18.08.2020 | ORIGINAL ARTICLE | Ausgabe 6/2020

Journal of Material Cycles and Waste Management 6/2020

Electrolysis using Pt/SS electrodes for aluminum recovery from drinking water treatment sludge

Zeitschrift:
Journal of Material Cycles and Waste Management > Ausgabe 6/2020
Autoren:
Rizkiy Amaliyah Barakwan, Wahyu Budi Pratiwi, Yulinah Trihadiningrum, Arseto Yekti Bagastyo
Wichtige Hinweise

Electronic supplementary material

The online version of this article (https://​doi.​org/​10.​1007/​s10163-020-01097-0) contains supplementary material, which is available to authorized users.

Publisher's Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Abstract

Alum sludge from the drinking water treatment plant (DWTP) of Surabaya City, Indonesia, potentially contains high aluminum and organic pollutant contents. Aluminum is sourced from the use of aluminum sulfate as a coagulant during the water treatment process. Whereas, the organic pollutant is from domestic and industrial wastewater discharges into the raw water source. Aims of this study were to characterize the alum sludge of the Surabaya DWTP, to determine suitable electrode materials and optimum electrical current for aluminum recovery using electrolysis. The sludge was characterized according to metal concentrations and chemical oxygen demand (COD). Cyclic voltammetry, a common method for determining appropriate electrode materials for electrolysis, was conducted to confirm platinum (Pt) and stainless steel A304 (SS A304) as suitable electrodes. A polarization test was applied to determine the current for electrolysis. Electrolysis using these electrodes was conducted in one compartment reactor for 6 h. The results showed that the sludge had high concentrations of aluminum and organic substance. The suitable anode and cathode in the electrolysis of acidified alum sludge at pH 3 were Pt and SS A304, respectively. Aluminum recovery efficiency was achieved at 300 mA (52.10%), in which metal impurities were low, and COD removal was 24%.

Bitte loggen Sie sich ein, um Zugang zu diesem Inhalt zu erhalten

Sie möchten Zugang zu diesem Inhalt erhalten? Dann informieren Sie sich jetzt über unsere Produkte:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Zusatzmaterial
Nur für berechtigte Nutzer zugänglich
Literatur
Über diesen Artikel

Weitere Artikel der Ausgabe 6/2020

Journal of Material Cycles and Waste Management 6/2020 Zur Ausgabe