Experimental research on the technical characteristics of lightweight concretes incorporating scoria was conducted. The objective of this research is to investigate the feasibility and effectiveness of the use of scoria, in lightweight concretes. Coarse scoria of 5/10 and 10/20 mm were used. A portion of the aggregate mixtures had an average particle size ≤100 μm. Scorias are often used as the constituents of structural concrete and insulating materials. The usability of the concretes tested in this study broadens as the porosity of the mixtures decreased and the cement dosage increased. According to the cement dosage and frequency types, the absorption coefficients of concretes ranged from 0.14 to 0.47. A compressive strength of 19 MPa corresponded to a density of 1800 kg/m3; compressive strengths from 10 to 18 MPa mapped to densities ranging from 1300 to 1700 kg/m3. The thermal conductivity of mixed concretes without scoria reached a maximum value of 0.268 W/m K. The thermal conductivity values of the concretes mixed without sand were below 0.403 W/m K. As sand content increased, the conductivity evolved from 0.565 to 0.657 W/m K. Freeze–thaw stability tests were conducted for 400 cycles or until specimens deteriorated. The experimental results helped in determining the optimum mixing conditions for the inclusion of scoria in cement to produce lightweight concretes.
ACI (2003). Guide for structural lightweight aggregate concrete (p. 38), ACI 213R-03, ACI Committee 213, American Concrete Institute.
Al-Chaar, G.K., Alkadi, M., Yaksic, D.A., & Kallemeyn, L.A. (2011). The use of natural pozzolan in concrete as an additive or substitute for cement. ERDC/CERL TR-11-46.
Al-Swaidani, A. M., & Aliyan, S. D. (2015). Effect of adding scoria as cement replacement on durability-related properties. International Journal of Concrete Structures and Materials,9(2), 241–254. CrossRef
Asdrubali, F., & Pispola, G. (2007). Properties of transparent sound absorbing panels for use in noise barriers. Journal of the Acoustical Society of America,121(1), 214–221. CrossRef
ASTM E492 (1996). Standard test method for laboratory measurement of impact sound transmission through floor-ceiling assemblies using the tapping machine.
ASTM C117 (2004). Standard test method for materials finer than 75-μm (No. 200) sieve in mineral aggregates by washing.
ASTM C150 (2009). Standard specification for Portland cement. 10 pp. doi: 10.1520/C0150_C0150M-09.
ASTM C 618 (2001). Standard specification for coal fly ash and raw or calcined natural pozzolan for use as a mineral admixture in concrete, ASTM C618-00, Annual Book ASTM Standard 04.02, 310-313.
ASTM C 33-03 (2003). Standard specifications for concrete aggregates.
ASTM C 143 (2014). Slump of hydraulic cement concrete. C. Roberts. doi: 10.1520/C0143_C0143M-08. http://www.astm.org/cgi-bin/resolver.cgi?C143C143M-08.
ASTM International. (2009). Annual book of ASTM standards. West Conshohocken: ASTM International.
ASTM Standard C666/C666M-03(2003) (2008). Standard test method for resistance of concrete to rapid freezing and thawing. West Conshohocken: ASTM International. www.astm.org.
ASTM Standard C672. (1992). Standard test method for scaling resistance of concrete surfaces exposed to deicing chemicals. American Society for Testing and Materials, Philadelphia, Annual Book of ASTM Standards,04(02), 341–343.
Baaroghel-Bouny, V., Mounanga, P., Khelidj, A., Loukili, A., & RafaI, N. (2006). Autogenous deformations of cement pastes: Part II. W/C effects, micro-macro correlations, and threshold values. Cement and Concrete Research,36(1), 123–136. CrossRef
Babu, G. K., & Babu, S. D. (2003). Behaviour of lightweight expanded polystyrene concrete containing silica fume. Cement and Concrete Research,33(5), 755–762. CrossRef
Beaucour, A.L., Fiorio, B., & Ortola, S. (2003). Prediction of the elastic modulus of structural lightweight aggregate concrete. In: Proceedings of the 6th CANMET/ACI International Conference on Recent Advances in Concrete Technologies, Bucharest, Romania.
Bessenouci, M.Z., Triki, N.E.B., Khelladi, S., Draoui, B., & Abene, A. (2011). The apparent thermal conductivity of pozzolana concrete. Seventh International Conference on Material Sciences (CSM7), Beirut–Lebanon. Elsevier- Physics Procedia 21, 59–66.
Beycioğlu, A., Doğan D., Çullu, M., & Şamandar, A. (2010). Alkali Silika Reaksiyonu Ve Beton Durabilitesine Etkileri. MYO-ÖS- Ulusal Meslek Yüksekokulları Öğrenci Sempozyumu, 21-22 EKİM –DŰZCE.
Bhattacharjee, B. (2014). Concrete Technology. Department of Civil Engineering Indian Institute of Technology, Delhi. Aggregates, lecture – 07.
Bodet, R. (2014). Standards and regulations: Present status in France vs, Europe and other countries. Workshop ENPC “Recycling concrete into concrete”.
Burlion, N., Bourgeois, F., & Shao, J. F. (2005). Effects of desiccation on mechanical behaviour of concrete. Cement and Concrete Research,27(3), 367–379. CrossRef
Chen, W., & Brouwers, H. J. H. (2007). The hydration of slag, part 2: Reaction models for blended cement. Journal of Materials Sciences,42(2), 444–464. CrossRef
Chen, B., & Liu, J. (2004). Properties of lightweight expanded polystyrene concrete reinforced with steel fiber. Cement and Concrete Research,4(7), 1259–1263. CrossRef
Chi, J. M., Huang, R., Yang, C. C., & Chang, J. J. (2003). Effect of aggregate properties on the strength and stiffness of lightweight concrete. Cement & Concrete Composites,25(2), 197–205. CrossRef
Coussy, O., & Monteiro, P. (2007). Unsaturated poroelasticity for crystallization in pores. Computers and Geotechnics,34(4), 279–290. CrossRef
Cwirzen, A., & Penttala, V. (2005). Aggregate-cement paste transition zone properties affecting the salt-frost damage of high-performance concretes. Cement and Concrete Research,35(5), 671–679. CrossRef
De Sa, C., Benboudjema, F., Duong, K., & Sicard, J. (2006). A meso-scale approach for the modeling of concrete behavior at high temperatures (pp. 557-564). In: Proceedings of the Euro-C Conference on Computational Modelling of Concrete structures, Austria 2006. The Netherlands: Taylor and Francis/Balkema.
de Sensale, G. R., & Goncalves, A. F. (2014). Effects of fine LWA and SAP as internal water curing agents. International Journal of Concrete Structures and Materials,8(3), 229–238. CrossRef
Durán-Herrera, A., Juárez, C. A., Valdez, P., & Bentz, D. P. (2011). Evaluation of sustainable high-volume fly ash concretes. Cement & Concrete Composites,33, 39–45. CrossRef
Elfordy, S., Lucas, F., Tancret, F., Scudeller, Y., & Goudet, L. (2008). Mechanical and thermal properties of lime and hemp concrete («hemprete») manufactured by a projection process. Construction and Building Materials,22(10), 2116–2123. CrossRef
Ezziane, K., Bougara, A., Kadri, A., Khelafi, H., & Kadri, E. (2007). Compressive strength of mortar containing naturel pozzolan under various curing temperature. Cement & Concrete Composites,29(8), 587–593. CrossRef
Gao, P., Wu, S., Lin, P., Wu, Z., & Tang, M. (2006). The characterisitics of air void and frost resisttance of RCC with fly ash and expansive agent. Construction and Building Materials,20(8), 586–590. CrossRef
Ghrici, M., Kenai, S., & Said-Mansour, M. (2007). Mechanical properties and durability of mortar and concrete containing natural pozzolana and limestone blended, cements. Cement & Concrete Composites,29(7), 542–549. CrossRef
Hamoush, S., Picornell-Darder, M., Abu-Lebdeh, T., & Mohamed, A. (2011). Freezing and thawing durability of very high strength concrete. American Journal of Engineering and Applied Sciences,4(1), 42–51. CrossRef
Hilal, A. A., Thom, N. H., & Dawson, A. R. (2015). The use of additives to enhance properties of pre-formed foamed concrete. IACSIT International Journal of Engineering and Technology,7(4), 286. CrossRef
ISO 354 (2003). Measurement of sound absorption in reverberation room, acoustics.
Kang, J., & Brocklesby, M. W. (2005). Feasibility of applying microperforated absorbers in acoustic window systems. Applied Acoustics,66(6), 669–689. CrossRef
Khedari, J., Charoenvai, S., & Hirunlabh, J. (2003). New insulating particleboards from durian peel and coconut coir. Building and Environment,38(3), 435–441. CrossRef
Lotfy, A., Hossain, K. M., & Lachemi, M. (2015). Lightweight self-consolidating concrete with expanded shale aggregates: Modelling and optimization. International Journal of Concrete Structures and Materials,9(2), 185–206. CrossRef
Maa, D. Y. (2007). Practical single MPP absorber. International Journal of Acoustics and Vibration,12(1), 3–6. CrossRef
Miled, K., Sab, K., & Le Roy, R. (2007). Particle size effect on EPS lightweight concrete compressive strength: Experimental investigation and modelling. Mechanics of Materials,39(3), 222–240. CrossRef
Mouli, M., & Khelafi, H. (2008). Performance characteristics of lightweight aggregate concrete containing naturel pozzolan. Building and Environement,43(1), 31–36. CrossRef
Norme NF EN 206-1 (2004). Concrete - Part 1: Specification, performance, production and conformity, AFNOR.
Parhizkar, T., Najimi, M., Pourkhorshidi, A. R., Jafarpour, F., Hillemeier, B., & Herr, R. (2010). Proposing a new approach for qualification of natural pozzolans. c Sharif University of Technology. Transaction A. Civil Engineering,17(6), 450–456.
Penttala, V. (2006). Surface and internal deterioration due to saline and non-saline freeze thaw loads. Cement and Concrete Research,36(5), 921–928. CrossRef
Ricardi, P. (2001). Study on the acoustic transmission loss of a rigid perforated screen backed with porous granular material. In: Proceedings of 17th ICA, Rome.
Rossignolo, J. A., Agnesini, M. V. C., & Morais, J. A. (2003). Properties of high- performance LWAC for precast structures with Brazilian lightweight concrete. Cement and Concrete Composite,25(1), 77–82. CrossRef
Ruzzene, M. (2004). Vibration and sound radiation of sandwich beams with honeycomb truss core. Journal of Sound and Vibration,277(4–5), 741–763. CrossRef
Shink, M., & Alaiwa, A. A. (2016). Structural lightweight concrete or mortar, method for manufacturing same and use thereof as self-placing concrete. US 2014/0336305 A1. 8 pp.
Sobolev, K. G., & Batrakov, V. G. (2007). Effect of a polyethylhydrosiloxane admixture on the durability of concrete with supplementary cementitious materials. Journal of Materials in Civil Engineering,19(10), 809–819. CrossRef
UCGCT (2009). Understanding cement glossary of cementitious terms, Version 2.5, © WHD Microanalysis Consultants Ltd.
UNESCO. (1995). Major regional project geology for sustainable development (pp. 0258–3674). Paris: UNESCO.
Valenza, J. J., II, & Scherer, G. W. (2007). A review of salt scaling: I. Phenomenology. Cement and Concrete Research,37(7), 1007–1021. CrossRef
Vlček, J., Drongová, L., Topinková, M., Matějka, V., Kukutschová, J., Vavro, M., et al. (2014). Identification of phase composition of binders from alkali activated mixtures of granulated blast furnace slag and fly ash. Ceramics – Silikáty,58(1), 79–88.
XPP 18420, (1995). Concrete- test on scaling surfaces of hardened concrete exposed to frost in presence salt solution. AFNOR.
Yaşar, E., Atis, C. D., & Kiliҫ, A. (2004). High strength lightweight concrete made with ternary mixtures of cement-fly ash-silica fume and scoria as aggregate. Turkish Journal of Engineering and Environmental Sciences,28, 95–100.
Zhang, B., Lang, Ge, S.P., & Zhuang, W. (2000). The study of sound absorption characteristic of micro-perforated panel with different diameter holes (p. 3871-3874). In Proceedings of Internoise-2000. France: Nice.
- Effect of Scoria on Various Specific Aspects of Lightweight Concrete
Eddie Franck Rajaonarison
Velomanantsoa Gabriely Ranaivoniarivo
Bam Haja Nirina Razafindrabe
- Springer Netherlands
- International Journal of Concrete Structures and Materials
Print ISSN: 1976-0485
Elektronische ISSN: 2234-1315