In this work, the local corrosion at crack tip on an API 5L X46 pipeline steel specimens was investigated under various applied loads in a near-neutral pH solution. Electrochemical measurements, including potentiodynamic polarization and electrochemical impedance spectroscopy, combined with micro-electrochemical technique and surface characterization, were conducted to investigate the effect of stress on local anodic solution of the steel at the crack tip. The stress corrosion cracking of the steel was dominated by an anodic dissolution mechanism, while the effect of hydrogen was negligible. The applied load (stress) increased the corrosion rate at the crack tip, contributing to crack propagation. The deposit of corrosion products at the crack tip could protect somewhat from further corrosion. At sufficiently large applied loads such as 740 N in the work, it was possible to generate separated cathode and anode, further accelerating the crack growth.
Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten
Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:
Y.F. Cheng, Stress Corrosion Cracking of Pipelines, Wiley, Hoboken, 2013 CrossRef
National Energy Board, Stress Corrosion Cracking on Canadian Oil and Gas Pipelines, Calgary, AB, 1996
M. Javidi and S. Bahalaou, Horeh, Investigating the Mechanism of Stress Corrosion Cracking in Near-Neutral and High pH Environments for API, 5L X52 Steel, Corros. Sci., 2014, 80, p 213–220 CrossRef
X.Y. Zhang, S.B. Lambert, and R. Sutherby, Transgranular Stress Corrosion Cracking of X-60 Pipeline Steel in Simulated Ground Water, Corrosion, 1999, 55, p 297–305 CrossRef
B.Y. Fang, E.H. Han, J.Q. Wang, and W. Ke, Stress Corrosion Cracking of X-70 Pipeline Steel in Near Neutral pH Solution Subjected to Constant Load and Cyclic Load Testing, Corros. Eng., Sci. Technol., 2007, 42, p 123–129 CrossRef
Z.Y. Liu, X.G. Li, and Y.F. Cheng, Mechanistic aspect of Near-Neutral pH Stress Corrosion Cracking of Pipelines under Cathodic Polarization, Corros. Sci., 2012, 55, p 54–60 CrossRef
G. Liang, X. Peng, E.S. Juan, and Y.F. Cheng, Strain Aging of X100 Steel in Service and the Enhanced Susceptibility of Pipelines to Stress Corrosion Cracking, J. Mater. Eng. Perform., 2013, 22, p 3778–3782 CrossRef
Y.F. Cheng, Analysis of Electrochemical Hydrogen Permeation Through X-65 Pipeline Steel and its Implications on Pipeline Stress Corrosion Cracking, Int. J. Hydrog. Energy, 2007, 32, p 1269–1276 CrossRef
H.B. Xue and Y.F. Cheng, Hydrogen Permeation and Electrochemical Corrosion Behavior of X80 Pipeline Steel Weld, J. Mater. Eng. Perform., 2013, 22, p 170–175 CrossRef
G.A. Zhang and Y.F. Cheng, Micro-Electrochemical Characterization of Corrosion of Pre-Cracked X70 Pipeline Steel in a Concentrated Carbonate/Bicarbonate Solution, Corros. Sci., 2010, 52, p 960–968 CrossRef
X. Tang and Y.F. Cheng, Micro-Electrochemical Characterization of the Effect of Applied Stress on Local Anodic Dissolution Behavior of Pipeline Steel under Near-Neutral pH Condition, Electrochim. Acta, 2009, 54, p 1499–1505 CrossRef
Y.F. Cheng, Fundamentals of Hydrogen Evolution Reaction and its Implications on Near-Neutral pH Stress Corrosion Cracking of Pipelines, Electrochim. Acta, 2007, 52, p 2661–2667 CrossRef
A. Turnbull, The Solution Composition and Electrode Potential in Pits, Crevices and Crack, Corros. Sci., 1983, 8, p 833–870 CrossRef
I. Dmytrakh, Corrosion Fracture of Structural Metallic Materials: Effect of Electrochemical Conditions in Crack, Strain Int. J. Exp. Mech., 2011, 47, p 427–435
Z.Y. Liu, X.G. Li, and Y.F. Cheng, Effect of Strain Rate on Cathodic Reaction During Stress Corrosion Cracking of X70 Steel in a Near-Neutral pH Solution, J. Mater. Eng. Perform., 2011, 20, p 1242–1246 CrossRef
ASTM, E647-15, Standard Test Method for Measurement of Fatigue Crack Growth Rates, West Conshohocken, PA, USA, 2015.
R.N. Parkins, W.K. Blanchard, and B.S. Delanty, Transgranular Stress Corrosion Cracking of High-Pressure Pipelines in Contact with Solutions of Near Neutral pH, Corrosion, 1994, 50, p 394–408 CrossRef
ASTM, E8/E8M Standard Test Methods for Tension Testing of Metallic Materials, West Conshohocken, PA, USA, 2010.
ASTM G59-97, Standard Test Method for Conducting Potentiodynamic Polarization Resistance Measurements, West Conshohocken, PA, USA, 2014.
C.F. Dong, Z.Y. Liu, X.G. Li, and Y.F. Cheng, Effects of Hydrogen-Charging on the Susceptibility of X100 Pipeline Steel to Hydrogen-Induced Cracking, Int. J. Hydrog. Energy, 2009, 34, p 9879–9884 CrossRef
L.Y. Xu and Y.F. Cheng, Corrosion of X100 Pipeline Steel under Plastic Strain in a Neutral pH Bicarbonate Solution, Corros. Sci., 2012, 64, p 145–152 CrossRef
L.Y. Xu and Y.F. Cheng, An Experimental Investigation of Corrosion of X100 Pipeline Steel under Uniaxial Elastic Stress in a Near-Neutral pH Solution, Corros. Sci., 2012, 59, p 103–109 CrossRef
G.Z. Meng, C. Zhang, and Y.F. Cheng, Effects of Corrosion Product Deposit on the Subsequent Cathodic and Anodic Reactions of X-70 Steel in Near-Neutral pH Solution, Corros. Sci., 2008, 50, p 3116–3122 CrossRef
- Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution
Y. Frank Cheng
- Springer US
in-adhesives, MKVS, Neuer Inhalt/© Zühlke, Hellmich GmbH/© Hellmich GmbH, Neuer Inhalt/© momius | stock.adobe.com