II, Internal Friction and Sodium Ion Diffusion in Tank Plate Glass, A Typical Soda-Lime-Silica Glass, J. Am. Ceram. Soc., 1951, 34, p 339–342CrossRef J.V. Fitzgerald, Anelasticity of Glass: II, Internal Friction and Sodium Ion Diffusion in Tank Plate Glass, A Typical Soda-Lime-Silica Glass, J. Am. Ceram. Soc., 1951, 34, p 339–342CrossRef
29.
Zurück zum Zitat H. Koo, H.W. You, K.E. Ko, O.J. Kwon, S.H. Chang, and C. Park, Thermochromic Properties of VO2 Thin Film on SiN x Buffered Glass Substrate, Appl. Surf. Sci., 2013, 277, p 237–241CrossRef H. Koo, H.W. You, K.E. Ko, O.J. Kwon, S.H. Chang, and C. Park, Thermochromic Properties of VO2 Thin Film on SiN x Buffered Glass Substrate, Appl. Surf. Sci., 2013, 277, p 237–241CrossRef
30.
Zurück zum Zitat K. Nagashima, T. Yanagida, H. Tanaka, and T. Kawai, Interface Effect on Metal-Insulator Transition of Strained Vanadium dioxide Ultrathin Films, J. Appl. Phys., 2007, 101, p 026103CrossRef K. Nagashima, T. Yanagida, H. Tanaka, and T. Kawai, Interface Effect on Metal-Insulator Transition of Strained Vanadium dioxide Ultrathin Films, J. Appl. Phys., 2007, 101, p 026103CrossRef
31.
Zurück zum Zitat Z. Zhang, Y.-F. Gao, H. Luo, L.-T. Kang, Z. Chen, J. Du, M. Kanehira, Y. Zhang, and Z.L. Wang, Solution-Based Fabrication of Vanadium dioxide on F:SnO2 Substrates with Largely Enhanced Thermochromism and Low-Emissivity for Energy-Saving Applications, Energy Environ. Sci., 2011, 4, p 4290–4297CrossRef Z. Zhang, Y.-F. Gao, H. Luo, L.-T. Kang, Z. Chen, J. Du, M. Kanehira, Y. Zhang, and Z.L. Wang, Solution-Based Fabrication of Vanadium dioxide on F:SnO2 Substrates with Largely Enhanced Thermochromism and Low-Emissivity for Energy-Saving Applications, Energy Environ. Sci., 2011, 4, p 4290–4297CrossRef
32.
Zurück zum Zitat L. Kang, Y. Gao, H. Luo, J. Wang, B. Zhu, Z. Zhang, J. Du, M. Kanehira, and Y. Zhang, Thermochromic Properties and Low Emissivity of ZnO:Al/VO2 Double-Layered Films with a Lowered Phase Transition Temperature, Sol. Energy Mater. Sol. Cells, 2011, 95, p 3189–3194CrossRef L. Kang, Y. Gao, H. Luo, J. Wang, B. Zhu, Z. Zhang, J. Du, M. Kanehira, and Y. Zhang, Thermochromic Properties and Low Emissivity of ZnO:Al/VO2 Double-Layered Films with a Lowered Phase Transition Temperature, Sol. Energy Mater. Sol. Cells, 2011, 95, p 3189–3194CrossRef
33.
Zurück zum Zitat L. Kang, Y.-F. Gao, Z. Chen, J. Du, Z. Zhang, and H.J. Luo, Pt/VO2 Double-Layered Films Combining Thermochromic Properties with Low Emissivity, Sol. Energy Mater. Sol. Cells, 2010, 94, p 2078–2084CrossRef L. Kang, Y.-F. Gao, Z. Chen, J. Du, Z. Zhang, and H.J. Luo, Pt/VO2 Double-Layered Films Combining Thermochromic Properties with Low Emissivity, Sol. Energy Mater. Sol. Cells, 2010, 94, p 2078–2084CrossRef
34.
Zurück zum Zitat Z. Chen, Y.-F. Gao, L. Kang, J. Du, Z. Zhang, H. Luo, H. Miao, and G. Tan, VO2-Based Double-Layered Films for Smart Windows: Optical Design, All-Solution Preparation and Improved Properties, Sol. Energy Mater. Sol. Cells, 2011, 95, p 2677–2684CrossRef Z. Chen, Y.-F. Gao, L. Kang, J. Du, Z. Zhang, H. Luo, H. Miao, and G. Tan, VO2-Based Double-Layered Films for Smart Windows: Optical Design, All-Solution Preparation and Improved Properties, Sol. Energy Mater. Sol. Cells, 2011, 95, p 2677–2684CrossRef
35.
Zurück zum Zitat H. Miyazaki and I. Yasui, Effect of Buffer Layer on VO x Film Fabrication by Reactive RF Sputtering, Appl. Surf. Sci., 2006, 252, p 8367–8370CrossRef H. Miyazaki and I. Yasui, Effect of Buffer Layer on VO x Film Fabrication by Reactive RF Sputtering, Appl. Surf. Sci., 2006, 252, p 8367–8370CrossRef
36.
Zurück zum Zitat J.J. Wu and S.C. Liu, Low-Temperature Growth of Well-Aligned ZnO Nanorods by Chemical Vapor Deposition, Adv. Mater., 2002, 14, p 215CrossRef J.J. Wu and S.C. Liu, Low-Temperature Growth of Well-Aligned ZnO Nanorods by Chemical Vapor Deposition, Adv. Mater., 2002, 14, p 215CrossRef
37.
Zurück zum Zitat K. Kato, P.K. Song, H. Odaka, and Y. Shigesato, Study on Thermochromic VO2 Films Grown on ZnO-Coated Glass Substrates for “Smart Windows”, Jpn. J. Appl. Phys., 2003, 42, p 6523–6531CrossRef K. Kato, P.K. Song, H. Odaka, and Y. Shigesato, Study on Thermochromic VO2 Films Grown on ZnO-Coated Glass Substrates for “Smart Windows”, Jpn. J. Appl. Phys., 2003, 42, p 6523–6531CrossRef
38.
Zurück zum Zitat C. Leroux, G. Nihoul, and G.V. Tendeloo, From VO2(B) to VO2(R): Theoretical Structures of VO2 Polymorphs and In Situ Electron Microscopy, Phys. Rev. B, 1998, 57, p 5111–5121CrossRef C. Leroux, G. Nihoul, and G.V. Tendeloo, From VO2(B) to VO2(R): Theoretical Structures of VO2 Polymorphs and In Situ Electron Microscopy, Phys. Rev. B, 1998, 57, p 5111–5121CrossRef
39.
Zurück zum Zitat P. Jin and S. Tanemura, Formation and Thermochromism of VO2 Films Deposited by RF Magnetron Sputtering at Low Substrate Temperature, Jpn. J. Appl. Phys., 1994, 33, p 1478–1483CrossRef P. Jin and S. Tanemura, Formation and Thermochromism of VO2 Films Deposited by RF Magnetron Sputtering at Low Substrate Temperature, Jpn. J. Appl. Phys., 1994, 33, p 1478–1483CrossRef
40.
Zurück zum Zitat D. Kucharczyk and T. Niklewski, Accurate x-ray Determination of the Lattice-Parameters and the Thermal-Expansion Coefficients of VO2 Near the Transition-Temperature, J. Appl. Cryst., 1979, 12, p 370–373CrossRef D. Kucharczyk and T. Niklewski, Accurate x-ray Determination of the Lattice-Parameters and the Thermal-Expansion Coefficients of VO2 Near the Transition-Temperature, J. Appl. Cryst., 1979, 12, p 370–373CrossRef
41.
Zurück zum Zitat J.F. De Natale, P.J. Hood, and A.B. Harker, Formation and Characterization of Grain-Oriented VO2 Thin Films, J. Appl. Phys., 1989, 66, p 5844–5850CrossRef J.F. De Natale, P.J. Hood, and A.B. Harker, Formation and Characterization of Grain-Oriented VO2 Thin Films, J. Appl. Phys., 1989, 66, p 5844–5850CrossRef
42.
Zurück zum Zitat J.B. Macchesney and H.J. Guggenheim, Growth and Electrical Properties of Vanadium dioxide Single Crystals Containing Selected Impurity Ions, J. Phys. Chem. Solids, 1969, 30, p 225CrossRef J.B. Macchesney and H.J. Guggenheim, Growth and Electrical Properties of Vanadium dioxide Single Crystals Containing Selected Impurity Ions, J. Phys. Chem. Solids, 1969, 30, p 225CrossRef
43.
Zurück zum Zitat J.Y. Suh, R. Lopez, L.C. Feldman, and R.F. Haglund, Jr., Semiconductor to Metal Phase Transition in the Nucleation and Growth of VO2 Nanoparticles and Thin Films, J. Appl. Phys., 2004, 96, p 1209–1213CrossRef J.Y. Suh, R. Lopez, L.C. Feldman, and R.F. Haglund, Jr., Semiconductor to Metal Phase Transition in the Nucleation and Growth of VO2 Nanoparticles and Thin Films, J. Appl. Phys., 2004, 96, p 1209–1213CrossRef
Metadaten
Titel
Effect of Oxide Buffer Layer on the Thermochromic Properties of VO2 Thin Films
verfasst von
Hyun Koo
Lu Xu
Kyeong-Eun Ko
Seunghyun Ahn
Se-Hong Chang
Chan Park
Publikationsdatum
01.12.2013
Verlag
Springer US
Erschienen in
Journal of Materials Engineering and Performance / Ausgabe 12/2013
Print ISSN: 1059-9495
Elektronische ISSN: 1544-1024
DOI
https://doi.org/10.1007/s11665-013-0696-7

Weitere Artikel der Ausgabe 12/2013

Journal of Materials Engineering and Performance 12/2013 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.