Curing behavior and bonding strength of two-component fast-setting adhesives prepared with phenol-liquefied Cryptomeria japonica wood

Journal:
European Journal of Wood and Wood Products > Issue 5/2018
Authors:
Yen-Chun Chen, Wen-Jau Lee
Important notes

Publisher’s Note

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Abstract

Honeymoon adhesive is a special adhesive system that contains two components which are applied onto two substrates separately for glulam manufacturing to provide a fast-setting capability. It has been confirmed that phenol-liquefied wood can be used as a raw material for preparing phenolic resins. In this study, liquefied wood (LW) was obtained by liquefying Cryptomeria japonica wood in phenol with sulfuric acid as a catalyst. Resorcinol–formaldehyde resin (RF), phenol-resorcinol–formaldehyde resins (PRF), LW–PF and LW–PRF (synthesized using LW as a raw material), and RF/LW and RF/LW–PF (blended RF with LW and LW–PF) were prepared. The properties such as non-volatile content, pH, viscosity gelation time and DSC curing behavior of these resins were measured. The results show all resins can be cured at room temperature when paraformaldehyde is added as a hardener, except for the LW–PF. The honeymoon adhesive was prepared by using RF and PRF that contains 10% paraformaldehyde as the A-component and LW–PRF, RF/LW and RF/LW–PF without paraformaldehyde as the B-component. After mixing the A-component and B-component, the gelation time of RF and PRF can be shortened. The glued lumber was prepared by separately applying the A-component and B-component on the surface of two wood strips and combining them. The result shows using RF/LW–PF as the B-component has faster bonding strength development than others. When PRF and RF are used as the A-component, they have a bonding strength of over 5.4 MPa, the requirement of CNS 11031 standard for the glued lumber of C. japonica, at pressing times of 2 and 4 h, respectively.

Please log in to get access to this content

To get access to this content you need the following product:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 58.000 Bücher
  • über 300 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literature
About this article

Other articles of this Issue 5/2018

European Journal of Wood and Wood Products 5/2018 Go to the issue