Fatigue failure due to repetitive loading of metallic devices is a pervasive engineering concern. The present work reveals extraordinary fatigue resistance in nanocrystalline (NC) alloys, which appears to be associated with the small (<100 nm) grain size inhibiting traditional cyclic damage processes. In this study, we examine the fatigue performance of three electrodeposited NC Ni-based metals: Ni, Ni-0.5Mn, and Ni-22Fe (PERMALLOY). When subjected to fatigue stresses at and above the tensile yield strength where conventional coarse-grained (CG) counterparts undergo low-cycle fatigue failure (<104 cycles to failure), these alloys exhibit exceptional fatigue lives (in some cases, >107 cycles to failure). Postmortem examinations show that failed samples contain an aggregate of coarsened grains at the crack initiation site. The experimental data and accompanying microscopy suggest that the NC matrix undergoes abnormal grain growth during cyclic loading, allowing dislocation activity to persist over length scales necessary to initiate a fatigue crack by traditional fatigue mechanisms. Thus, the present observations demonstrate anomalous fatigue behavior in two regards: (1) quantitatively anomalous when considering the extremely high stress levels needed to drive fatigue failure and (2) mechanistically anomalous in light of the grain growth process that appears to be a necessary precursor to crack initiation.
Notes
U.S. GOVERNMENT WORK NOT PROTECTED BY U.S. COPYRIGHT
Manuscript submitted November 19, 2010.
1 Introduction
The origins of modern understanding of metal fatigue date back to the 1830s and 1840s when mine conveyor chain failures in Clausthal, Germany and a catastrophic locomotive axle failure in Versailles, France were linked to repetitive cyclic loading of metal components.[1] Since that time, researchers have been in search of metals that are either impervious or highly resistant to fatigue failure. The advent of nanocrystalline (NC) metals,[2] with their superior strength and hardness to conventional coarse-grained (CG) counterparts, offers the possibility of a new metallurgical pathway to improved fatigue performance.[3‐9] Indeed, published literature on the fatigue performance of NC metals clearly demonstrates improvements in fatigue strength over CG metals.[10‐15]
Aside from quantitative improvements in fatigue performance, NC metals also hold the possibility of new insight into the mechanisms responsible for traditional fatigue failure. In the recent past, studies on the monotonic strength of NC metals have not only revealed quantitative details regarding the Hall–Petch strengthening effect,[16‐18] but also led to the discovery of mechanistic transitions in dislocation behavior. For example, while individual dislocation slip is still active in NC metals with a grain size in the range of 20 to 50 nm,[4,19,20] there is insufficient space for the collective dislocation interaction mechanisms found in CG metals such as pileups and subgrain formation. Instead, deformation is governed by dislocation nucleation and absorption at grain boundaries.[19‐22] In large-grained metals, persistent slip bands (PSBs) are responsible for the formation of surface extrusions and intrusions, which are the precursor for fatigue crack initiation.[23] This process requires the collective activity of many dislocations within a grain, which the literature indicates should be on the order of hundreds of nanometers in size.[24] While other researchers have previously noted that crack initiation susceptibility typically decreases with decreasing grain size in metals,[25] we further postulate that the persistent slip mechanism responsible for conventional fatigue crack initiation may be suppressed when the grain size is below a certain threshold, likely on the order of 100 nm or several hundred nanometers. This length scale threshold is between grain sizes that support collective dislocation activity and grain sizes that support individual dislocation activity. However, a survey of the available literature on the fatigue of NC metals reveals that fatigue failure still occurs for NC metals, often with nothing more than a modest improvement in performance over CG metals.[26,27]
Advertisement
Perhaps the explanation for the lack of dramatic improvements in fatigue performance is related to the instability of NC grain structures, which are known to evolve even during storage at room temperature.[28] Previous experimental observations of NC grain growth during plastic deformation,[29,30] indentation experiments[31] and as a result of fatigue loading[14,32] warrant serious consideration. The grain growth reported by Witney etal.’s[14] fatigue experiments on NC Cu presumably refers to modest overall grain growth, rather than discontinuous local coarsening observed in monotonic loading experiments by Gianola et al.[29] In addition, several numerical models predicted evolution in NC grain structures under both elastic[33,34] and plastic[35‐37] deformation. These previous observations on room-temperature mechanically driven grain growth lead one to suspect that NC metals may evolve such coarse grain structures during fatigue loading, and that the fatigue mechanisms may be influenced more by the evolved grain structure than by the initial structure.
To investigate the relationship between deformation mechanisms and the fatigue behavior of NC metals, stress-life fatigue tests were performed on three Ni-based NC alloys with microstructural evaluation both before and after testing using focused ion beam (FIB) cross sectioning, electron backscattered diffraction (EBSD), and transmission electron microscopy (TEM).
2 Experimental Method
Three NC nickel alloys were fabricated by electrodeposition via the direct-LIGA lithographic micromolding process with varying solute content: nominally pure Ni deposited in a Watts bath,[38] Ni-22 wt pct Fe,[39] and Ni-0.5 wt pct Mn.[40] These alloys represent different metallurgical configurations: the Watts Ni contains only trace impurities, the Ni-0.5Mn alloy contains <1 pct alloying content,[41] while the Ni-Fe samples contain ≥20 pct alloying content. LIGA Ni alloys were deposited in a cantilever geometry for fatigue experiments (described in detail subsequently), while various dogbone specimens were also fabricated using similar dimensions for characterizing the stress-strain response. Dogbone-shaped Ni-Fe samples were electrodeposited separately in lithographically patterned molds for fatigue testing under pure tensile stresses. These dogbone samples were 10-μm thick with a gage length of 2000 μm and a gage width of 1000 μm.
As-deposited grain size distributions are shown in Figure 1, revealing that the average grain sizes of the alloys are 42 nm (Ni), 25 nm (Ni-22Fe), and 115 nm (Ni-0.5Mn). The inset in Figure 1(a) shows a grain size distribution from a NC Ni sample that was annealed at 523 K (250 °C) for 1 hour for comparison to the as-deposited materials. The largest grains in the as-deposited Ni and Ni-22Fe are ≤100 nm, while the largest grains in the as-deposited Ni-0.5Mn and annealed Ni are several hundred nanometers in size. Cross-sectional ion channeling imaging of the as-deposited grain structures for these three alloys showed homogeneous grain distributions with no evidence of grain inhomogeneity or bimodality. A representative image showing the field of view of these cross sections is given in Figure 2.
Fig. 1
Grain size distributions for as-deposited (a) Ni, (b) Ni-22Fe, and (c) Ni-0.5Mn. Inset in (a) shows distribution for annealed Ni sample, which was held at 250 °C for 1 h
Fig. 2
Representative as-deposited grain structure of Ni-0.5Mn. This low-magnification ion-channeling induced image of the cross section of a plated tensile bar highlights the homogeneity of the as-deposited grain structure. The other two alloys exhibited similar homogeneity in grain structure
×
×
Advertisement
In addition to initial and annealed grain size measurements, the crystallographic texture of the as-deposited material was also characterized by X-ray diffraction (XRD). The lattice parameter for the Ni-22Fe alloy was ~3.55 Å compared to ~3.52 Å for Ni and Ni-0.5Mn. This is consistent with larger atomic radii of Fe solute causing lattice expansion. (100), (110), and (111) pole figure intensities were collected for each material and integrated around the normal direction to present the textures as normalized intensity (multiple times random (MRD)) vs chi (χ), which is the angle measured from the sample normal (deposition direction), as shown in Figure 3. Nickel has an essentially random texture, while Ni-22Fe has a bimodal \( \left\langle {111} \right\rangle + \left\langle {100} \right\rangle \) fiber texture aligned with the deposition direction as well as a \( \left\langle {110} \right\rangle \) component at approximately 35 deg from the deposition direction. By contrast, Ni-0.5Mn has a \( \left\langle {110} \right\rangle \) texture aligned with the deposition direction.
Fig. 3
As-deposited crystallographic texture of (a) Ni, (b) Ni-22, and (c) Ni-0.5Mn as measured by XRD. Plots show pole intensity as a function of χ, the angle measured away from the sample normal (deposition) direction
×
Fatigue lifetime experiments of the LIGA Ni alloys were performed under fully reversed bending (R = σmin/σmax = –1) using a unique tapered cantilever geometry[42] producing constant peak surface stresses along a significant portion of the cantilever (Figure 4). In these lithographically patterned fatigue samples, the maximum bending stresses resulted in crack nucleation on the sidewalls of the deposition. These sidewall surfaces contained only very fine surface roughness features, on the order of the 100-nm scale of the grain size. Due to the small size of these samples (~26-μm beam width), no further attempts were made to electropolish the surfaces prior to fatigue testing. SEM imaging of sidewall crack initiation sites indicated that the native surface roughness was not a substantial contributor to crack initiation. Cyclic loading was performed under force control at a rate of 10 Hz using a custom built MTS servohydraulic loadframe with a 5 N loadcell. To investigate effects of different loading scenarios, a bending dwell test was also performed using the same bending geometry with hold times up to 3 weeks, as well as a set of Vickers dwell microindentation tests with hold times up to 8 hours. For comparison to bending fatigue experiments, tensile fatigue loading was performed on thin film Ni-Fe dogbone coupons using a piezoelectrically driven actuator capable of 1-μm resolution and a loading frequency of up to 30 Hz.
Fig. 4
(a) Secondary electron image of the as-fabricated fatigue specimen design with critical dimensions labeled. The 26- μm width tapered along the length of the gage section to produce a wide zone of constant maximum stress. (b) An elastic finite element model of the specimen configuration with an applied load of 10 mN. Image taken from Ref. 42
×
While fatigue testing was performed primarily on as-deposited material, in a separate study, each alloy was subjected to annealing treatments to determine the thermal stability of the grain structure. As-deposited samples underwent annealing in a vacuum of 10−3 torr for 1 hour at 473, 623, 773, or 923 K (200, 350, 500, or 650 °C). Grain structures were examined by making FIB cross sections and viewing under channeling ion imaging conditions. Average grain sizes for the annealing experiments were measured based on ASTM standard E 112.[43] The results of these measurements show that Ni-0.5Mn is significantly more resistant to thermally driven grain growth than either Ni or Ni-22Fe.
Postmortem microscopy was performed on fatigue samples using FIB milling and ion channeling imaging techniques using an FEI Nova1 600 Nanolab and FEI Helios2 Nanolab. Additionally, electron transparent foils were prepared using FIB milling and low keV cleaning for subsequent EBSD and TEM using a TECNAI3 F30 ST operating at 300 kV. FIB cross sections and TEM foils were cut normal to the deposition direction (i.e., the X-Y plane described in Figure 4).
3 Results
The results of fatigue lifetime experiments for NC Ni (yield strength, σy = 1300 MPa), Ni-0.5Mn (σy = 1200 MPa), and Ni-22Fe (σy = 1500 MPa) are plotted as stress-life or “S-N” curves in Figure 5. The 0.2 pct yield strengths and ultimate strengths of the alloys were determined previously from tensile samples fabricated using the LIGA process.[44] Figure 5(a) shows the number of cycles to failure as a function of the maximum stress in the fatigue cycle, whereas Figure 5(b) normalizes the maximum stress by the ultimate tensile strength. Tests in which the sample did not fail within ~107 cycles are indicated with arrows (so-called “runouts”). For comparison, Figure 5(a) includes shaded regions representing the range of fatigue behavior that exists in current conventional alloy classes.[45] The data demonstrate that the NC alloys exhibit exceptional resistance to fatigue failure. While conventional alloys typically fail within 104 to 106 cycles when loaded at peak stresses near the yield strength, the present NC alloys can exhibit lifetimes in excess of 107 cycles at peak stresses up to 25 pct above the nominal monotonic yield strength. This anomalous behavior is also apparent when scaling with the ultimate tensile strength (Figure 5(b)): while conventional Ni alloys have an endurance limit4 that is ~35 pct of the ultimate tensile strength,[42] the NC Ni alloy, for example, has an endurance limit that is 89 pct of the ultimate tensile strength. For comparison, the HCF behavior of electrodeposited Ni reported by Hanlon et al.[11] showed a scaled endurance limit of approximately 40 pct. Even without scaling, the fatigue performance of Ni and Ni-22Fe is extraordinary; at maximum stress levels of 1.5 GPa, these materials can survive up to 107 fatigue cycles.
Fig. 5
(a) Fatigue lifetime plot showing performance of three NC alloys compared to conventional metals.[45] (b) Ultimate strength normalized fatigue data for NC metals. All data in both plots were collected under fully reversed loading, R = –1, at 10 Hz
×
If the grain size is increased, however, the exceptional fatigue resistance is diminished. The Ni sample annealed at 250 °C was tested in fatigue and is shown as a solid circle data point in Figure 5(a). The grain size distribution of this annealed sample (inset Figure 1(a)) contains a substantial fraction of grains with diameters greater than 100 nm. At a peak stress amplitude of 1.5 GPa, the annealed Ni sample failed at 105 cycles, whereas the as-deposited material had a fatigue life of >107 cycles at this stress level.
Fatigued samples of all three alloys show characteristic features near the crack initiation site and are examined in greater detail using FIB and TEM cross sections as well as EBSD orientation mapping. Figure 6 shows examples of fracture surfaces for a failed Ni sample (Figure 6(a)) and a failed Ni-22Fe sample (Figure 6(b)). In the vicinity of near crack initiation, there is a rough, blocky fracture morphology that transitions to a smoother surface as the fatigue crack propagated away from the initiation zone. The micron-sized fractographic features in the initiation zone are much larger than the as-deposited grain size, indicating that the grain structure in the initiation zone is much different than the bulk grain structure. This is confirmed by FIB cross sectioning at each fracture initiation site. Typical grain structures from all three alloys are shown in Figure 7, with red arrows indicating aggregates of grains that have coarsened to micron-scale dimensions. White boxes in the Ni and Ni-22Fe sample indicate where EBSD orientation maps were later collected for analysis. The ion channeling conditions in Figure 7 produce contrast based on local grain orientation, and in all three materials, the as-deposited NC matrix can be seen surrounding the coarsened grain regions. Such aggregates were always found at crack initiation sites, forming groups of 10 to 30 grains spanning a region several microns in size. Also noteworthy are the elongated shapes of the coarse grains, which are most pronounced in the Ni-22Fe sample shown in Figure 7(b). The grains are elongated preferentially along the directions of maximum shear stress, implying that grain growth is strongly influenced by the shear component of the stress tensor. Two NC Ni samples (not shown) were also fatigued to the onset of crack initiation. Visual inspection and subsequent FIB cross sections confirmed coarse grains at the initiation site, providing additional supporting evidence of the clear tie between coarse grain formation and crack initiation.
Fig. 6
Representative fracture surfaces after fatigue failure of (a) Ni and (b) Ni-22Fe. The fracture surface is the lower right surface, and the specimen sidewall, which is the location of maximum fiber (bending) stress, is the top surface in this perspective. In both images, coarse micron-sized features are present at the site of crack initiation on the fracture surface
Fig. 7
Ion channeling induced images of large grains present near fatigue crack initiation sites in (a) Ni, (b) Ni-22Fe, and (c) Ni-0.5Mn. Images are shown at the same scale. Red arrows denote coarse grain aggregates at crack initiation sites. The white box indicates the location of EBSD analysis in the Ni and Ni-22Fe sample
×
×
To examine whether fatigue-induced grain growth in these alloys could also be induced by static loading, we prepared two additional experiments: a constant bending stress experiment for Ni-0.5Mn (the alloy which had the strongest propensity for fatigue-induced grain growth) and a sustained-load microindentation of all three NC alloys. The loading fixture from the fatigue experiments was used to apply a constant peak bending stress of 750 MPa to an as-deposited test specimen of Ni-0.5Mn for 20 days (10 continuous days at + 750 MPa and 10 days at –750 MPa). This represented comparable peak stress levels and overall time duration of the experimental conditions, which resulted in the formation of coarsened grains, as shown in Figure 7(c). After holding the stress at each peak (+/–) for 10 days, the sample was subsequently dissected using FIB cross sectioning to inspect for grain coarsening, but no evidence of grain growth was found. Vickers indentation was performed on all three alloys with a peak force of 0.5 N, held constant for 8 hours. FIB cross sections underneath the indentation marks in all three NC alloys also showed no evidence of coarsening beneath the indentation. These results suggest that the cyclic nature of the fatigue process was responsible for grain growth, rather than a static-loading mechanism.
To complement the bulk XRD texture measurements on undeformed material, EBSD measurements on deformed specimens describe the local orientation of the coarsened grain aggregates, providing insight into how the fatigue-driven growth process affects the evolution of local crystallographic texture. Figure 8 shows orientation maps for coarse grain aggregates in (a) Ni, (b) Ni-22Fe, and (c) Ni-0.5Mn along the deposition direction (Z). Coarsened Ni grains did not favor any particular orientation, mimicking the as-deposited untextured condition (Figure 3). Ni-0.5Mn coarse grains showed a preference for a \( \left\langle {110} \right\rangle \) orientation, again following the as-deposited texture. Ni-22Fe coarse grains, on the other hand, showed a strong \( \left\langle {110} \right\rangle \) orientation, which had been conspicuously absent from the as-deposited texture. In addition, along the principle stress (X) direction, those coarsened Ni-22Fe grains possessed a \( \left\langle {1\bar{1}2} \right\rangle \) orientation. This unique preferred texture only appeared in the coarsened Ni-22Fe grains.
Fig. 8
Grain orientation maps along the deposition (z) direction in fatigued (a) Ni, (b) Ni-22Fe, and (c) Ni-0.5Mn showing coarse grains in the fatigue crack initiation zone. The NC grain size in Ni and Ni-22Fe was too small to index using EBSD. The only sample that showed distinctly different texture in the coarse grains compared to the as-deposited state was Ni-22Fe
×
The cross-sectional EBSD map shown in Figure 8(c) was extracted from a region of distributed microcracks on the fatigue surface shown in Figure 9. More careful examination of the orientation of grain C (Figure 8(c)) reveals a \( \left\langle {111} \right\rangle \) orientation along the tensile axis (X) and a \( \left\langle {110} \right\rangle \) orientation along the deposition axis (Z). Using the EBSD orientation information coupled with the morphology of the surface persistent slip extrusions, a Thompson tetrahedron can be used to confirm that the most highly stressed slip system is responsible for the surface extrusions. Figure 9 illustrates this analysis, indicating that the slip system indicated by a red arrow is on a {111} plane coincident with the extrusion plane lying at 30 deg to the tensile axis. The crack initiates in this CG region on slip extrusions that are crystallographically dictated, and as the crack begins to propagate, it reorients to the preferred mode-I crack path.
Fig. 9
(above) Isometric view of the crack initiation surface of the Ni-0.5Mn sample corresponding to the EBSD map shown in Fig. 8(c). (below) Cross-sectional EBSD maps of grain C confirm that {111} planes coincide with extruded material located at the arrow marked “PSB” in the top view. The red arrow indicates the most likely slip direction to promote persistent slip
×
The CG crack initiation region of the Ni sample shown in Figures 7(a) and 8(a) was harvested for TEM analysis to examine the grain growth and cyclic deformation processes in more detail. In Figure 10(a), the original NC matrix of the Ni sample can be seen surrounding two coarse grains (labeled A and B in both Figures 8 and 10). Moderate grain growth was also observed along the crack wake (indicated by arrows in Figure 10(a)), possibly due to the high but transient stress field associated with the propagating crack front. Figure 11(b) shows a higher magnification view of the region shown by a white box in (a). Dislocations, indicated by arrows in grain A (Figure 10(b)), are accompanied by several small, isolated subgrains (indicated by circles), which are engulfed by the coarse grain. The subgrains have a close orientation relationship (<3 deg misorientation) to the encompassing coarse grain based on selected area diffraction patterns. The low energy nature of these boundaries explains why they would persist after absorption by the growing grain. Last, the far left boundary of grain A has a scalloped shape, indicating that the boundary maintained a distinct mobility advantage over its neighbors throughout the growth process.[46,47]
Fig. 10
TEM micrographs of Ni coarsened grains; rotated to maintain the same X-Y coordinates as in Fig 9(a). (a) Bright-field imaging condition showing coarse grain aggregate embedded in the NC parent matrix. Moderate grain growth (indicated by arrows) is evident in the crack wake. (b) Detail of area marked in (a) showing dislocations in the grain interior (arrows), an irregular boundary (highlighted on the left), and several included grains (black circles), which are oriented within 3 deg to the parent grain
Fig. 11
TEM cross sections of (a) NC Ni-20Fe tensile fatigue sample showing coarse grains at the crack initiation site and (b) annealed Ni-20Fe fatigue sample showing PSBs (black and white arrows) in microcrystalline grains. Red arrows note locations where dislocation ladders intersect the surface
×
×
TEM micrographs of fatigued Ni-Fe tensile coupons are shown in Figure 11, showing the coarse grain aggregate at the crack initiation site. Evidence of CG aggregates in tension-tension fatigue is important, because it demonstrates that the mechanism is not dependent on the specific stress state of the test sample, as the NC LIGA samples were tested under fully reversed bending. Several of the tensile coupons were annealed at various temperatures to grow the grains and probe the fatigue behavior. One sample is shown in the cross section in Figure 11(b). This sample was annealed at 650 °C for 1 hour (resulting in grain sizes >>1 μm) and shows traditional dislocation ladder structures associated with persistent slip in the microcrystalline grains near the crack wake. These collective dislocation structures occur over micron-scale dimensions and intersect the top surface of the sample at the locations shown by red arrows. At these locations, the top surface of the grain exhibits marked surface depressions, or so-called “intrusions,” coincident with the dislocation pileups. The micron length scale of the dislocation structures emphasizes the fact that truly NC grains cannot support persistent slip, because they are not large enough to contain such arrangements.
4 Discussion
The preceding results establish several important facts, the first of which is that these NC Ni alloys possess exceptional fatigue resistance, with S-N behavior far exceeding existing commercial alloys. The endurance limit of NC Ni and Ni-22Fe is quantitatively anomalous when scaled by the ultimate strength: whereas conventional Ni and its alloys typically have an endurance limit that is ~35 pct of the ultimate tensile strength, the Ni and Ni-22Fe alloys presented here exhibit endurance limits >60 pct of the ultimate tensile strength. The average grain size of these alloys is well below 100 nm, and when stress levels are raised enough to cause failure, the fatigue process results in grain growth associated with crack initiation. TEM analysis of coarse grains suggests that the length scale of traditional dislocation-based mechanisms such as PSBs requires several hundreds of nanometers or even microns to operate. The fatigue behavior of these alloys represents an interruption of traditional fatigue failure processes analogous to the breakdown in Hall–Petch scaling associated with transitions in dislocation mechanisms.[18]
The importance of small grain size in achieving high fatigue performance is demonstrated most clearly by comparing the performance of NC Ni and NC Ni-22Fe to the Ni-0.5Mn and annealed Ni alloys. While the maximum grain sizes of the former are approximately 150 and 75 nm, respectively, the Ni-0.5Mn and annealed Ni alloys contain grains several hundred nanometers in size. Grains this large located in regions of maximum stress would be more susceptible to persistent slip because of their ability to sustain collective dislocation structures necessary to form surface intrusions and extrusions. A more subtle point is that both the Ni-0.5Mn alloy and annealed Ni fatigue samples showed distributed microcracking, whereas the NC Ni and NC Ni-22Fe only contained a single crack. The presence of multiple microcracks points to the fact that many regions in the material were similarly susceptible to crack initiation. While the NC grained materials may suppress the traditional crack initiation process, this fine grain structure offers little resistance to subsequent crack propagation. Once a single crack initiated in a NC alloy, the flaw would propagate and cause failure before any other coarsening and initiation could occur.
The present observations also suggest that grain stability is an important factor affecting the crack initiation and propagation process in these NC alloys. The schematic shown in Figure 12 describes a conceptual process leading to crack initiation in these NC metals. Material with an initial grain size distribution below ~100 nm undergoes (a) cyclic loading, which leads to the growth of an aggregate of large grains (b). These coarse grains are large enough to support the to-and-fro motion of dislocations without the interference of grain boundaries, which allows PSBs (c) to initiate a crack (d). Once the fatigue crack has grown through the coarse grains, it propagates unencumbered through the NC matrix due to limited crack-tip plasticity and tortuosity.[4,12] This model of the fatigue process implies that improvements in fatigue performance of NC metals hinges on stabilizing the grain boundaries against this growth process.
Fig. 12
Schematic illustrating the apparent fatigue-crack initiation mechanism observed in these NC Ni-based alloys. (a) Cyclic fatigue stresses are applied to a homogeneous NC starting grain structure, (b) localized clusters of coarsened grains are formed at the surface of maximum stress, (c) traditional persistent slip processes can proceed in coarsened grains, and (d) a fatigue crack initiates in the coarsened grains and propagates into the parent NC material. A modest degree of coarsening can be observed on the flanks of the propagating crack
×
4.1 Adiffusional Grain Growth
Grain growth is typically thought of as a diffusive thermally activated process. Most metals and alloys are stable at low homologous temperatures due to limited diffusional boundary mobility, which decreases exponentially with decreasing temperature.[48] An estimate of grain boundary velocity supports this assertion: in aluminum,[49] for example, the estimated velocity of nanoscale grain boundaries drops from 40 μm/s at 0.7Tm to only 10−9 μm/s at room temperature.
The existence of athermal grain growth in NC metals is supported by observation of coarsening at cryogenic temperatures[31] and by many other observations at ambient temperatures.[14,28,29,50,51] Molecular dynamics studies on Ni grain boundaries has predicted that ~25 pct of the grain boundary types can undergo nonthermally activated motion.[52] In the present investigation, there is indirect evidence that athermal coarsening may be present in the NC Ni alloys; of the three alloys considered in this study, the Ni-0.5Mn exhibited the least resistance to fatigue-induced grain growth even though this same alloy showed the best resistance to annealing-induced grain growth.
Stress-driven boundary motion has been observed experimentally,[29‐31,50,53,54] as well as predicted by simulations[33,34] and theory.[55] Recent experimental results by Rupert et al.[30] confirmed much of this theory in NC aluminum, although for monotonic tensile stresses. Independent simulations[33] predict that elastic stresses result in a significant driving force for boundary motion even greater than if plasticity occurs concomitantly. In such cases, stored elastic strain energy can exceed the local curvature driving force, resulting in rippled boundaries during grain growth, qualitatively similar to the wavy grain boundary shown in Figure 10. The elongated nature of the grains along directions of maximum shear, most evident in the Ni-22Fe example in Figure 8(b), is further evidence indicating that the shear component of the stress tensor is important to the coarsening process.
The observed mechanically induced grain growth process may be related to the well-known process of dynamic recrystallization (DRX); however, there are several features of the microstructural evolution that distinguish the observed phenomenon from DRX. Grains that have dynamically recrystallized have been observed due to high temperature fatigue in Ni,[56] with similar boundary shapes (serrated grain boundaries and preferential growth along planes of maximum shear stress). However, the present experiments were run at room temperature (homologous temperature T < 0.2Tmp), whereas previous work on the DRX process is associated with much higher homologous temperatures (T > 0.4Tmp). Dynamic recrystallization also typically involves the nucleation of new grains through the formation of high-angle subgrain boundaries. This process necessarily involves the formation of dislocation cells, a collective process that is not possible due to the extremely fine starting grain size of these Ni alloys. Therefore, the presently observed room-temperature fatigue-induced grain evolution appears fundamentally distinct from the DRX process.
Well-established metallurgical principles of grain stabilization against normal grain growth suggest that the incorporation of either pinning particles or solute content will impede boundary motion; however, current research on this exact phenomenon in NC metals suggests something quite different, that solute encourages abnormal grain growth.[57] The three alloys examined in this study represent three distinct metallurgical scenarios in this regard: Ni with only impurity content, Ni-0.5Mn with a small solute content, and Ni-22Fe with a large solute content. Ordering of these metals by alloy content, however (Ni, Ni-0.5Mn, Ni-22Fe), does not correspond to their vulnerability to fatigue-induced coarsening (Ni-0.5Mn, Ni-22Fe/Ni). More detailed analysis of the effect of impurity content, which is beyond the scope of the work presented here, may shed light on this issue.
Grain orientation can also have profound effects on growth behavior,[52,58] from elastic mismatch accentuating the elastic driving force[33] to causing local variations in boundary mobility.[59] Comparison between the as-deposited and evolved coarse grain textures reveals that while Ni and Ni-0.5Mn coarse grains maintain the parent texture, Ni-22Fe coarse grains develop a preferred \( \left\langle {110} \right\rangle \) texture along the Z direction, which is notably absent from the as-deposited texture (Figure 3). In the NC Ni and Ni-0.5Mn alloys, texture does not appear to play as strong a role in the boundary mobility. Inspection of the EBSD patterns for the Ni-22Fe coarsened grains also reveals that the grains have the \( \left\langle {1\bar{1}2} \right\rangle \) pole aligned with the stress axis (X direction). This texture happens to be the well-known orientation that any fcc single crystal rotates toward during uniaxial deformation[60] to take full advantage of available slip systems. NC grains in these experiments would behave quite differently than a single crystal under uniaxial tension, although collective grain rotation was observed in both experiments and simulation.[7,35,61‐64] Evidence of this is suggested by the grain orientation map for Ni-22Fe (Figure 8(b)). Examination of the elongated coarse grains reveals that they contain several low-angle sub-boundaries, which may be remnants of smaller grains. This structure is reminiscent of a mechanism suggested by experiments[7] and simulation[61,65] in which neighboring grains under an external stress rotate to a common orientation, eliminating high-angle grain boundaries between them and allowing collective dislocation mechanisms to occur. Unfortunately, a clear conclusion on this topic cannot yet be drawn from the available data, and additional work is needed to identify the precise mechanism of fatigue-induced grain growth in all three alloys.
4.2 Future Work
There are several questions that these experiments raise that cannot yet be fully answered. One issue is whether locally coarsened grains form in uncracked specimens. The presence of cracks provides a fiduciary mark pointing to the location of coarse grain regions, but without such a means to find these grains, the search for CG aggregates becomes a “needle-in-a-haystack” exercise. In an effort to survey large regions of material for coarsening prior to failure, other methods of inspection are possible including the use of XRD. Such a study, however, is beyond the scope of this work. Another question to be answered by additional research is whether there is a threshold stress amplitude below which the coarsening process does not occur. The present results do suggest the existence of such a threshold for grain growth; such a threshold stress may be the source of the observed endurance limit in the absence of dislocation-induced thresholds. Further study is also necessary to understand why cyclic loading drives the growth process, while similar levels of static stresses do not. There is experimental evidence of cyclically driven local coarsening in ultra-fine-grained Cu[66] and NC-twinned Cu;[32] however, in those cases, there was no evidence of anomalous fatigue performance. In neither this study nor other local coarsening studies does there emerge a clear mechanism distinction between cyclically driven and monotonically driven coarsening.
5 Conclusions
In conclusion, we have examined three NC Ni alloys in high-cycle fatigue and found evidence of exceptional, quantitatively anomalous performance. The most striking result is the apparent suppression of fatigue crack nucleation and failure by prevention of collective dislocation slip through the preservation of a NC grain structure. In cases when the stress is increased, leading to failure, thorough examination reveals that crack initiation is always preceded by the formation of a region of highly coarsened grains. Postmortem microscopy of these coarsened regions appears consistent with published literature, which suggests an adiffusional shear stress driven growth process. Analysis of several fatigued samples indicates a potential mechanism for fatigue failure in which grains coarsen to a size that supports collective dislocation activity, allowing PSBs to initiate a fatigue crack. Once the crack traverses the tougher, coarsened grains, the less ductile NC matrix presents little propagation resistance.
Acknowledgments
The authors thank Drs. T.R Christensen and S.H. Goods for supplying the various electroplated alloys used in this investigation, as well as Dr. E.A. Holm for helpful discussions and guidance regarding grain growth phenomenon. The authors also thank Dr. P.G. Kotula, Dr. B.G. Clark, Dr. J.R. Michael, M. Rye, and B. McKenzie for electron microscopy support, as well as Dr. M. Rodriguez for XRD support. This work was performed, in part, at the Center for Integrated Nanotechnologies, a United States Department of Energy, Office of Basic Energy Sciences, user facility. This work was funded by the United States Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering. Sandia is a multiprogram laboratory operated by Sandia Corporation, a Lockheed Martin Company, for the United States Department of Energy’s National Nuclear Security Administration under Contract No. DE-AC04-94AL85000.
Open Access This is an open access article distributed under the terms of the Creative Commons Attribution Noncommercial License (
https://creativecommons.org/licenses/by-nc/2.0