Electrical properties of 0.94Bi0.5Na0.5TiO3–0.06Ba(Zr0.055Ti0.945)O3 lead-free ceramics with high thermal stability

Authors: Jun-Jun Wang, Fei-Fei Guo, Bin Yang, Shan-Tao Zhang, Li-Mei Zheng, Feng-Min Wu, Wen-Wu Cao

Published in: Journal of Materials Science: Materials in Electronics | Issue 3/2018

Log in

Activate our intelligent search to find suitable subject content or patents.

search-config
loading …

Abstract

Here we report the 0.94(Bi0.5Na0.5)TiO3–0.06Ba(Zr0.055Ti0.945)O3 (0.94BNT–0.06BZT) lead-free ceramics was synthesized by two-step solid state reaction route. The structural, dielectric, ferroelectric, piezoelectric and electromechanical properties of the ceramics were studied, and showed excellent electric properties (P s  = 39.9 μC/cm2, P r  = 33.7 μC/cm2, E c  = 2.79 kV/mm, S = 0.20%, d 33  = 174 pC/N, k p = 0.33). The depolarization temperature (T d ) of the ceramics is about 65 °C, which is determined from the first hump of relative dielectric constant. The electromechanical factor k p disappears at 65 °C, is consistent with the depolarization temperature (T d ) and the ferroelectric-antiferroelectric phase transition temperature (T feafe ) determined from the temperature-dependent PE and bipolar SE curves. These results indicate the 0.94BNT–0.06BZT ceramics has a good thermal stability in range of − 60–60 °C, and meets the actual demand.

Dont have a licence yet? Then find out more about our products and how to get one now:

Springer Professional "Wirtschaft+Technik"

Online-Abonnement

Mit Springer Professional "Wirtschaft+Technik" erhalten Sie Zugriff auf:

  • über 102.000 Bücher
  • über 537 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Maschinenbau + Werkstoffe
  • Versicherung + Risiko

Jetzt Wissensvorsprung sichern!

Springer Professional "Technik"

Online-Abonnement

Mit Springer Professional "Technik" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 390 Zeitschriften

aus folgenden Fachgebieten:

  • Automobil + Motoren
  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Elektrotechnik + Elektronik
  • Energie + Nachhaltigkeit
  • Maschinenbau + Werkstoffe




 

Jetzt Wissensvorsprung sichern!

Springer Professional "Wirtschaft"

Online-Abonnement

Mit Springer Professional "Wirtschaft" erhalten Sie Zugriff auf:

  • über 67.000 Bücher
  • über 340 Zeitschriften

aus folgenden Fachgebieten:

  • Bauwesen + Immobilien
  • Business IT + Informatik
  • Finance + Banking
  • Management + Führung
  • Marketing + Vertrieb
  • Versicherung + Risiko




Jetzt Wissensvorsprung sichern!

Literature
2.
go back to reference J. Rödel, W. Jo, K.T.P. Seifert, E.N. Anton, T. Granzow, J. Am. Ceram. Soc. 92(6), 1153–1177 (2009)CrossRef J. Rödel, W. Jo, K.T.P. Seifert, E.N. Anton, T. Granzow, J. Am. Ceram. Soc. 92(6), 1153–1177 (2009)CrossRef
3.
go back to reference T. Takenak, ,K. Maruyama, K. Sakata, Jpn. J. Appl. Phys. 30(9S), 2236 (1991)CrossRef T. Takenak, ,K. Maruyama, K. Sakata, Jpn. J. Appl. Phys. 30(9S), 2236 (1991)CrossRef
4.
5.
go back to reference A.B. Kounga, S.T. Zhang, W. Jo, T. Granzow, J. Rödel, Appl. Phys. Lett. 92(22), 222902 (2008)CrossRef A.B. Kounga, S.T. Zhang, W. Jo, T. Granzow, J. Rödel, Appl. Phys. Lett. 92(22), 222902 (2008)CrossRef
6.
go back to reference A. Sasaki, T. Chiba, Y. Mamiya, E. Otsuki, Jpn. J. Appl. Phys. 38(9S), 5564 (1999)CrossRef A. Sasaki, T. Chiba, Y. Mamiya, E. Otsuki, Jpn. J. Appl. Phys. 38(9S), 5564 (1999)CrossRef
7.
8.
go back to reference H. Nagata, M. Yoshida, Y. Makiuchi, T. Takenaka, Jpn. J. Appl. Phys. 42(12R), 7401 (2003)CrossRef H. Nagata, M. Yoshida, Y. Makiuchi, T. Takenaka, Jpn. J. Appl. Phys. 42(12R), 7401 (2003)CrossRef
9.
10.
go back to reference G.F. Fan, W.Z. Lu, X.H. Wang, F. Liang, Appl. Phys. Lett. 91(20), 202908 (2007)CrossRef G.F. Fan, W.Z. Lu, X.H. Wang, F. Liang, Appl. Phys. Lett. 91(20), 202908 (2007)CrossRef
11.
go back to reference S.T. Zhang, F. Yan, B. Yang, W.W. Cao, Appl. Phys. Lett. 97(12), 122901 (2010)CrossRef S.T. Zhang, F. Yan, B. Yang, W.W. Cao, Appl. Phys. Lett. 97(12), 122901 (2010)CrossRef
12.
13.
go back to reference W.C. Lee, Y.F. Lee, M.H. Tseng, C.Y. Huang, Y.C. Wu, J. Am. Ceram. Soc. 92(5), 1069–1073 (2009)CrossRef W.C. Lee, Y.F. Lee, M.H. Tseng, C.Y. Huang, Y.C. Wu, J. Am. Ceram. Soc. 92(5), 1069–1073 (2009)CrossRef
14.
go back to reference H.Y. Tian, K.W. Kwok, H.L.W. Chan, C.E. Buckley, J. Mater. Sci. 42(23), 9750–9755 (2007)CrossRef H.Y. Tian, K.W. Kwok, H.L.W. Chan, C.E. Buckley, J. Mater. Sci. 42(23), 9750–9755 (2007)CrossRef
15.
go back to reference P. Kantha, K. Pengpat, P. Jarupoom, U. Intatha, G. Rujijanagul, T. Tunkasiri, Curr. Appl. Phys. 9(2), 460–466 (2009)CrossRef P. Kantha, K. Pengpat, P. Jarupoom, U. Intatha, G. Rujijanagul, T. Tunkasiri, Curr. Appl. Phys. 9(2), 460–466 (2009)CrossRef
16.
go back to reference I. Franke, K. Roleder, L. Mitoseriu, R. Piticescu, Z. Ujma, Phys. Rev. B 73(14), 144114 (2006)CrossRef I. Franke, K. Roleder, L. Mitoseriu, R. Piticescu, Z. Ujma, Phys. Rev. B 73(14), 144114 (2006)CrossRef
17.
go back to reference T. Leist, J. Chen, W. Jo, E. Aulbach, J. Suffner, J. Rödel, J. Am. Ceram. Soc. 95(2), 711–715 (2012)CrossRef T. Leist, J. Chen, W. Jo, E. Aulbach, J. Suffner, J. Rödel, J. Am. Ceram. Soc. 95(2), 711–715 (2012)CrossRef
18.
go back to reference L. Luo, W.W. Ge, J.F. Li, D. Viehland, C. Farley, R. Bodnar, Q.H. Zhang, H.S. Luo, J. Appl. Phys. 109(11), 113507 (2011)CrossRef L. Luo, W.W. Ge, J.F. Li, D. Viehland, C. Farley, R. Bodnar, Q.H. Zhang, H.S. Luo, J. Appl. Phys. 109(11), 113507 (2011)CrossRef
19.
go back to reference J. Suchanicz, I. Jankowska-Sumara, T.V. Kruzina, J. Electroceram. 27(2), 45 (2011)CrossRef J. Suchanicz, I. Jankowska-Sumara, T.V. Kruzina, J. Electroceram. 27(2), 45 (2011)CrossRef
20.
go back to reference D. Rout, K.S. Moon, V.S. Rao, S.J.L. Kang, J.Ceram.Soc. Jpn. 117(1367), 797–800 (2009)CrossRef D. Rout, K.S. Moon, V.S. Rao, S.J.L. Kang, J.Ceram.Soc. Jpn. 117(1367), 797–800 (2009)CrossRef
21.
go back to reference J. Petzelt, S. Kamba, J. Fabry, D. Noujni, V. Porokhonskyy, A. Pashkin, I. Franke, K. Roleder, J. Suchanicz, R. Klein, G.E. Kugel, J. Phys. 16(15), 2719 (2004) J. Petzelt, S. Kamba, J. Fabry, D. Noujni, V. Porokhonskyy, A. Pashkin, I. Franke, K. Roleder, J. Suchanicz, R. Klein, G.E. Kugel, J. Phys. 16(15), 2719 (2004)
22.
23.
go back to reference S.T. Zhang, A.B. Kounga, E. Aulbach, T. Granzow, W. Jo, H.J. Kleebe, J. Rödel, J. Appl. Phys. 103(3), 034108 (2008)CrossRef S.T. Zhang, A.B. Kounga, E. Aulbach, T. Granzow, W. Jo, H.J. Kleebe, J. Rödel, J. Appl. Phys. 103(3), 034108 (2008)CrossRef
24.
go back to reference S.T. Zhang, A.B. Kounga, E. Aulbach, Y. Deng, J. Am. Ceram. Soc. 91(12), 3950–3954 (2008)CrossRef S.T. Zhang, A.B. Kounga, E. Aulbach, Y. Deng, J. Am. Ceram. Soc. 91(12), 3950–3954 (2008)CrossRef
Metadata
Title
Electrical properties of 0.94Bi0.5Na0.5TiO3–0.06Ba(Zr0.055Ti0.945)O3 lead-free ceramics with high thermal stability
Authors
Jun-Jun Wang
Fei-Fei Guo
Bin Yang
Shan-Tao Zhang
Li-Mei Zheng
Feng-Min Wu
Wen-Wu Cao
Publication date
31-10-2017
Publisher
Springer US
Published in
Journal of Materials Science: Materials in Electronics / Issue 3/2018
Print ISSN: 0957-4522
Electronic ISSN: 1573-482X
DOI
https://doi.org/10.1007/s10854-017-8154-1

Other articles of this Issue 3/2018

Journal of Materials Science: Materials in Electronics 3/2018 Go to the issue