Aluminum Deoxidation Equilibrium of Fe-Ni Alloy at 1773 K and 1873 K

The aluminum deoxidation equilibrium in molten Fe-36 mass pct Ni and Fe-46 mass pct Ni alloys was experimentally determined at 1773 K and 1873 K to obtain the thermodynamic parameters around the liquidus temperature, which is required to predict the deoxidation reaction for the ingot-casting process. Automatic SEM-EDS inclusion analysis was performed to estimate the undissolved oxygen content. Thermodynamic analysis on Al deoxidation was carried out using Miki and Hino’s formula, which is based on Darken’s quadratic formalism and the Redlich–Kister polynomial. From the composition dependence of the apparent equilibrium constant in Fe-Ni alloy, the necessity of the third-order interaction parameter of Ni-Al was found. Then, the interaction parameters of Fe-Al, Al-O and Ni-Al were evaluated.