Effects of Ga–Ag, Ga–Al and Al–Ag additions on the wetting characteristics of Sn–9Zn–X–Y lead-free solders
Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 12/2009
EinloggenAktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.
Wählen Sie Textabschnitte aus um mit Künstlicher Intelligenz passenden Patente zu finden. powered by
Markieren Sie Textabschnitte, um KI-gestützt weitere passende Inhalte zu finden. powered by
Abstract
The effects of Ga–Al, Ga–Ag and Al–Ag binary additions on the wetting characteristics of Sn–9Zn–X–Y lead-free solders are studied by the wetting balance method. Experimental results show that Sn–9Zn–1.0Ga–0.3Ag, Sn–9Zn–0.005Al–0.3Ag, and Sn–9Zn–0.3Ga–0.002Al possess better wettability than the other alloys tested. The mechanism by which Ga, Al, and Ag additions improve the wettability is also proposed. It appears that dense aluminum oxide film formation and the enrichment of Ga on the surface may protect the bulk liquid solder from further oxidation. Moreover, results also indicate that, AgZn3 IMCs layer formed at the interface, which may release reaction energy during the wetting, results in improving the wettability of the solder.