04-03-2020 | Research Paper | Issue 2/2020

Acta Mechanica Sinica 2/2020

Effect of interfacial delamination on coating crack in thick diamond-like carbon coatings under indentation

Journal:
Acta Mechanica Sinica > Issue 2/2020
Authors:
Zhongbao Wang, Xiangli Zhong, Limei Jiang, Fugang Qi, Xiaoping Ouyang, Jinbin Wang, Bin Liao, Jun Luo

Abstract

Coating crack and interfacial delamination are recognized as two critical factors inducing spallation of thick diamond-like carbon (DLC) coatings. The effect of the two factors is found to dramatically accelerate the failure of thick DLC coatings. However, there are few reports on the effect of interfacial delamination on coating crack. In this work, in order to investigate the evolution of the coating crack and interfacial delamination, as well as the effect of interfacial delamination on coating crack, a finite element model that combines the bilinear cohesive zone model and the extended finite element method (XFEM) is established. It is found that the occurrence of interfacial delamination triggers a second expansion of coating crack. Factors influencing the degree of interfacial delamination on coating crack can be modulated by coating thickness and coating elastic modulus. As the coating thickness increases, the length of interfacial delamination increases, and thus the propagation of coating crack is accelerated. In contrast, the increase of coating elastic modulus could reduce the length of interfacial delamination, which consequently weakens its influence on the propagation of coating crack.

Please log in to get access to this content

To get access to this content you need the following product:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 69.000 Bücher
  • über 500 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Testen Sie jetzt 30 Tage kostenlos.

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 50.000 Bücher
  • über 380 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Umwelt
  • Maschinenbau + Werkstoffe




Testen Sie jetzt 30 Tage kostenlos.

Literature
About this article

Other articles of this Issue 2/2020

Acta Mechanica Sinica 2/2020 Go to the issue

Premium Partners

    Image Credits