Effects of Bi2O3–WO3 additive on microstructure and magnetic properties of low-temperature-fired MgCuZn ferrites
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 6/2015
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The low-temperature-fired MgCuZn ferrites with various amounts of Bi2O3 and WO3 additives were prepared by a conventional solid-state reaction method. The effects of Bi2O3 and WO3 additives on sintering behavior, microstructures and magnetic properties of MgCuZn ferrites were investigated. It is found that Bi2O3 and WO3 additives overtly improve the densification of samples through the formation of liquid phase and grains growth. Appropriate Bi2O3 and WO3 additives not only can noticeably increase the initial permeability (μ
i
) and saturation flux density (B
s
), but also can obviously reduce coercive field strength (H
c
). However, too much additive will deteriorate the magnetic properties. The ferrite sample with 0.1 wt% Bi2O3 and 0.1 wt% WO3 shows excellent magnetic properties: μ
i
= 703.27 at 100 kHz, B
s
= 213.28 mT, B
r
= 117.98 mT and H
c
= 44.01 A m−1.