Dynamic Recrystallization in Cu-Cr-Zr-Ti Alloy Under Large Plane Strain Conditions

Authors: Aditya Sarkar, S. V. S. Narayana Murty, M. J. N. V. Prasad

Published in: Metallurgical and Materials Transactions A | Issue 9/2020

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The Cu-Cr-Zr-Ti alloy was subjected to single-hit plane strain compression tests in the temperature range of 923 K to 1073 K (650 °C to 800 °C) and at two different strain rates of 0.1 and 1 s−1. These tests were performed to ascertain the kinetics of microstructural evolution resulting by dynamic recrystallization (DRX) in the alloy under hot deformation conditions. The differences in the extent of DRX under various deformation conditions were established by plotting fractional softening as a function of strain and time. Further, the Avrami exponent was found to decrease with increase in deformation temperature. This was attributed to early onset of recrystallization leading to subsequent work hardening of the recrystallized grains and grain growth at higher temperatures which results in the loss of nucleation sites due to reduced grain boundary area. Microstructural observations made using optical microscopy, scanning electron microscopy (SEM), and electron backscattered diffraction (EBSD) revealed nucleation to occur in the following steps: elongation of grains perpendicular to the compression direction, bulging of elongated grain boundaries due to strain-induced boundary migration (SIBM), and subsequent subgrain formation behind the bulged boundary due to strain-induced low-angle boundaries. Finally, the equation describing the DRX kinetics under plane strain conditions for the alloy was established as \( X = 1 - \exp \left[ { - 0.455 \times \left( {{{\left( {\varepsilon - \varepsilon_{\text{c}} } \right)} \mathord{\left/ {\vphantom {{\left( {\varepsilon - \varepsilon_{\text{c}} } \right)} {\varepsilon_{\text{p}} }}} \right. \kern-0pt} {\varepsilon_{\text{p}} }}} \right)^{2.84} } \right] \).

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literature
1.
go back to reference C.M. Sellars, W.J. McG. Tegart, International Metallurgical Reviews 1972, vol. 17, pp. 1-24.CrossRef C.M. Sellars, W.J. McG. Tegart, International Metallurgical Reviews 1972, vol. 17, pp. 1-24.CrossRef
2.
go back to reference J. Jonas, C. M. Sellars, W. J. McG. Tegart, Metallurgical Reviews, 1969, vol. 14, pp. 1-24. J. Jonas, C. M. Sellars, W. J. McG. Tegart, Metallurgical Reviews, 1969, vol. 14, pp. 1-24.
3.
go back to reference H.J. McQueen, N.D. Ryan, Materials Science and Engineering A, 2002, vol. 322, pp. 43-63.CrossRef H.J. McQueen, N.D. Ryan, Materials Science and Engineering A, 2002, vol. 322, pp. 43-63.CrossRef
5.
go back to reference Y.V.R.K. Prasad, H.L. Gegel, S.M. Doraivelu, J.C. Malas, J.T. Morgan, K.A. Lark, D.R. Barker, Metallurgical Transactions A, 1984, vol. 15, pp. 1883-1892.CrossRef Y.V.R.K. Prasad, H.L. Gegel, S.M. Doraivelu, J.C. Malas, J.T. Morgan, K.A. Lark, D.R. Barker, Metallurgical Transactions A, 1984, vol. 15, pp. 1883-1892.CrossRef
6.
go back to reference T. Sakai, A. Belyakov, R. Kaibyshev, H. Miura, J.J. Jonas, Progress in Materials Science, 2014, vol. 60, pp. 130–207.CrossRef T. Sakai, A. Belyakov, R. Kaibyshev, H. Miura, J.J. Jonas, Progress in Materials Science, 2014, vol. 60, pp. 130–207.CrossRef
7.
8.
go back to reference Y. Zhang, H. Sun, A. A. Volinsky, B. Tian, Z. Chai, P. Liu, Acta Metallurgica Sinica 2016, vol. 29, pp. 422–430.CrossRef Y. Zhang, H. Sun, A. A. Volinsky, B. Tian, Z. Chai, P. Liu, Acta Metallurgica Sinica 2016, vol. 29, pp. 422–430.CrossRef
9.
go back to reference Y. Zhang, Z. Chai, A. A. Volinsky, B. Tian, H. Sun, P. Liu, Y. Liu, Materials Science & Engineering A, 2016, vol. 662, pp. 320–329.CrossRef Y. Zhang, Z. Chai, A. A. Volinsky, B. Tian, H. Sun, P. Liu, Y. Liu, Materials Science & Engineering A, 2016, vol. 662, pp. 320–329.CrossRef
10.
go back to reference Y. Zhang, Z. Chai, A. A. Volinsky, H. Sun, B. Tian, P. Liu, Y. Liu, Journal of Materials Engineering and Performance, 2016, vol. 25, pp. 1191-1198.CrossRef Y. Zhang, Z. Chai, A. A. Volinsky, H. Sun, B. Tian, P. Liu, Y. Liu, Journal of Materials Engineering and Performance, 2016, vol. 25, pp. 1191-1198.CrossRef
11.
go back to reference H. Zhang, J. Wang, Q. Chen, D. Shu, C. Wang, G. Chen, Z. Zhao, Journal of Alloys and Compounds, 2019, vol. 784, pp. 1071-1083CrossRef H. Zhang, J. Wang, Q. Chen, D. Shu, C. Wang, G. Chen, Z. Zhao, Journal of Alloys and Compounds, 2019, vol. 784, pp. 1071-1083CrossRef
12.
go back to reference I. S. Batra, G. K. Dey, U. D. Kulkarni, S. Banerjee, Journal of Nuclear Materials, 2001, vol. 299, pp. 91-100.CrossRef I. S. Batra, G. K. Dey, U. D. Kulkarni, S. Banerjee, Journal of Nuclear Materials, 2001, vol. 299, pp. 91-100.CrossRef
13.
go back to reference I. S. Batra, G. K. Dey, U. D. Kulkarni, S. Banerjee, Materials Science & Engineering A, 2002, vol. 356, pp. 32-36.CrossRef I. S. Batra, G. K. Dey, U. D. Kulkarni, S. Banerjee, Materials Science & Engineering A, 2002, vol. 356, pp. 32-36.CrossRef
14.
go back to reference G. Sudarshan-Rao, V. M. J. Sharma, S.G. Sundara-Raman, M. Amruth, P. Ramesh-Narayanan, S. C. Sharma, P.V. Venkitakrishnan, Materials Science & Engineering A, 2016, vol. 668, pp. 97–104.CrossRef G. Sudarshan-Rao, V. M. J. Sharma, S.G. Sundara-Raman, M. Amruth, P. Ramesh-Narayanan, S. C. Sharma, P.V. Venkitakrishnan, Materials Science & Engineering A, 2016, vol. 668, pp. 97–104.CrossRef
15.
go back to reference G. Sudarshan-Rao, J. Srinath, S. G. Sundara-Raman, V.M.J. Sharma, S.V.S. Narayana-Murty, P. Ramesh-Narayanan, K. Thomas-Tharian, P. Ram-Kumar, P.V. Venkitakrishnan, Materials Science & Engineering A, 2017, vol. 692 pp. 156–167.CrossRef G. Sudarshan-Rao, J. Srinath, S. G. Sundara-Raman, V.M.J. Sharma, S.V.S. Narayana-Murty, P. Ramesh-Narayanan, K. Thomas-Tharian, P. Ram-Kumar, P.V. Venkitakrishnan, Materials Science & Engineering A, 2017, vol. 692 pp. 156–167.CrossRef
16.
go back to reference S. Chenna-Krishna, G. Sudarsana-Rao, A. K. Jha, B Pant, P.V. Venkitakrishnan, Materials Science & Engineering A 674 (2016) 164–170.CrossRef S. Chenna-Krishna, G. Sudarsana-Rao, A. K. Jha, B Pant, P.V. Venkitakrishnan, Materials Science & Engineering A 674 (2016) 164–170.CrossRef
17.
go back to reference P. Zhang, J. Jie, Y. Gao, T. Wang, T. Li, Materials Science Forum, 2015, vol. 817, pp. 307-311.CrossRef P. Zhang, J. Jie, Y. Gao, T. Wang, T. Li, Materials Science Forum, 2015, vol. 817, pp. 307-311.CrossRef
18.
go back to reference A. Sarkar, S.V.S. Narayana-Murty, M.J.N.V. Prasad, Materials Performance and Characterization, 2019, vol. 8, pp. 1076–1090. A. Sarkar, S.V.S. Narayana-Murty, M.J.N.V. Prasad, Materials Performance and Characterization, 2019, vol. 8, pp. 1076–1090.
19.
go back to reference A. Sarkar, M.J.N.V. Prasad, S.V.S. Narayana-Murty, Materials Characterization, 2020, vol. 160, 110-112.CrossRef A. Sarkar, M.J.N.V. Prasad, S.V.S. Narayana-Murty, Materials Characterization, 2020, vol. 160, 110-112.CrossRef
20.
go back to reference S.V.S. Narayana-Murty, B. Nageswara-Rao, B.P. Kashyap, International Materials Reviews, 2000, vol. 45, pp. 15-26.CrossRef S.V.S. Narayana-Murty, B. Nageswara-Rao, B.P. Kashyap, International Materials Reviews, 2000, vol. 45, pp. 15-26.CrossRef
21.
go back to reference S.V.S. Narayana-Murty, A. Sarkar, P. Ramesh-Narayanan, P.V. Venkitakrishnan, J. Mukhopadhyay, Materials Science & Engineering A, 2016, vol. 677, pp. 41–49.CrossRef S.V.S. Narayana-Murty, A. Sarkar, P. Ramesh-Narayanan, P.V. Venkitakrishnan, J. Mukhopadhyay, Materials Science & Engineering A, 2016, vol. 677, pp. 41–49.CrossRef
22.
23.
go back to reference H. Mirzadeh, A. Najafizadeh, Materials and Design, 2010, vol. 31, pp.1174–1179.CrossRef H. Mirzadeh, A. Najafizadeh, Materials and Design, 2010, vol. 31, pp.1174–1179.CrossRef
24.
25.
26.
go back to reference D. Qian, Y. Peng, Journal of Materials Engineering and Performance, 2015, vol. 24, pp. 1906-1917.CrossRef D. Qian, Y. Peng, Journal of Materials Engineering and Performance, 2015, vol. 24, pp. 1906-1917.CrossRef
27.
go back to reference J. J. Jonas, X. Quelennec, L. Jiang, E. Martin, Acta Materialia, 2009, vol. 57, pp. 2748–2756.CrossRef J. J. Jonas, X. Quelennec, L. Jiang, E. Martin, Acta Materialia, 2009, vol. 57, pp. 2748–2756.CrossRef
28.
go back to reference M. El Wahabi, L. Gavard, F. Montheillet, J.M. Cabrera, J.M. Prado, Acta Materialia, 2005 vol. 53, pp. 4605–4612.CrossRef M. El Wahabi, L. Gavard, F. Montheillet, J.M. Cabrera, J.M. Prado, Acta Materialia, 2005 vol. 53, pp. 4605–4612.CrossRef
29.
go back to reference A.M. Wusatowska-Sarnek, H. Miura, T. Sakai, Materials Science & Engineering A, 2002, vol. 323, pp. 177–186.CrossRef A.M. Wusatowska-Sarnek, H. Miura, T. Sakai, Materials Science & Engineering A, 2002, vol. 323, pp. 177–186.CrossRef
30.
go back to reference B. Verlinden, J. Driver, I. Samajdar, R. D. Doherty, R. W. Cahn (Editor), Thermo-mechanical processing of metallic materials, Pergamon Mater. Ser., 2007, pp. 168–77. B. Verlinden, J. Driver, I. Samajdar, R. D. Doherty, R. W. Cahn (Editor), Thermo-mechanical processing of metallic materials, Pergamon Mater. Ser., 2007, pp. 168–77.
31.
go back to reference S. Suwas, R.K. Ray, B. Derby (Series Editor), Crystallographic Texture of Materials, Springer Engineering Materials and Processes Series, 2014, pp. 109–113. S. Suwas, R.K. Ray, B. Derby (Series Editor), Crystallographic Texture of Materials, Springer Engineering Materials and Processes Series, 2014, pp. 109–113.
32.
go back to reference F.J. Humphreys, M. Hatherly, Recrystallization and related annealing phenomena, 2nd edition, 2014, Elsevier, Amsterdam, pp. 68-72. F.J. Humphreys, M. Hatherly, Recrystallization and related annealing phenomena, 2nd edition, 2014, Elsevier, Amsterdam, pp. 68-72.
Metadata
Title
Dynamic Recrystallization in Cu-Cr-Zr-Ti Alloy Under Large Plane Strain Conditions
Authors
Aditya Sarkar
S. V. S. Narayana Murty
M. J. N. V. Prasad
Publication date
01-07-2020
Publisher
Springer US
Published in
Metallurgical and Materials Transactions A / Issue 9/2020
Print ISSN: 1073-5623
Electronic ISSN: 1543-1940
DOI
https://doi.org/10.1007/s11661-020-05892-0

Other articles of this Issue 9/2020

Metallurgical and Materials Transactions A 9/2020 Go to the issue

Metallurgical and Materials Transactions 50th Anniversary Collection

Grain Refinement of Alloys in Fusion-Based Additive Manufacturing Processes

Premium Partners