Effect of TiBCN Content on Microstructure and Properties of Laser Cladding Ti/TiBCN Composite Coatings

verfasst von: Yuxin Li, Keqiang Su, Peikang Bai, Liyun Wu, Bin Liu, Hongwen Su, Wenbo Du

Erschienen in: Metals and Materials International | Ausgabe 5/2019

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

The Ti/TiBCN composite coatings were fabricated on the substrate of Ti6Al4V alloy by laser cladding. The effects of TiBCN content on the microstructre, microhardness, corrosion resistance and tribological properties of the composite coatings were studied. The results showed that, when the TiBCN content was 60 wt%, the composite coatings were mainly composed of the dendritic and rod-shaped TiBCN phases, small white lump TiC phases, fine lamellar TiN phases, small and scattered white block TiB2 phases, In addition, there was a small quantity of short whisker Al3Ti phases and uniform layer block TiAl phases. Furhtermore, the maximum microhardness was 1596 HV, which was about 4.6 folds greater than that of the substrate; the corrosion potential (Ecorr) reached − 1.258 V and the corrosion current density (Icorr) was 4.035 × 10−5 A/cm2, which was one order lower than that of the substrate (1.172 × 10−4 A/cm2); the worn surface was relatively smooth and the mass loss (1.22 g) was only 9/50 of that of the substrate (6.71 g).

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Y.M. Chi, G.C. Gu, H.J. Yu, C.Z. Chen, Opt. Laser. Eng. 100, 23 (2018)CrossRef Y.M. Chi, G.C. Gu, H.J. Yu, C.Z. Chen, Opt. Laser. Eng. 100, 23 (2018)CrossRef
2.
Zurück zum Zitat X. Su, W. Tao, Y. Chen, X. Chen, Z. Tian, Mater. Lett. 195, 228 (2017)CrossRef X. Su, W. Tao, Y. Chen, X. Chen, Z. Tian, Mater. Lett. 195, 228 (2017)CrossRef
3.
Zurück zum Zitat M. Nabhani, R.S. Razavi, M. Barekat, Opt. Laser. Eng. 100, 265 (2018)CrossRef M. Nabhani, R.S. Razavi, M. Barekat, Opt. Laser. Eng. 100, 265 (2018)CrossRef
4.
Zurück zum Zitat C.T. Kwok, H.C. Man, F.T. Cheng, K.H. Lo, Surf. Coat. Tech. 291, 189 (2016)CrossRef C.T. Kwok, H.C. Man, F.T. Cheng, K.H. Lo, Surf. Coat. Tech. 291, 189 (2016)CrossRef
5.
Zurück zum Zitat X.Y. Jiao, J. Wang, C.M. Wang, Z.Q. Gong, X.X. Pang, S.M. Xiong, Opt. Laser. Eng. 110, 163 (2018)CrossRef X.Y. Jiao, J. Wang, C.M. Wang, Z.Q. Gong, X.X. Pang, S.M. Xiong, Opt. Laser. Eng. 110, 163 (2018)CrossRef
8.
9.
Zurück zum Zitat D.B. Wei, P.Z. Zhang, Z.J. Yao, X.H. Chen, F.K. Li, Vacuum 155, 233 (2018)CrossRef D.B. Wei, P.Z. Zhang, Z.J. Yao, X.H. Chen, F.K. Li, Vacuum 155, 233 (2018)CrossRef
10.
Zurück zum Zitat C.M. Lin, W.Y. Kai, C.Y. Su, C.N. Tsai, Y.C. Chen, J. Alloy. Compd. 717, 197 (2017)CrossRef C.M. Lin, W.Y. Kai, C.Y. Su, C.N. Tsai, Y.C. Chen, J. Alloy. Compd. 717, 197 (2017)CrossRef
11.
Zurück zum Zitat J.L. Daure, M.J. Carrington, P.H. Shipway, D.G. McCartney, D.A. Stewartb, Surf. Coat. Tech. 350, 40 (2018)CrossRef J.L. Daure, M.J. Carrington, P.H. Shipway, D.G. McCartney, D.A. Stewartb, Surf. Coat. Tech. 350, 40 (2018)CrossRef
12.
13.
Zurück zum Zitat M. Staszuk, D. Pakuła, G. Chladek, M. Pawlyta, M. Pancielejko, P. Czaja, Vacuum 154, 272 (2018)CrossRef M. Staszuk, D. Pakuła, G. Chladek, M. Pawlyta, M. Pancielejko, P. Czaja, Vacuum 154, 272 (2018)CrossRef
14.
Zurück zum Zitat D. Hui, K. Endo, K. Yamamura, Int. J. Mach. Tools Manuf 115, 38 (2017)CrossRef D. Hui, K. Endo, K. Yamamura, Int. J. Mach. Tools Manuf 115, 38 (2017)CrossRef
15.
16.
17.
Zurück zum Zitat C. Czettl, J. Thurner, U. Schleinkofer, Int. J. Refract. Met. H. 71, 330 (2018)CrossRef C. Czettl, J. Thurner, U. Schleinkofer, Int. J. Refract. Met. H. 71, 330 (2018)CrossRef
18.
Zurück zum Zitat T. Lutzler, T.V.J. Charpentier, R. Barker, S. Soltanahmadi, W. Taleb, C. Wang, A. Alejo-Rodriguez, E. Perre, H. Schneider, A. Nevillea, Mater. Chem. Phys. 216, 272 (2018)CrossRef T. Lutzler, T.V.J. Charpentier, R. Barker, S. Soltanahmadi, W. Taleb, C. Wang, A. Alejo-Rodriguez, E. Perre, H. Schneider, A. Nevillea, Mater. Chem. Phys. 216, 272 (2018)CrossRef
19.
Zurück zum Zitat A. Alcantara-Garcia, A. Garcia-Casas, A. Jimenez-Morales, Prog. Org. Coat. 124, 267 (2018)CrossRef A. Alcantara-Garcia, A. Garcia-Casas, A. Jimenez-Morales, Prog. Org. Coat. 124, 267 (2018)CrossRef
20.
Zurück zum Zitat W. Gao, C. Chang, G. Li, Y. Xue, J. Wang, Z. Zhang, X. Lin, Optik. 178, 950 (2019)CrossRef W. Gao, C. Chang, G. Li, Y. Xue, J. Wang, Z. Zhang, X. Lin, Optik. 178, 950 (2019)CrossRef
21.
22.
Zurück zum Zitat G.H. Meng, X. Lin, H. Xie, T.M. Yue, X. Ding, L. Sun, M. Qi, Mater. Des. 108, 157 (2016)CrossRef G.H. Meng, X. Lin, H. Xie, T.M. Yue, X. Ding, L. Sun, M. Qi, Mater. Des. 108, 157 (2016)CrossRef
23.
Zurück zum Zitat D. Shu, Z.G. Li, K. Zhang, C.W. Yao, D.Y. Li, Z.B. Dai, Mater. Lett. 195, 178 (2017)CrossRef D. Shu, Z.G. Li, K. Zhang, C.W. Yao, D.Y. Li, Z.B. Dai, Mater. Lett. 195, 178 (2017)CrossRef
24.
25.
26.
Zurück zum Zitat X.Y. Jiao, C.M. Wang, Z.Q. Gong, G.M. Wang, H.F. Sun, H.R. Yang, Surf. Coat. Technol. 325, 643 (2017)CrossRef X.Y. Jiao, C.M. Wang, Z.Q. Gong, G.M. Wang, H.F. Sun, H.R. Yang, Surf. Coat. Technol. 325, 643 (2017)CrossRef
28.
Zurück zum Zitat X.Y. Jiao, C.M. Wang, Z.Q. Gong, G.M. Wang, H.F. Sun, H.R. Yang, Surf. Coat. Technol. 325, 643 (2017)CrossRef X.Y. Jiao, C.M. Wang, Z.Q. Gong, G.M. Wang, H.F. Sun, H.R. Yang, Surf. Coat. Technol. 325, 643 (2017)CrossRef
29.
Zurück zum Zitat S. Kumar, A. Mandal, A. Das, A. Dixit, Surf. Coat. Technol. 349, 37 (2018)CrossRef S. Kumar, A. Mandal, A. Das, A. Dixit, Surf. Coat. Technol. 349, 37 (2018)CrossRef
30.
32.
Zurück zum Zitat H. Liu, X. Zhang, Y. Jiang, R. Zhou, J. Alloy. Compd. 670, 268 (2016)CrossRef H. Liu, X. Zhang, Y. Jiang, R. Zhou, J. Alloy. Compd. 670, 268 (2016)CrossRef
33.
Zurück zum Zitat Y. Lei, R. Sun, J. Lei, Y. Tang, W. Niu, Opt. Laser Eng. 48, 899 (2010)CrossRef Y. Lei, R. Sun, J. Lei, Y. Tang, W. Niu, Opt. Laser Eng. 48, 899 (2010)CrossRef
34.
Zurück zum Zitat Y. Lin, J. Yao, Y. Lei, H. Fu, L. Wang, Opt. Laser Eng. 86, 216 (2016)CrossRef Y. Lin, J. Yao, Y. Lei, H. Fu, L. Wang, Opt. Laser Eng. 86, 216 (2016)CrossRef
36.
Zurück zum Zitat J.L. Li, G.Y. Cai, H.S. Zhong, Y.X. Wang, J.M. Chen, Rare Met. 36, 858 (2017)CrossRef J.L. Li, G.Y. Cai, H.S. Zhong, Y.X. Wang, J.M. Chen, Rare Met. 36, 858 (2017)CrossRef
37.
Zurück zum Zitat Y. Li, P. Zhang, P. Bai, L. Wu, B. Liu, Z. Zhao, Surf. Coat. Technol. 334, 142 (2018)CrossRef Y. Li, P. Zhang, P. Bai, L. Wu, B. Liu, Z. Zhao, Surf. Coat. Technol. 334, 142 (2018)CrossRef
38.
39.
Zurück zum Zitat M.O.H. Amuda, E.T. Akinlabi, M. Moolla, Mater. Today 4, 763 (2017) M.O.H. Amuda, E.T. Akinlabi, M. Moolla, Mater. Today 4, 763 (2017)
40.
Zurück zum Zitat Y.G. Han, Y. Yang, L. Wang, X.G. Chen, Z.H. Chu, X.N. Zhang, Y.C. Dong, Z. Liu, D.R. Yan, J.X. Zhang, C.G. Li, Appl. Surf. Sci. 431, 48 (2018)CrossRef Y.G. Han, Y. Yang, L. Wang, X.G. Chen, Z.H. Chu, X.N. Zhang, Y.C. Dong, Z. Liu, D.R. Yan, J.X. Zhang, C.G. Li, Appl. Surf. Sci. 431, 48 (2018)CrossRef
42.
Zurück zum Zitat L. Yang, Z. Li, Y. Zhang, S. Wei, F. Liu, Appl. Surf. Sci. 435, 1187 (2018)CrossRef L. Yang, Z. Li, Y. Zhang, S. Wei, F. Liu, Appl. Surf. Sci. 435, 1187 (2018)CrossRef
43.
Zurück zum Zitat S. Sun, H. Fu, X. Ping, J. Lin, Y. Lei, W. Wu, J. Zhou, Appl. Surf. Sci. 455, 160 (2018)CrossRef S. Sun, H. Fu, X. Ping, J. Lin, Y. Lei, W. Wu, J. Zhou, Appl. Surf. Sci. 455, 160 (2018)CrossRef
44.
Zurück zum Zitat Z. Li, R. Xu, Z. Zhang, I. Kucukkoc, Int. J. Mach. Tools Manuf 126, 1 (2018)CrossRef Z. Li, R. Xu, Z. Zhang, I. Kucukkoc, Int. J. Mach. Tools Manuf 126, 1 (2018)CrossRef
45.
Zurück zum Zitat Y.X. Li, J.D. Hu, H.Y. Wang, Z.X. Guo, Adv. Eng. Mater. 9, 689 (2017)CrossRef Y.X. Li, J.D. Hu, H.Y. Wang, Z.X. Guo, Adv. Eng. Mater. 9, 689 (2017)CrossRef
46.
Zurück zum Zitat Y.X. Li, J.D. Hu, H.Y. Wang, Z.X. Guo, Adv. Eng. Mater. 9, 689 (2010)CrossRef Y.X. Li, J.D. Hu, H.Y. Wang, Z.X. Guo, Adv. Eng. Mater. 9, 689 (2010)CrossRef
47.
Zurück zum Zitat Y. Guo, Y. Zhang, Z. Li, S. Wei, T. Zhang, L. Yang, S. Liu, Surf. Coat. Technol. 334, 471 (2018)CrossRef Y. Guo, Y. Zhang, Z. Li, S. Wei, T. Zhang, L. Yang, S. Liu, Surf. Coat. Technol. 334, 471 (2018)CrossRef
48.
49.
Zurück zum Zitat J. Park, H.S. Han, J. Park, H. Seo, J. Edwards, Y.C. Kim, M.R. Ok, H.K. Seok, H. Jeon, Appl. Surf. Sci. 448, 424 (2018)CrossRef J. Park, H.S. Han, J. Park, H. Seo, J. Edwards, Y.C. Kim, M.R. Ok, H.K. Seok, H. Jeon, Appl. Surf. Sci. 448, 424 (2018)CrossRef
50.
Zurück zum Zitat D. Hawelka, J. Stollenwerk, N. Pirch, K. Wissenbach, P. Loosen, J. Coat. Technol. Res. 11, 3 (2014)CrossRef D. Hawelka, J. Stollenwerk, N. Pirch, K. Wissenbach, P. Loosen, J. Coat. Technol. Res. 11, 3 (2014)CrossRef
51.
Zurück zum Zitat B. Cárcel, A. Serrano, J. Zambrano, A.C. Amigo cárcelc, Phys. Procedia 56, 284 (2014)CrossRef B. Cárcel, A. Serrano, J. Zambrano, A.C. Amigo cárcelc, Phys. Procedia 56, 284 (2014)CrossRef
52.
Zurück zum Zitat Z.T. Wang, X. Lin, Y.Q. Cao, F.C. Liu, W.D. Huang, Opt. Laser Technol. 99, 154 (2018)CrossRef Z.T. Wang, X. Lin, Y.Q. Cao, F.C. Liu, W.D. Huang, Opt. Laser Technol. 99, 154 (2018)CrossRef
53.
Zurück zum Zitat X. Duan, S. Gao, Q. Dong, Y. Zhou, M. Xi, X. Xian, B. Wang, Surf. Coat. Technol. 291, 230 (2016)CrossRef X. Duan, S. Gao, Q. Dong, Y. Zhou, M. Xi, X. Xian, B. Wang, Surf. Coat. Technol. 291, 230 (2016)CrossRef
54.
Zurück zum Zitat Y.B. Cao, S.X. Zhi, Q. Gao, X.T. Tian, T. Geng, X. Guan, Mater. Charact. 119, 159 (2016)CrossRef Y.B. Cao, S.X. Zhi, Q. Gao, X.T. Tian, T. Geng, X. Guan, Mater. Charact. 119, 159 (2016)CrossRef
55.
Zurück zum Zitat N. Atta, M. Abd El Fatah, A. Galal, Int. J. Electrochem. Sci. 12, 1625 (2017)CrossRef N. Atta, M. Abd El Fatah, A. Galal, Int. J. Electrochem. Sci. 12, 1625 (2017)CrossRef
56.
57.
Zurück zum Zitat J. Lin, J.J. Moore, B. Mishra, M. Pinkas, W.D. Sproul, Acta Mater. 58, 1554 (2010)CrossRef J. Lin, J.J. Moore, B. Mishra, M. Pinkas, W.D. Sproul, Acta Mater. 58, 1554 (2010)CrossRef
Metadaten
Titel
Effect of TiBCN Content on Microstructure and Properties of Laser Cladding Ti/TiBCN Composite Coatings
verfasst von
Yuxin Li
Keqiang Su
Peikang Bai
Liyun Wu
Bin Liu
Hongwen Su
Wenbo Du
Publikationsdatum
09.05.2019
Verlag
The Korean Institute of Metals and Materials
Erschienen in
Metals and Materials International / Ausgabe 5/2019
Print ISSN: 1598-9623
Elektronische ISSN: 2005-4149
DOI
https://doi.org/10.1007/s12540-019-00287-2

Weitere Artikel der Ausgabe 5/2019

Metals and Materials International 5/2019 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.