Effect of Shock and Vibration Preloading on the Deformation and Fracture Behavior of 17G1S-U Steel

Authors: P. O. Marushchak, M. G. Chausov, A. P. Pylypenko, A. P. Sorochak

Published in: Strength of Materials | Issue 3/2019

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

The procedure of evaluating the crack resistance of 17G1S-U sheet steel after shock and vibration loading was advanced and experimentally tested using the method of complete deformation diagrams. The technical potential was employed to provide the growth of a mixed mode (I+III) macrocrack on the specimens with an identical central circular opening, which guaranteed the self-similar macrocrack propagation. The complete deformation diagrams displayed initial almost straight descending portion. In real constructions of gas mains, rather long macrocracks can arise after this fracture mode. The advanced procedure permits of reliable assessment of energy variations spent for a (I+III) mode crack propagation under any complex combined loading. The straight descending branch slope of the deformation diagram is established to be used for evaluating crack resistance variations of pipe steel subject to thermomechanical loading. Shock and vibration loading of a high frequency (1–2 kHz) is shown to essentially influence the crack resistance of pipe steel and plastic strain in the vicinity of a stress raiser. The impact of a power pulse on the material is dependent on its prestrain level through static tension and damage of its initial structure correspondingly. The controlling factor influencing the change in mechanical properties is the intensity of the power pulse. Basic fracture mechanisms of steel were established on the basis of examination of specimen fractures with scanning electron microscopy. The shock and vibration loading is evidently accompanied by energy contribution not only to the existing damages of the material but also to the initiating ones, which causes the localization of deformation and growth of pores in their vicinity. Since the energy accumulation can contribute to the modification of the material in the vicinity of those damages, the shape and sizes of ductile tear dimples are the informative parameters for evaluating the strength and plasticity of examined steel.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Literature
1.
go back to reference V. F. Pichugin (Ed.), P. O. Marushchak, S. V. Panin, et al., Large-Scale Strain and Fracture Levels for Heat-Resistant Steels [in Russian], TPU, Tomsk (2013). V. F. Pichugin (Ed.), P. O. Marushchak, S. V. Panin, et al., Large-Scale Strain and Fracture Levels for Heat-Resistant Steels [in Russian], TPU, Tomsk (2013).
2.
go back to reference S. V. Panin, P. O. Maruschak, I. V. Vlasov, et al., “Impact toughness of 12Cr1MoV steel. Part 2 – Influence of high intensity ion beam irradiation on energy and deformation parameters and mechanisms of fracture,” Theor. Appl. Fract. Mech., 83, 82–92 (2016).CrossRef S. V. Panin, P. O. Maruschak, I. V. Vlasov, et al., “Impact toughness of 12Cr1MoV steel. Part 2 – Influence of high intensity ion beam irradiation on energy and deformation parameters and mechanisms of fracture,” Theor. Appl. Fract. Mech., 83, 82–92 (2016).CrossRef
3.
go back to reference M. G. Chausov, P. O. Marushchak, A. P. Pylypenko, and V. V. Berezin, Deformation and Fracture Behavior of Plastic Materials under Shock and Vibration Loading [in Ukrainian], Terno-graf, Ternopil (2018). M. G. Chausov, P. O. Marushchak, A. P. Pylypenko, and V. V. Berezin, Deformation and Fracture Behavior of Plastic Materials under Shock and Vibration Loading [in Ukrainian], Terno-graf, Ternopil (2018).
4.
go back to reference M. G. Chausov, A. P. Pylypenko, and P. O. Marushchak, Procedure of Improving the Plastic Properties of Sheet Two-Phase High-Strength Titanium Alloys by Shock and Vibration Loading: Scientific-Methodical Recommendations for Plants of Ukraine as Regards Designing of Agricultural Equipment Manufacture [in Ukrainian], FOP V. A. Palyanytsya, Ternopil (2017). M. G. Chausov, A. P. Pylypenko, and P. O. Marushchak, Procedure of Improving the Plastic Properties of Sheet Two-Phase High-Strength Titanium Alloys by Shock and Vibration Loading: Scientific-Methodical Recommendations for Plants of Ukraine as Regards Designing of Agricultural Equipment Manufacture [in Ukrainian], FOP V. A. Palyanytsya, Ternopil (2017).
5.
go back to reference N. G. Chausov and A. P. Pilipenko, “Influence of dynamic overloading on fracture kinetics of metals at the final stages of deformation,” Mechanika, 48, 13–18 (2004). N. G. Chausov and A. P. Pilipenko, “Influence of dynamic overloading on fracture kinetics of metals at the final stages of deformation,” Mechanika, 48, 13–18 (2004).
6.
go back to reference M. G. Chausov, V. B. Berezin, A. P. Pylypenko, and V. B. Hutsaylyuk, “Strain field evolution on the surface of aluminum sheet alloys exposed to specific impact with oscillation loading,” J. Strain Anal. Eng., 50, No. 1, 61–72 (2015).CrossRef M. G. Chausov, V. B. Berezin, A. P. Pylypenko, and V. B. Hutsaylyuk, “Strain field evolution on the surface of aluminum sheet alloys exposed to specific impact with oscillation loading,” J. Strain Anal. Eng., 50, No. 1, 61–72 (2015).CrossRef
7.
go back to reference M. Chausov, V. Hutsaylyuk, L. Sniezek, et al., “Strain field evolution on the surface of stainless sheet steel 12Cr17 exposed to a specific impact with oscillation loading,” in: Proc. of the 11th Int. Conf. on Intelligent Technologies in Logistics and Mechatronics Systems (ITELMS’2016, April 28–29, 2016, Panevéþys, Lithuania), Medimond, Bologna, Italy (2016), pp. 47–52. M. Chausov, V. Hutsaylyuk, L. Sniezek, et al., “Strain field evolution on the surface of stainless sheet steel 12Cr17 exposed to a specific impact with oscillation loading,” in: Proc. of the 11th Int. Conf. on Intelligent Technologies in Logistics and Mechatronics Systems (ITELMS’2016, April 28–29, 2016, Panevéþys, Lithuania), Medimond, Bologna, Italy (2016), pp. 47–52.
8.
go back to reference M. G. Chausov, O. E. Zasymchuk, and K. M. Volyans’ka, “Studies on the display process of yield plateaus under pulse load adjustment of aluminum alloys,” Visn. NTUU “KPI”, Ser. Mashynobuduvannya, No. 63, 244–248 (2011). M. G. Chausov, O. E. Zasymchuk, and K. M. Volyans’ka, “Studies on the display process of yield plateaus under pulse load adjustment of aluminum alloys,” Visn. NTUU “KPI”, Ser. Mashynobuduvannya, No. 63, 244–248 (2011).
9.
go back to reference M. G. Chausov, A. P. Pylypenko, V. B. Berezin, et al., “Influence of impact-oscillatory loading upon the mechanical properties of the VT-22 titanium alloy sheet,” J. Mater. Eng. Perfom., 25, No. 8, 3482–3492 (2016).CrossRef M. G. Chausov, A. P. Pylypenko, V. B. Berezin, et al., “Influence of impact-oscillatory loading upon the mechanical properties of the VT-22 titanium alloy sheet,” J. Mater. Eng. Perfom., 25, No. 8, 3482–3492 (2016).CrossRef
10.
go back to reference S. V. Panin, P. O. Maruschak, I. V. Vlasov, and O. Prentkovskis, “Effect of stress concentrator shape on impact fracture mechanisms of 17Mn1Si steel,” Procedia Engineer., 165, 1925–1930 (2016).CrossRef S. V. Panin, P. O. Maruschak, I. V. Vlasov, and O. Prentkovskis, “Effect of stress concentrator shape on impact fracture mechanisms of 17Mn1Si steel,” Procedia Engineer., 165, 1925–1930 (2016).CrossRef
11.
go back to reference P. O. Maruschak, S. V. Panin, M. G. Chausov, et al., “Effect of long-term operation on steels of main gas pipeline. Reduction of static fracture toughness,” J. Nat. Gas Sci. Eng., 38, 182–186 (2017).CrossRef P. O. Maruschak, S. V. Panin, M. G. Chausov, et al., “Effect of long-term operation on steels of main gas pipeline. Reduction of static fracture toughness,” J. Nat. Gas Sci. Eng., 38, 182–186 (2017).CrossRef
12.
go back to reference V. Hutsaylyuk, M. Chausov, V. Berezin, et al., “Influence of dissipative structures formed by impulse loads on the processes of deformation and fracture,” Key Eng. Mater., 577–578, 273–276 (2014). V. Hutsaylyuk, M. Chausov, V. Berezin, et al., “Influence of dissipative structures formed by impulse loads on the processes of deformation and fracture,” Key Eng. Mater., 577–578, 273–276 (2014).
13.
go back to reference M. Chausov, P. Maruschak, A. Pylypenko, and L. Markashova, “Enhancing plasticity of high-strength titanium alloys VT22 under impact-oscillatory loading,” Philos. Mag., 97, No. 6, 389–399 (2017).CrossRef M. Chausov, P. Maruschak, A. Pylypenko, and L. Markashova, “Enhancing plasticity of high-strength titanium alloys VT22 under impact-oscillatory loading,” Philos. Mag., 97, No. 6, 389–399 (2017).CrossRef
14.
go back to reference A. A. Lebedev and N. G. Chausov, New Methods of Evaluating In-Service Degradation of Mechanical Properties of the Structure Metal [in Russian], Pisarenko Institute of Problems of Strength, National Academy of Sciences of Ukraine, Kiev (2004). A. A. Lebedev and N. G. Chausov, New Methods of Evaluating In-Service Degradation of Mechanical Properties of the Structure Metal [in Russian], Pisarenko Institute of Problems of Strength, National Academy of Sciences of Ukraine, Kiev (2004).
15.
go back to reference N. G. Chausov, “Complete deformation diagram as the source of information on the kinetics of damage accumulation and crack resistance of materials,” Zavod. Lab. Diagnost. Mater., 70, No. 7, 42–49 (2004). N. G. Chausov, “Complete deformation diagram as the source of information on the kinetics of damage accumulation and crack resistance of materials,” Zavod. Lab. Diagnost. Mater., 70, No. 7, 42–49 (2004).
16.
go back to reference M. G. Chausov, A. P. Pylypenko, P. O. Marushchak, and V. A. Dovganyuk, Method of Assessment of the Pulse Energy Input to the Plastic Material [in Ukrainian], Patent of Ukraine No. 113940, Valid since March 27, 2017, Bull. No. 6. M. G. Chausov, A. P. Pylypenko, P. O. Marushchak, and V. A. Dovganyuk, Method of Assessment of the Pulse Energy Input to the Plastic Material [in Ukrainian], Patent of Ukraine No. 113940, Valid since March 27, 2017, Bull. No. 6.
17.
go back to reference M. A. Smirnov, I. Yu. Pyshmintsev, A. N. Maltseva, and O. V. Mushina, “Effect of ferrite-bainite structure on the properties of high-strength pipe steel,” Metallurgist, 56, Nos. 1–2, 43–51 (2012).CrossRef M. A. Smirnov, I. Yu. Pyshmintsev, A. N. Maltseva, and O. V. Mushina, “Effect of ferrite-bainite structure on the properties of high-strength pipe steel,” Metallurgist, 56, Nos. 1–2, 43–51 (2012).CrossRef
18.
go back to reference V. M. Farber, I. Yu. Pyshmintsev, A. B. Arabei, et al., “Contributions of structural factors to the strength of K65 steels,” Steel Transl., 42, No. 9, 687–690 (2012).CrossRef V. M. Farber, I. Yu. Pyshmintsev, A. B. Arabei, et al., “Contributions of structural factors to the strength of K65 steels,” Steel Transl., 42, No. 9, 687–690 (2012).CrossRef
19.
go back to reference I. N. Veselov, I. Yu. Pyshmintsev, K. A. Laev, and S. Yu. Zhukova, “Structure and mechanical properties of low-carbon steel for oil and gas pipelines,” Steel Transl., 41, No. 2, 165–170 (2011).CrossRef I. N. Veselov, I. Yu. Pyshmintsev, K. A. Laev, and S. Yu. Zhukova, “Structure and mechanical properties of low-carbon steel for oil and gas pipelines,” Steel Transl., 41, No. 2, 165–170 (2011).CrossRef
20.
go back to reference P. O. Marushchak, R. T. Bishchak, and I. M. Danylyuk, Crack Resistance of Materials and Structures: Long-Term Operated Gas Mains [in Ukrainian], Zazaprint, Ternopil (2016). P. O. Marushchak, R. T. Bishchak, and I. M. Danylyuk, Crack Resistance of Materials and Structures: Long-Term Operated Gas Mains [in Ukrainian], Zazaprint, Ternopil (2016).
21.
go back to reference S. V. Panin, D. D. Moiseenko, P. V. Maksimov, et al., “Influence of energy dissipation at the interphase boundaries on impact fracture behaviour of a plain carbon steel,” Theor. Appl. Fract. Mech., 97, 478–499 (2018).CrossRef S. V. Panin, D. D. Moiseenko, P. V. Maksimov, et al., “Influence of energy dissipation at the interphase boundaries on impact fracture behaviour of a plain carbon steel,” Theor. Appl. Fract. Mech., 97, 478–499 (2018).CrossRef
22.
go back to reference I. Sevostianov and M. Kachanov, “Is the concept of “average shape” for a mixture of inclusions of diverse shapes legitimate?” Int. J. Solids Struct., 49, 3242–3254 (2012).CrossRef I. Sevostianov and M. Kachanov, “Is the concept of “average shape” for a mixture of inclusions of diverse shapes legitimate?” Int. J. Solids Struct., 49, 3242–3254 (2012).CrossRef
23.
go back to reference I. Sevostianov and M. Kachanov, “Normal and tangential compliances of interface of rough surfaces with contacts of elliptic shape,” Int. J. Solids Struct., 45, 2723–2732 (2008).CrossRef I. Sevostianov and M. Kachanov, “Normal and tangential compliances of interface of rough surfaces with contacts of elliptic shape,” Int. J. Solids Struct., 45, 2723–2732 (2008).CrossRef
24.
go back to reference Y. Sun, X. Li, X. Yu, et al., “Fracture morphologies of advanced high strength steel during deformation,” Acta Metall. Sin. (Engl. Lett.), 27, No. 1, 101–106 (2014).CrossRef Y. Sun, X. Li, X. Yu, et al., “Fracture morphologies of advanced high strength steel during deformation,” Acta Metall. Sin. (Engl. Lett.), 27, No. 1, 101–106 (2014).CrossRef
25.
go back to reference S. Osovski, D. Rittel, J. A. Rodriguez-Martinez, and R. Zaera, “Dynamic tensile necking: Influence of specimen geometry and boundary conditions,” Mech. Mater., 62, 1–13 (2013).CrossRef S. Osovski, D. Rittel, J. A. Rodriguez-Martinez, and R. Zaera, “Dynamic tensile necking: Influence of specimen geometry and boundary conditions,” Mech. Mater., 62, 1–13 (2013).CrossRef
26.
go back to reference A. Dorogoy, D. Rittel, and A. Godinger, “A shear-tension specimen for large strain testing,” Exp. Mech., 56, No. 3, 437–449 (2015).CrossRef A. Dorogoy, D. Rittel, and A. Godinger, “A shear-tension specimen for large strain testing,” Exp. Mech., 56, No. 3, 437–449 (2015).CrossRef
27.
go back to reference M. Chausov, A. Pylypenko, V. Berezin, et al., “Influence of dynamic non-equilibrium processes on strength and plasticity of materials of transportation systems,” Transport, 33, No. 1, 231–241 (2018).CrossRef M. Chausov, A. Pylypenko, V. Berezin, et al., “Influence of dynamic non-equilibrium processes on strength and plasticity of materials of transportation systems,” Transport, 33, No. 1, 231–241 (2018).CrossRef
Metadata
Title
Effect of Shock and Vibration Preloading on the Deformation and Fracture Behavior of 17G1S-U Steel
Authors
P. O. Marushchak
M. G. Chausov
A. P. Pylypenko
A. P. Sorochak
Publication date
13-08-2019
Publisher
Springer US
Published in
Strength of Materials / Issue 3/2019
Print ISSN: 0039-2316
Electronic ISSN: 1573-9325
DOI
https://doi.org/10.1007/s11223-019-00088-3

Other articles of this Issue 3/2019

Strength of Materials 3/2019 Go to the issue

Premium Partners