Effect of pH on the microstructure and luminescence of Eu3+-doped BiPO4 phosphors

verfasst von: Shu-qing Yan

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 6/2015

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

We focus on the effect of pH on the microstructure and luminescence of an Eu3+-doped BiPO4 phosphor, BiPO4:0.05Eu3+. X-ray diffraction and field-emission scanning microscopy (FESEM) results show that as-prepared BiPO4:0.05Eu3+ has a hexagonal rod with cones, and that its crystallinity decreases with increased pH. With increased pH, more OH ions exist and BiPO4 cannot completely precipitate, which leads to increased irregular morphology. Afterwards, intensities of emission spectra decrease. The best excitation wavelength is 395 nm. Emission spectra of BiPO4:0.05Eu3+ samples display bands associated with 5D0 → 7FJ electronic transition characteristics of Eu3+ ions at different positions. Intensities of emission spectra decrease with increased pH. These results reveal the possibility of using pH adjustment to improve the luminescence of BiPO4 phosphors for future research on device fabrication.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
2.
Zurück zum Zitat A. Wolfert, E.W.J.L. Oomen, G. Blasse, J. Solid State Chem. 59, 280 (1985)CrossRef A. Wolfert, E.W.J.L. Oomen, G. Blasse, J. Solid State Chem. 59, 280 (1985)CrossRef
3.
4.
5.
Zurück zum Zitat H. Shabir, B. Lal, M. Rafat, J. Sol-Gel Sci Tech. 53, 399–404 (2010)CrossRef H. Shabir, B. Lal, M. Rafat, J. Sol-Gel Sci Tech. 53, 399–404 (2010)CrossRef
6.
Zurück zum Zitat P. Zhang, Y. Wang, Y. Wen, D. Wang, Y. Tao, Opt. Mater. 33, 475–479 (2011)CrossRef P. Zhang, Y. Wang, Y. Wen, D. Wang, Y. Tao, Opt. Mater. 33, 475–479 (2011)CrossRef
7.
Zurück zum Zitat G. Phaomei, W.R. Singh, R.S. Ningthoujam, J. Lumin. 131, 1154–1171 (2011)CrossRef G. Phaomei, W.R. Singh, R.S. Ningthoujam, J. Lumin. 131, 1154–1171 (2011)CrossRef
8.
Zurück zum Zitat C. Cao, A. Xia, S. Liu, L. Tong, J. Mater. Sci. Mater. EL 24, 4901 (2013)CrossRef C. Cao, A. Xia, S. Liu, L. Tong, J. Mater. Sci. Mater. EL 24, 4901 (2013)CrossRef
9.
Zurück zum Zitat L. Miao, H. Zhang, Y. Zhu, Y. Yang et al., J. Mater. Sci: Mater. EL 23, 1887 (2012) L. Miao, H. Zhang, Y. Zhu, Y. Yang et al., J. Mater. Sci: Mater. EL 23, 1887 (2012)
10.
Zurück zum Zitat L.F. Koao, F.B. Dejene, R.E. Kroon, H.C. Swart, J. Lumin. 147, 85–89 (2014)CrossRef L.F. Koao, F.B. Dejene, R.E. Kroon, H.C. Swart, J. Lumin. 147, 85–89 (2014)CrossRef
11.
Zurück zum Zitat X. Shi, Y. Liu, J. Zhang et al., Ceram. Int. 41(2), 3162–3168 (2015)CrossRef X. Shi, Y. Liu, J. Zhang et al., Ceram. Int. 41(2), 3162–3168 (2015)CrossRef
12.
Zurück zum Zitat M. Shivram, S.C. Prashantha, H. Nagabhushana et al., Spectrochim. Acta A 120, 395–400 (2014)CrossRef M. Shivram, S.C. Prashantha, H. Nagabhushana et al., Spectrochim. Acta A 120, 395–400 (2014)CrossRef
13.
Zurück zum Zitat B.F. Lei, S.Q. Man, Y.L. Liu, S. Yue, Mater. Chem. Phys. 124, 912 (2010)CrossRef B.F. Lei, S.Q. Man, Y.L. Liu, S. Yue, Mater. Chem. Phys. 124, 912 (2010)CrossRef
14.
15.
Zurück zum Zitat O. Singh, M.P. Singh, N. Kohli et al., Sens. Actuators B Chem. 166–167, 438–443 (2012)CrossRef O. Singh, M.P. Singh, N. Kohli et al., Sens. Actuators B Chem. 166–167, 438–443 (2012)CrossRef
16.
Metadaten
Titel
Effect of pH on the microstructure and luminescence of Eu3+-doped BiPO4 phosphors
verfasst von
Shu-qing Yan
Publikationsdatum
01.06.2015
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 6/2015
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-015-2897-3

Weitere Artikel der Ausgabe 6/2015

Journal of Materials Science: Materials in Electronics 6/2015 Zur Ausgabe

Neuer Inhalt