Efficacious realization of Ba0.5Sr0.5TixM1−xO3 (M = Mn2+, Co2+) perovskite nanostructures through oxalate precursor strategy

verfasst von: Ali Omar Turky, Ahmed Esmail Shalan, Mohamed M. Rashad, Hailei Zhao, Mikhael Bechelany

Erschienen in: Journal of Materials Science: Materials in Electronics | Ausgabe 17/2018

Einloggen

Aktivieren Sie unsere intelligente Suche um passende Fachinhalte oder Patente zu finden.

search-config
loading …

Abstract

Nowadays, barium strontium titanate (BST; Ba0.5Sr0.5TiO3) as a versatile material is a prospect candidate in different electronic and magnetic applications. In this study, cubic BST nanoparticles have been prosperity fabricated based on the oxalate precursor method. Afterwards, the formed precursor powders are further annealed at temperature 1000 °C for time 2 h. Meanwhile, the insertion of Mn2+ or Co2+ ions as an acceptor substitution to BST crystal was described at different concentrations from 0.1 to 0.3 molar ratios. Accordingly, the crystallite size and cell unit volume were found to enhance due to the introduction of acceptor ions. The Mn2+ or Co2+ ions replacements have the magnificent impact on the morphology, optical as well as dielectric and magnetic properties compared to the pure one. For instance, the optical transparency of BST material was found to increase with increasing Mn2+ or Co2+ ion content. Typically, the band gap energy and the refractive index were increased with acceptor doped ions. The dielectric performance in terms of different substitutions was decreased with Co2+ ions and increased with Mn2+ ions compared with pure BST sample. Eventually, the magnetic peculiarities were improved by addition of Mn2+ or Co2+ ions at different molar ratios.

Sie haben noch keine Lizenz? Dann Informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literatur
1.
Zurück zum Zitat G. Houzet, K. Blary, S. Lepilliet, D. Lippens, L. Burgnies, G. Ve´lu, J.C. Carru, E. Ngue´ma, P. Mounaix, J. Appl. Phys. 109, 014116 (2011)CrossRef G. Houzet, K. Blary, S. Lepilliet, D. Lippens, L. Burgnies, G. Ve´lu, J.C. Carru, E. Ngue´ma, P. Mounaix, J. Appl. Phys. 109, 014116 (2011)CrossRef
2.
3.
Zurück zum Zitat U. Ellerkmann, R. Liedtke, U. Boettger, R. Waser, Appl. Phys. Lett. 85, 4708 (2004)CrossRef U. Ellerkmann, R. Liedtke, U. Boettger, R. Waser, Appl. Phys. Lett. 85, 4708 (2004)CrossRef
4.
Zurück zum Zitat X. Hu, H. Li, Y. Liang, Y. Wei, Z. Yu, D. Marshall Jr., J. Edwards, R. Droopad, X. Zhang, A.A. Demkov, K. Moore, J. Kulik, Appl. Phys. Lett. 82, 203 (2003)CrossRef X. Hu, H. Li, Y. Liang, Y. Wei, Z. Yu, D. Marshall Jr., J. Edwards, R. Droopad, X. Zhang, A.A. Demkov, K. Moore, J. Kulik, Appl. Phys. Lett. 82, 203 (2003)CrossRef
5.
Zurück zum Zitat X. Zhu, W. Peng, J. Miao, D. Zheng, Mater. Lett. 58, 2045–2048 (2004)CrossRef X. Zhu, W. Peng, J. Miao, D. Zheng, Mater. Lett. 58, 2045–2048 (2004)CrossRef
6.
Zurück zum Zitat A.O. Turky, M.M. Rashad, A.M. Hassan, E.M. Elnaggar, M. Bechelany, Phys. Chem. Chem. Phys. 19, 6878–6886 (2017)CrossRef A.O. Turky, M.M. Rashad, A.M. Hassan, E.M. Elnaggar, M. Bechelany, Phys. Chem. Chem. Phys. 19, 6878–6886 (2017)CrossRef
7.
Zurück zum Zitat H.J. Noh, S.G. Lee, S.P. Nam, Y.H. Lee, Mater. Res. Bull. 45, 339–342 (2010)CrossRef H.J. Noh, S.G. Lee, S.P. Nam, Y.H. Lee, Mater. Res. Bull. 45, 339–342 (2010)CrossRef
8.
Zurück zum Zitat C. Sun Gyu, H. Tae-Jung, Y. Byoung-Gon, J. Seung Pil, O. Kwon, P. Hyung-Ho, Ceram. Int. 34, 2008, 833–836CrossRef C. Sun Gyu, H. Tae-Jung, Y. Byoung-Gon, J. Seung Pil, O. Kwon, P. Hyung-Ho, Ceram. Int. 34, 2008, 833–836CrossRef
9.
Zurück zum Zitat A.O. Turky, M.M. Rashad, A.T. Kandil, M. Bechelany, Phys. Chem. Chem. Phys. 17, 12553–12560 (2016)CrossRef A.O. Turky, M.M. Rashad, A.T. Kandil, M. Bechelany, Phys. Chem. Chem. Phys. 17, 12553–12560 (2016)CrossRef
10.
Zurück zum Zitat A.O. Turky, M.M. Rashad, M. Bechelany, Mater. Des. 90, 54–59 (2016)CrossRef A.O. Turky, M.M. Rashad, M. Bechelany, Mater. Des. 90, 54–59 (2016)CrossRef
11.
Zurück zum Zitat L.C. Costa, A. Aoujgal, M.P.F. Graca, N. Hadik, M.E. Achour, A. Tachafine, J.C. Carru, A. Oueriagli, A. Outzourit, Physica B 405, 3741–3744 (2010)CrossRef L.C. Costa, A. Aoujgal, M.P.F. Graca, N. Hadik, M.E. Achour, A. Tachafine, J.C. Carru, A. Oueriagli, A. Outzourit, Physica B 405, 3741–3744 (2010)CrossRef
12.
Zurück zum Zitat G.Z. Zhang, S.L. Jiang, Y.K. Zeng, Y.Y. Zhang, Q.F. Zhang, Y. Yu, High, J. Am. Ceram. Soc. 92, 3132–3134 (2009)CrossRef G.Z. Zhang, S.L. Jiang, Y.K. Zeng, Y.Y. Zhang, Q.F. Zhang, Y. Yu, High, J. Am. Ceram. Soc. 92, 3132–3134 (2009)CrossRef
13.
Zurück zum Zitat L. Xiaoa, K.-L. Choy, I. Harrisona, Surf. Coat. Technol. 205, 2989–2993 (2011)CrossRef L. Xiaoa, K.-L. Choy, I. Harrisona, Surf. Coat. Technol. 205, 2989–2993 (2011)CrossRef
14.
Zurück zum Zitat S.-Y. Chen, H.-W. Wang, L.-C. Huang, Jpn. J. Appl. Phys. 40, 4974 (2001)CrossRef S.-Y. Chen, H.-W. Wang, L.-C. Huang, Jpn. J. Appl. Phys. 40, 4974 (2001)CrossRef
15.
Zurück zum Zitat K. Hyun Yoon, J.Chan Lee, J. Park, D. Heon Kang, C. Moo Song, Y. Gyo Seo. Jpn. J. Appl. Phys. 40, 5497 (2001)CrossRef K. Hyun Yoon, J.Chan Lee, J. Park, D. Heon Kang, C. Moo Song, Y. Gyo Seo. Jpn. J. Appl. Phys. 40, 5497 (2001)CrossRef
17.
Zurück zum Zitat M. Jain, S.B. Majumder, R.S. Katiyar, Appl. Phys. Lett. 81, 3212 (2002)CrossRef M. Jain, S.B. Majumder, R.S. Katiyar, Appl. Phys. Lett. 81, 3212 (2002)CrossRef
18.
Zurück zum Zitat M. Yamaka, T. Kawahara, T. Makita, A. Yuuki, K. Ono, Jpn. J. Appl. Phys. 35, 729 (1996)CrossRef M. Yamaka, T. Kawahara, T. Makita, A. Yuuki, K. Ono, Jpn. J. Appl. Phys. 35, 729 (1996)CrossRef
20.
Zurück zum Zitat H.J. Chung, J.H. Choi, J.Y. Lee, S.I. Woo, Thin Solid Films 382, 106 (2001)CrossRef H.J. Chung, J.H. Choi, J.Y. Lee, S.I. Woo, Thin Solid Films 382, 106 (2001)CrossRef
21.
Zurück zum Zitat C.S. Hwang, B.T. Lee, C.S. Kang, J.W. Kim, K.H. Lee, H.J. Cho, H. Horii, W.D. Kim, S.I. Lee, Y.B. Roh, M.Y. Lee, J. Appl. Phys. 83, 3703 (1998)CrossRef C.S. Hwang, B.T. Lee, C.S. Kang, J.W. Kim, K.H. Lee, H.J. Cho, H. Horii, W.D. Kim, S.I. Lee, Y.B. Roh, M.Y. Lee, J. Appl. Phys. 83, 3703 (1998)CrossRef
22.
Zurück zum Zitat M.M. Rashad, A.O. Turky, A.T. Kandil, J. Mater. Sci. Mater. Electron. 24, 3284–3291 (2013)CrossRef M.M. Rashad, A.O. Turky, A.T. Kandil, J. Mater. Sci. Mater. Electron. 24, 3284–3291 (2013)CrossRef
23.
Zurück zum Zitat M.M. Rashad, E.M. Elsayed, M.S. Al-Kotb, A.E. Shalan, J. Alloy. Compd. 581, 71–78 (2013)CrossRef M.M. Rashad, E.M. Elsayed, M.S. Al-Kotb, A.E. Shalan, J. Alloy. Compd. 581, 71–78 (2013)CrossRef
24.
Zurück zum Zitat M. Rasly, M. Afifi, A.E. Shalan, M.M. Rashad, Appl. Phys. A 123, 331 (2017)CrossRef M. Rasly, M. Afifi, A.E. Shalan, M.M. Rashad, Appl. Phys. A 123, 331 (2017)CrossRef
25.
Zurück zum Zitat M.M. Rashad, S.M. Mahmoud, Z. Abdel-Hamid, H.M. El-Sayed, A.E. Shalan, N.A. Khalifa, A.T. Kandil, Part. Sci. Technol. 36, 172–177 (2018)CrossRef M.M. Rashad, S.M. Mahmoud, Z. Abdel-Hamid, H.M. El-Sayed, A.E. Shalan, N.A. Khalifa, A.T. Kandil, Part. Sci. Technol. 36, 172–177 (2018)CrossRef
26.
Zurück zum Zitat L. Xiao, K.-L. Choy, I. Harrison, Surf. Coat. Technol. 205, 2989–2993 (2011)CrossRef L. Xiao, K.-L. Choy, I. Harrison, Surf. Coat. Technol. 205, 2989–2993 (2011)CrossRef
27.
Zurück zum Zitat M. Liu, C. Ma, G. Collins, J. Liu, C. Chen, L. Shui, H. Wang, C. Dai, Y. Lin, J. He, J. Jiang, E.I. Meletis, Q. Zhang, Cryst. Growth Des. 10, 4221–4223 (2010)CrossRef M. Liu, C. Ma, G. Collins, J. Liu, C. Chen, L. Shui, H. Wang, C. Dai, Y. Lin, J. He, J. Jiang, E.I. Meletis, Q. Zhang, Cryst. Growth Des. 10, 4221–4223 (2010)CrossRef
28.
29.
Zurück zum Zitat X. Wang, S. Lv, C. Zhang, Q. Hu, L. Li, J. Alloys Compd. 576, 262–264 (2013)CrossRef X. Wang, S. Lv, C. Zhang, Q. Hu, L. Li, J. Alloys Compd. 576, 262–264 (2013)CrossRef
33.
34.
Zurück zum Zitat L.S. Cavalcante, J.C. Sczancoski, F.S. De Vicente, M.T. Frabbro, M.S. Li, J.A. Varela, E. Longo, J. Sol-Gel Sci. Technol. 49, 35–46 (2009)CrossRef L.S. Cavalcante, J.C. Sczancoski, F.S. De Vicente, M.T. Frabbro, M.S. Li, J.A. Varela, E. Longo, J. Sol-Gel Sci. Technol. 49, 35–46 (2009)CrossRef
35.
Zurück zum Zitat J. Wang, J. Xiang, S. Duo, W. Li, M. Li, L. Bai, J. Mater. Sci. Mater. Electron. 20, 319–322 (2009)CrossRef J. Wang, J. Xiang, S. Duo, W. Li, M. Li, L. Bai, J. Mater. Sci. Mater. Electron. 20, 319–322 (2009)CrossRef
36.
Zurück zum Zitat R. Thielsch, K. Kaemmer, B. Holzapfel, L. Schultz, Thin Solid Films 301, 203–210 (1997)CrossRef R. Thielsch, K. Kaemmer, B. Holzapfel, L. Schultz, Thin Solid Films 301, 203–210 (1997)CrossRef
37.
Zurück zum Zitat Y. Fan, S. Yu, R. Sun, L. Li, Y. Yin, K.W. Wong, R. Du, Appl. Surf. Sci. 256, 6531–6535 (2010)CrossRef Y. Fan, S. Yu, R. Sun, L. Li, Y. Yin, K.W. Wong, R. Du, Appl. Surf. Sci. 256, 6531–6535 (2010)CrossRef
38.
Zurück zum Zitat J. Liao, X. Wei, Z. Xu, X. Wei, P. Wang, Mater. Chem. Phys. 135, 1030–1035 (2012)CrossRef J. Liao, X. Wei, Z. Xu, X. Wei, P. Wang, Mater. Chem. Phys. 135, 1030–1035 (2012)CrossRef
39.
Zurück zum Zitat M.B. Gonzalez, A. Wu, P.M. Vilarinho, Chem. Mater. 18, 1737–1744 (2006)CrossRef M.B. Gonzalez, A. Wu, P.M. Vilarinho, Chem. Mater. 18, 1737–1744 (2006)CrossRef
40.
Zurück zum Zitat M.M. Rashad, D.A. Rayan, A.O. Turky, M.M. Hessien, J. Magn. Magn. Mater. 374, 359–366 (2015)CrossRef M.M. Rashad, D.A. Rayan, A.O. Turky, M.M. Hessien, J. Magn. Magn. Mater. 374, 359–366 (2015)CrossRef
Metadaten
Titel
Efficacious realization of Ba0.5Sr0.5TixM1−xO3 (M = Mn2+, Co2+) perovskite nanostructures through oxalate precursor strategy
verfasst von
Ali Omar Turky
Ahmed Esmail Shalan
Mohamed M. Rashad
Hailei Zhao
Mikhael Bechelany
Publikationsdatum
05.07.2018
Verlag
Springer US
Erschienen in
Journal of Materials Science: Materials in Electronics / Ausgabe 17/2018
Print ISSN: 0957-4522
Elektronische ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-018-9593-z

Weitere Artikel der Ausgabe 17/2018

Journal of Materials Science: Materials in Electronics 17/2018 Zur Ausgabe

Neuer Inhalt