Effects of Grain Size on the Fatigue Properties in Cold-Expanded Austenitic HNSs

verfasst von: Jong-Ho Shin, Young-Deak Kim, Jong-Wook Lee

Erschienen in: Metals and Materials International | Ausgabe 6/2018

Einloggen

Aktivieren Sie unsere intelligente Suche, um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Cold-expanded austenitic high nitrogen steel (HNS) was subjected to investigate the effects of grain size on the stress-controlled high cycle fatigue (HCF) as well as the strain-controlled low cycle fatigue (LCF) properties. The austenitic HNSs with two different grain sizes (160 and 292 μm) were fabricated by the different hot forging strain. The fine-grained (FG) specimen exhibited longer LCF life and higher HCF limit than those of the coarse-grained (CG) specimen. Fatigue crack growth testing showed that crack propagation rate in the FG specimen was the same as that in the CG specimen, implying that crack propagation rate did not affect the discrepancy of LCF life and HCF limit between two cold-expanded HNSs. Therefore, it was estimated that superior LCF and HCF properties in the FG specimen resulted from the retardation of the fatigue crack initiation as compared with the CG specimen. Transmission electron microscopy showed that the effective grain size including twin boundaries are much finer in the FG specimen than that in the CG specimen, which can give favorable contributions to strengthening.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat Y. Kim, Y. Park, J. Corr. Sci. Kor. 18, 67 (1989) Y. Kim, Y. Park, J. Corr. Sci. Kor. 18, 67 (1989)
3.
4.
Zurück zum Zitat E. Werner, Mater. Sci. Eng., A 101, 93 (1988) E. Werner, Mater. Sci. Eng., A 101, 93 (1988)
6.
Zurück zum Zitat G. Saller, K. Spiradek-Hahn, C. Scheu, H. Clemens, Mater. Sci. Eng., A 427, 246 (2006)CrossRef G. Saller, K. Spiradek-Hahn, C. Scheu, H. Clemens, Mater. Sci. Eng., A 427, 246 (2006)CrossRef
7.
Zurück zum Zitat P. Mullner, C. Solenthaler, P. Uggowitzer, M.O. Speidel, Mater. Sci. Eng., A 164, 164 (1993)CrossRef P. Mullner, C. Solenthaler, P. Uggowitzer, M.O. Speidel, Mater. Sci. Eng., A 164, 164 (1993)CrossRef
9.
Zurück zum Zitat K. Orita, Y. Ikeda, T. Iwadate, J. Ishizaka, ISIJ Int. 30, 587 (1990)CrossRef K. Orita, Y. Ikeda, T. Iwadate, J. Ishizaka, ISIJ Int. 30, 587 (1990)CrossRef
12.
Zurück zum Zitat A. Chlupova, J. Man, I. Kubena, J. Polak, L.P. Karkalainen, Proc. Eng. 74, 147 (2014)CrossRef A. Chlupova, J. Man, I. Kubena, J. Polak, L.P. Karkalainen, Proc. Eng. 74, 147 (2014)CrossRef
13.
Zurück zum Zitat S. Kang, J. Jung, M. Kang, W. Woo, Y. Lee, Mater. Sci. Eng., A 652, 212 (2016)CrossRef S. Kang, J. Jung, M. Kang, W. Woo, Y. Lee, Mater. Sci. Eng., A 652, 212 (2016)CrossRef
14.
15.
Zurück zum Zitat A. Järvenpää, L.P. Karjalainen, M. Jaskari, Int. J. Fatigue 65, 93 (2014)CrossRef A. Järvenpää, L.P. Karjalainen, M. Jaskari, Int. J. Fatigue 65, 93 (2014)CrossRef
16.
Zurück zum Zitat A. Di Schino, M. Barteri, J.M. Kenny, J. Mater. Sci. Lett. 22, 1511 (2003)CrossRef A. Di Schino, M. Barteri, J.M. Kenny, J. Mater. Sci. Lett. 22, 1511 (2003)CrossRef
17.
Zurück zum Zitat M. Roach, S. Wright, J. Lemons, L. Zardiackas, Mater. Sci. Eng., A 586, 382 (2013)CrossRef M. Roach, S. Wright, J. Lemons, L. Zardiackas, Mater. Sci. Eng., A 586, 382 (2013)CrossRef
19.
Zurück zum Zitat A. Frehn, E. Ratte, W. Bleck, in Proceedings 7th International Conference High Nitrogen Steels, eds by N. Akdut, B.C. Decooman, J. Foct (GRIPS Media GmbH, Ostend, Belgium, 2004), p. 447 A. Frehn, E. Ratte, W. Bleck, in Proceedings 7th International Conference High Nitrogen Steels, eds by N. Akdut, B.C. Decooman, J. Foct (GRIPS Media GmbH, Ostend, Belgium, 2004), p. 447
21.
Zurück zum Zitat P. Changizian, A. Zarei-Hanzaki, H. Abedi, Mater. Sci. Eng., A 558, 44 (2012)CrossRef P. Changizian, A. Zarei-Hanzaki, H. Abedi, Mater. Sci. Eng., A 558, 44 (2012)CrossRef
22.
Zurück zum Zitat H.E. Kadiri, J. Kapil, A.L. Oppedal Jr., L.G. Hector, S.R. Agnew, M. Cherkaoui, S.C. Vogel, Acta Mater. 61, 3549 (2013)CrossRef H.E. Kadiri, J. Kapil, A.L. Oppedal Jr., L.G. Hector, S.R. Agnew, M. Cherkaoui, S.C. Vogel, Acta Mater. 61, 3549 (2013)CrossRef
23.
24.
25.
Zurück zum Zitat Y. Luo, C. Huang, R. Tian, Q. Wang, J. Iron Steel Inst. 20, 50 (2007)CrossRef Y. Luo, C. Huang, R. Tian, Q. Wang, J. Iron Steel Inst. 20, 50 (2007)CrossRef
26.
Zurück zum Zitat Q. Zhou, L. Qian, J. Meng, L. Zhao, F. Zhang, Mater. Des. 85, 487 (2015)CrossRef Q. Zhou, L. Qian, J. Meng, L. Zhao, F. Zhang, Mater. Des. 85, 487 (2015)CrossRef
27.
Zurück zum Zitat P. Guo, L. Qian, J. Meng, F. Zhang, L. Li, Mater. Sci. Eng., A 584, 133 (2013)CrossRef P. Guo, L. Qian, J. Meng, F. Zhang, L. Li, Mater. Sci. Eng., A 584, 133 (2013)CrossRef
29.
Zurück zum Zitat G.E. Dieter, Mechanical Metallurgy (McGraw-Hill, London, 1988) G.E. Dieter, Mechanical Metallurgy (McGraw-Hill, London, 1988)
30.
Zurück zum Zitat M. Mokhtarishirazabad, S.M.A. Boutorabi, M. Azadi, M. Nikravan, Mater. Sci. Eng., A 587, 179 (2013)CrossRef M. Mokhtarishirazabad, S.M.A. Boutorabi, M. Azadi, M. Nikravan, Mater. Sci. Eng., A 587, 179 (2013)CrossRef
31.
Zurück zum Zitat P. Paris, F. Erdogan, J. Fluids Eng. 85, 528 (1963) P. Paris, F. Erdogan, J. Fluids Eng. 85, 528 (1963)
32.
Zurück zum Zitat Y. Uematsu, M. Akita, M. Nakajima, K. Tokaji, Int. J. Fatigue 30, 642 (2008)CrossRef Y. Uematsu, M. Akita, M. Nakajima, K. Tokaji, Int. J. Fatigue 30, 642 (2008)CrossRef
33.
Zurück zum Zitat S. Kang, J. Jung, M. Kang, W. Woo, Y. Lee, Mater. Sci. Eng., A 652, 212 (2016)CrossRef S. Kang, J. Jung, M. Kang, W. Woo, Y. Lee, Mater. Sci. Eng., A 652, 212 (2016)CrossRef
34.
Zurück zum Zitat A.S. Hamada, L.P. Karjalainen, J. Puustinen, Mater. Sci. Eng., A 517, 68 (2009)CrossRef A.S. Hamada, L.P. Karjalainen, J. Puustinen, Mater. Sci. Eng., A 517, 68 (2009)CrossRef
Metadaten
Titel
Effects of Grain Size on the Fatigue Properties in Cold-Expanded Austenitic HNSs
verfasst von
Jong-Ho Shin
Young-Deak Kim
Jong-Wook Lee
Publikationsdatum
09.05.2018
Verlag
The Korean Institute of Metals and Materials
Erschienen in
Metals and Materials International / Ausgabe 6/2018
Print ISSN: 1598-9623
Elektronische ISSN: 2005-4149
DOI
https://doi.org/10.1007/s12540-018-0127-2

Weitere Artikel der Ausgabe 6/2018

Metals and Materials International 6/2018 Zur Ausgabe

    Marktübersichten

    Die im Laufe eines Jahres in der „adhäsion“ veröffentlichten Marktübersichten helfen Anwendern verschiedenster Branchen, sich einen gezielten Überblick über Lieferantenangebote zu verschaffen.